Nano material compound waste crumb rubber modified asphalt for heavy traffic road and preparation process thereof

A technology of nano-materials and modified asphalt, which is applied in building insulation materials, building components, buildings, etc., can solve the problems of rubber asphalt that are prone to cracking at low temperature, difficult to achieve road use effect, segregation, etc., and achieve anti-ultraviolet aging ability Improved, enhanced storage stability, improved temperature sensitivity effects

Inactive Publication Date: 2015-07-29
GUANGXI UNIV
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The storage stability of rubber asphalt has become a technical problem in the application. Since the density of rubber asphalt is higher than that of base asphalt, the rubber powder gradually sinks and causes segregation during the use and storage of rubber asphalt, making it difficult to achieve satisfactory road performance.
After the rubber asphalt concrete is paved, with the ultraviolet radiation, the rubber asphalt will gradually age and reduce the low temperature performance, which will lead to cracking and other diseases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano material compound waste crumb rubber modified asphalt for heavy traffic road and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1: A kind of nano-material composite waste rubber powder modified asphalt, made of the following raw materials in parts by mass:

[0024] Base asphalt 100kg; nano titanium dioxide 0.08kg; waste rubber powder 8kg;

[0025] The preparation method of nano-material composite waste rubber powder modified asphalt is characterized in that it comprises the following steps:

[0026] 1), take each component by mass ratio;

[0027] 2) Heat the base asphalt to 160°C, slowly add the weighed nano-titanium dioxide, and shear at high speed for 30 minutes to make it evenly mixed;

[0028] 3) Heat the asphalt mixture in step 2 to 205°C, slowly add the weighed waste rubber powder, and shear at high speed for 120 minutes to prepare nano-material compound waste rubber powder modified asphalt.

Embodiment 2

[0029] Embodiment 2: A nano-material composite waste rubber powder modified asphalt is made of the following raw materials in parts by mass:

[0030] 100 parts of base asphalt; 0.15 parts of nano-titanium dioxide; 15 parts of waste rubber powder;

[0031] The preparation method is the same as in Example 1.

Embodiment 3

[0032] Embodiment 3: A nano-material compound waste rubber powder modified asphalt, made of the following raw materials in parts by mass:

[0033] 100 parts of base asphalt; 0.3 parts of nano-titanium dioxide; 30 parts of waste rubber powder;

[0034] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
penetrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano material compound waste crumb rubber modified asphalt for a heavy traffic road. The nano material compound waste crumb rubber modified asphalt is prepared from matrix asphalt, waste rubber powder and nano titanium dioxide, wherein the content of the waste rubber powder accounts for 8 to 30wt% of the matrix asphalt, and the content of the nano titanium dioxide accounts for 0.08 to 0.3wt% of the matrix asphalt. A preparation method of the nano material compound waste crumb rubber modified asphalt comprises the following steps of (1) heating the matrix asphalt to 35 to 160 DEG C, slowly adding the weighed nano titanium dioxide, and performing high-speed shearing for 10 to 30 minutes so as to ensure that the matrix asphalt and the nano titanium dioxide are uniformly mixed; (2) heating the asphalt mixture obtained in the step 1 to 180 to 215 DEG C, slowly adding the weighed waste rubber powder, and performing high-speed shearing for 90 to 100 minutes, thereby preparing the nano material compound waste crumb rubber modified asphalt. The prepared modified asphalt is capable of improving the asphalt storage stability, the asphalt temperature sensitivity (anti-track property at a high temperature and anti-cracking property at a low temperature) and the ultraviolet radiation aging resistance, further is capable of effectively decomposing nitric oxides in automobile exhaust, and has an air purification effect and favorable social and environment-friendly benefits.

Description

technical field [0001] The invention relates to a nano-material composite waste rubber powder modified asphalt for heavy-duty traffic roads and a preparation method thereof, belonging to the technical field of road paving materials Background technique [0002] Process waste tires into waste rubber powder of more than 20 meshes, add a certain proportion of waste rubber powder to base asphalt, and make rubber asphalt after fully reacting under high temperature conditions. Since rubber is a kind of high molecular compound, in addition to being elastic, it also has high self-adhesiveness and inter-adhesiveness. When rubber powder and asphalt are melted together, the viscosity of asphalt increases significantly, which is beneficial to improve the cementation of asphalt mixture. At the same time, asphalt has the characteristics of rubber elasticity and flexibility, so as to improve the high temperature stability and low temperature crack resistance of rubber asphalt concrete. Pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L7/00C08L9/06C08L9/00C08K3/22
Inventor 孟勇军毛明亮杨斌蒋允田李方念邵明明程维
Owner GUANGXI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com