Solvothermal synthetic method of TiO2 hollow-structure submicron spheres

A technology of hollow structure and synthesis method, which is applied in the direction of titanium dioxide, titanium oxide/hydroxide, etc.

Active Publication Date: 2015-08-05
HEFEI INSTITUTES OF PHYSICAL SCIENCE - CHINESE ACAD OF SCI
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Both ethylene glycol dimethyl ether and acetylacetone are conventional reagents. There have been some reports on the synthesis of TiO2 hollow microspheres, but ethylene glycol dimethyl ether and acetylacetone were used as solvents to synthesize TiO 2Micro-nano materials have not been reported yet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solvothermal synthetic method of TiO2 hollow-structure submicron spheres
  • Solvothermal synthetic method of TiO2 hollow-structure submicron spheres

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Mix acetylacetone and ethylene glycol dimethyl ether at a volume ratio of 1:4 to form a mixed solvent. After stirring evenly, add 2ml of tetra-n-butyl titanate (TBT), then fully stir and transfer the mixed solution to the reaction kettle, 200 °C for 12 hours. After natural cooling, TiO was obtained by centrifugation, washing and drying. 2 Hollow structure submicron spheres ( figure 1 ), the microsphere diameter is 450-550 nm.

Embodiment 2

[0021] Mix acetylacetone and ethylene glycol dimethyl ether at a volume ratio of 1:4 to form a mixed solvent. After stirring evenly, add 2ml of tetra-n-butyl titanate (TBT), then fully stir and transfer the mixed solution to the reaction kettle, 200 °C for 24 hours. After natural cooling, TiO was obtained by centrifugation, washing and drying. 2 Hollow structure submicron spheres ( figure 2 ), the diameter of microspheres is 500-600 nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a solvothermal synthetic method of TiO2 hollow-structure submicron spheres, wherein the solvothermal synthetic method comprises the steps of mixing acetylacetone with glycol dimethyl ether to obtain a mixed solvent, adding tetra-n-butyl titanate or tetra-isopropyl titanate with fully stirring, performing a reaction at 160-230 DEG C for 6-24 h in a reaction kettle, naturally cooling a reaction product, and separating, washing and drying the reaction product to obtain the TiO2 hollow-structure submicron spheres. The solvothermal synthetic method is mild in reaction conditions, is simple in process, is uniform in product particle size and is high in yield. The TiO2 hollow-structure submicron spheres have wide applications in the fields of solar cells, photo-catalysis, lithium ion batteries and the like.

Description

technical field [0001] The invention belongs to the preparation of inorganic nanometer materials, in particular to a kind of TiO 2 Solvothermal synthesis method of hollow structure submicron spheres. Background technique [0002] Titanium dioxide is widely used in photocatalysis, solar cells, lithium-ion batteries and other fields due to its advantages of non-toxicity, rich content, stability and photoactivity. With the rapid development of nanomaterials science, it has been possible to control TiO in the range of micro-nanoscale 2 The size and shape of the material. So far, various forms of TiO have been successfully prepared 2 Micro-nano materials, including zero-dimensional materials, such as quantum dots, nano-clusters, etc., one-dimensional materials, such as nanorods, nanowires, nanotubes, etc., two-dimensional materials, such as nanosheets, nanobelts, etc. Three-dimensional materials, such as micro-nanospheres, micro-nano hierarchical structures, etc. Compared wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G23/053
Inventor 胡林华李兆乾莫立娥戴松元
Owner HEFEI INSTITUTES OF PHYSICAL SCIENCE - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com