A knitted fabric, high-grade technology, applied in the field of textile fabrics, can solve the problems of high strength and elasticity without cotton fiber, easy to break, non-mechanical friction, etc., and achieve the effects of excellent moisture absorption, soft hand feeling and good hydrophilicity

Inactive Publication Date: 2015-06-03
ZHEJIANG YANA TEXTILE
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The above invention uses 70% tencel / 30% cupro ammonia fiber, which has relatively high performance, but the fabric does not have the high strength and elasticity of cotton fiber, cannot be mechanically rubbed, and is easy to break, and its gloss, brightness and hydrophilicity are not artificial. silk good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blending high-grade knitting fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Such as figure 1 As shown, the blended high-grade knitted fabric is made of tencel fiber, cotton fiber and cupro ammonia fiber, and then twisted with rayon to form the first yarn 1 and the second yarn 2. The first yarn 1 is the S twist direction, the second yarn 2 is the Z twist direction, and the first yarn 1 and the second yarn 2 are interwoven into fabrics at intervals, in which rayon, tencel fiber, cotton fiber, and cupro fiber account for high-grade knitting fabrics. The percentages of the total fabric weight are 36%; 32%; 32%; 10%.

[0027] The first coils formed by interweaving the first yarns are inclined towards the first direction, the second coils formed by the second yarns are inclined towards the second direction, and the first direction is opposite to the second direction.

[0028] Tencel fiber adopts Lenzing A100 Tencel.

[0029] The cotton fiber is made of high-quality long-staple cotton, the length of which is more than 35mm, the linear density is 1.5...

Embodiment 2

[0033] Blended high-grade knitted fabric, the high-grade knitted fabric is made of tencel fiber, cotton fiber, cupro ammonia fiber mixed yarn, and then twisted with rayon to make the first yarn 1 and the second yarn 2, the first yarn Thread 1 is in the S twist direction, and the second yarn 2 is in the Z twist direction. The first yarn 1 and the second yarn 2 are interwoven at intervals to form a fabric, in which rayon, tencel fiber, cotton fiber, and cupro fiber occupy high grades. The percentages of the total weight of the knitted fabric are 36%; 32%; 32%; 10%.

[0034] Tencel fiber adopts Lenzing A100 Tencel.

[0035] The cotton fiber is made of high-quality long-staple cotton, the length of which is more than 35mm, the linear density is 1.18dtex, and the strength is more than 4.9cN.

[0036] The linear density of cupro ammonia fiber is 1.33dtex.

[0037] The fabric is made by interweaving the yarns composed of the above-mentioned tencel fibers, cotton fibers, cupro ammon...

Embodiment 3

[0039]Blended high-grade knitted fabric, the high-grade knitted fabric is made of tencel fiber, cotton fiber, cupro ammonia fiber mixed yarn, and then twisted with rayon to make the first yarn 1 and the second yarn 2, the first yarn Thread 1 is in the S twist direction, and the second yarn 2 is in the Z twist direction. The first yarn 1 and the second yarn 2 are interwoven at intervals to form a fabric, in which rayon, tencel fiber, cotton fiber, and cupro fiber occupy high grades. The percentages of the total weight of the knitted fabric are 36%; 32%; 32%; 10%.

[0040] Tencel fiber adopts Lenzing A100 Tencel.

[0041] The cotton fiber is made of high-quality long-staple cotton, the length of which is more than 35mm, the linear density is 1.36dtex, and the strength is more than 4.9cN.

[0042] The linear density of cupro ammonia fiber is 0.89dtex.

[0043] The fabric is made by interweaving the yarns composed of the above-mentioned tencel fiber, cotton fiber, cupro ammonia ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a blending high-grade knitting fabric, and belongs to the technical field of knitting. The blending high-grade knitting fabric is characterized in that according to the percentage by weight in the high-grade knitting fabric, 32% of tencel fibers, 32% of cotton fibers and 10% of copper ammonia fibers are blended and spun, and 10% of rayon is added to be twisted into first yarns and second yarns, each first yarn adopts the S twisting direction, each second yarn adopts the Z twisting direction, and the first yarns and the second yarns are interweaved into the fabric. The blending high-grade knitting fabric has the advantages that the elasticity is good, the strength is high, the hand feel is soft, the luster and brightness are realized, and the trend of environment-friendly clothes is met; the good moisture-absorbing, moisture-discharging, anti-electrostatic, hanging and hydrophily functions are realized.

Description

technical field [0001] The invention belongs to the technical field of textile fabrics and relates to a blended high-grade knitted fabric. Background technique [0002] With the development of the economy and the improvement of people's living standards, consumption concepts are constantly updated, people pay more and more attention to the quality of life and living environment, and the requirements for clothing are getting higher and higher, so they are more and more particular about clothing fabrics. Wool knitted fabrics are simple and thick, suitable for autumn and winter fashion, but because of their simple colors, only plain and mixed colors, it is difficult to meet the high-end fashion requirements. In order to meet people's needs, a variety of knitted fabrics with different properties have appeared in the existing market. The different components and proportions of knitted fabrics will affect the performance of knitted fabrics. [0003] Artificial silk is made of na...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/14
Inventor 张新宇朱金华张勤华
Owner ZHEJIANG YANA TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products