A kind of preparation method of magnesium chloride particle

A magnesium chloride and particle technology, applied in magnesium chloride, magnesium halide and other directions, can solve the problems of uneven size of magnesium chloride particles, unfavorable energy saving and emission reduction, high blast energy consumption, and achieve the effects of rapid dissolution, not easy to stick, and high product quality.

Active Publication Date: 2017-05-10
TIANJIN SEA WATER DESALINATION & COMPLEX UTILIZATION INST STATE OCEANOGRAPHI
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this method is that the particles stick to each other during the cooling process, resulting in uneven particle size of the final formed magnesium chloride
If you want to get a product with uniform particles, you need to sieve again, resulting in low work efficiency and high production costs
Moreover, the blast energy consumption is high, which is not conducive to energy saving and emission reduction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of magnesium chloride particle

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Heat the magnesium chloride melt to 130°C in the heating kettle, and through the insulation pipe, spray the magnesium chloride melt to the pressure nozzle on the top of the tower, and control the pressure at 2.5MPa. The magnesium chloride melt is sprayed out through the pressure nozzle and dispersed into fine droplets . Keep the temperature of the saturated magnesium chloride aqueous solution at the bottom of the spray tower at 20°C, and the magnesium chloride melt droplets enter the saturated magnesium chloride aqueous solution at the bottom of the spray tower to cool and form into uniform magnesium chloride particles. The saturated aqueous solution of magnesium chloride containing magnesium chloride particles is separated from solid and liquid by a centrifuge to obtain finished magnesium chloride particles with a particle size of about 0.7mm.

Embodiment 2

[0018] Heat the magnesium chloride melt to 140°C in the heating kettle, and spray the magnesium chloride melt to the pressure nozzle on the top of the tower through the insulation pipe, and control the pressure at 3.5MPa. The magnesium chloride melt is sprayed out through the pressure nozzle and dispersed into fine droplets . Keep the temperature of the saturated magnesium chloride aqueous solution at the bottom of the spray tower at 15°C, and the molten magnesium chloride droplets enter the saturated magnesium chloride aqueous solution at the bottom of the spray tower to cool and form into uniform magnesium chloride particles. The magnesium chloride saturated aqueous solution containing magnesium chloride particles is separated from solid and liquid by a centrifuge to obtain finished magnesium chloride particles with a particle size of about 0.5mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention discloses a preparation method for magnesium chloride particles, which comprises the technical steps of obtaining the magnesium chloride melt in a heating pot, conveying the magnesium chloride melt to a pressure nozzle at the top of a spray tower through an insulating pipeline, spraying the magnesium chloride melt out of the pressure nozzle to disperse the magnesium chloride melt into fine droplets, controlling the pressure of the droplets of the magnesium chloride melt to be at 2.5-3.5 MPa, feeding the droplets of the magnesium chloride melt in a magnesium chloride saturated aqueous solution at the bottom of the spray tower so as to cool and shape the droplets of the magnesium chloride melt as uniform magnesium chloride particles, keeping the temperature of the magnesium chloride saturated aqueous solution at the bottom of the spray tower at 15-20 DEG C, and subjecting the magnesium chloride saturated aqueous solution containing magnesium chloride particles to the solid-liquid separation treatment in a centrifuge to obtain the finished product of magnesium chloride particles. Magnesium chloride particles prepared by the above method are uniform in particle size, fast to dissolve, and broad in application prospect.

Description

technical field [0001] The invention relates to a preparation method of magnesium chloride particles. Background technique [0002] At present, in industrial production, the preparation method of magnesium chloride particles is mostly air cooling granulation, that is, air is blown into the prilling tower, and the magnesium chloride melt is circulated and cooled in the prilling tower to obtain magnesium chloride particles. The disadvantage of this method is that the particles stick to each other during cooling, resulting in uneven particle size of the final magnesium chloride formed. If you want to get a product with uniform particles, you need to sieve again, resulting in low work efficiency and high production costs. Moreover, the blast energy consumption is high, which is not conducive to energy saving and emission reduction. In view of the above problems, it is an urgent problem to be solved in the field to develop a new preparation method of magnesium chloride particle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F5/30
Inventor 王玉琪黄西平张琦刘伟王涛王亮
Owner TIANJIN SEA WATER DESALINATION & COMPLEX UTILIZATION INST STATE OCEANOGRAPHI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com