Antibacterial finishing method of a kind of blended cotton fabric

An antibacterial finishing, cotton fabric technology, applied in the direction of fiber treatment, textile and papermaking, fiber type, etc., can solve the problems of low antibacterial strength, easy to be polluted and invaded by bacteria, etc., to achieve the effect of improving antibacterial strength

Active Publication Date: 2016-08-24
素肌(广州)科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Technical problem to be solved: The antibacterial strength of cotton and spandex or polyester blended fabric is low, and it is easy to be polluted and invaded by bacteria. To improve the antibacterial strength of blended cotton fabric, it is necessary to carry out antibacterial finishing on blended cotton fabric to improve the antibacterial effect of blended cotton fabric. Antibacterial properties of Escherichia coli and Staphylococcus aureus

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] (1) Pulverize juniper, add 20wt% ethanol aqueous solution after pulverization, the weight ratio of material to liquid is 1:9, the extraction temperature is 65°C, the extraction time is 5h, centrifuge after extraction, and concentrate the supernatant to prepare Juniper extract;

[0020] (2) Dried the green bark and crushed it, added 60wt% ethanol aqueous solution, the weight ratio of solid to liquid was 1:6, the extraction temperature was 60°C, the extraction time was 3 hours, after the extraction, it was centrifuged, and the supernatant was concentrated to prepare the green bark extract thing;

[0021] (3) taking chitosan by weight is 13 parts, nano-titanium dioxide is 6 parts, the juniper bark extract prepared by step (1) is 5 parts, the green bark extract prepared by step (2) is 5 parts, and water is 145 parts , dissolving chitosan, nano-titanium dioxide, juniper extract and green bark extract in water, stirring until uniform after dissolving;

[0022] (4) Immerse t...

Embodiment 2

[0024] (1) Pulverize juniper, add 40wt% ethanol aqueous solution after pulverization, the weight ratio of solid to liquid is 1:6, the extraction temperature is 55°C, the extraction time is 3h, centrifuge after extraction, and concentrate the supernatant to prepare Obtain juniper extract;

[0025] (2) Dried the green bark and crushed it, added 40wt% ethanol aqueous solution, the weight ratio of material to liquid was 1:4, the extraction temperature was 40°C, the extraction time was 2 hours, after extraction, it was centrifuged, and the supernatant was concentrated to prepare the green bark extract thing;

[0026] (3) taking chitosan by weight is 5 parts, nano-titanium dioxide is 3 parts, the juniper bark extract prepared by step (1) is 3 parts, the green bark extract prepared by step (2) is 2 parts, and water is 165 parts , dissolving chitosan, nano-titanium dioxide, juniper extract and green bark extract in water, stirring until uniform after dissolving;

[0027] (4) Immerse...

Embodiment 3

[0029] (1) Pulverize juniper, add 40wt% ethanol aqueous solution after pulverization, the weight ratio of solid to liquid is 1:6, the extraction temperature is 55°C, the extraction time is 3h, centrifuge after extraction, and concentrate the supernatant to prepare Obtain juniper extract;

[0030] (2) Dried the green bark and crushed it, added 40wt% ethanol aqueous solution, the weight ratio of material to liquid was 1:4, the extraction temperature was 40°C, the extraction time was 2 hours, after extraction, it was centrifuged, and the supernatant was concentrated to prepare the green bark extract thing;

[0031] (3) taking chitosan by weight is 7 parts, nano-titanium dioxide is 5 parts, the juniper bark extract prepared by step (1) is 4 parts, the green bark extract prepared by step (2) is 4 parts, and water is 160 parts , dissolving chitosan, nano-titanium dioxide, juniper extract and green bark extract in water, stirring until uniform after dissolving;

[0032] (4) Immerse...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibacterial finish method for a blended cotton fabric. The antibacterial finish method comprises the following steps: (1) grinding sabina chinensis, extracting the sabina chinensis in ethanol aqueous solution after grinding, performing centrifugal separation after extracting, and concentrating the supernatant, thereby obtaining a sabina chinensis extract; (2) additionally taking green tangerine peel, drying and grinding the green tangerine peel, extracting the green tangerine peel in the ethanol aqueous solution, performing centrifugal separation after extracting, and concentrating the supernatant, thereby obtaining the green tangerine peel extract; (3) taking chitosan, nanometer titania, the sabina chinensis extract, the green tangerine peel extract and water according to the weight, dissolving the chitosan, nanometer titania, sabina chinensis extract and green tangerine peel extract by using water, and stirring to be uniform after dissolving; and (4) immersing a blended cotton fabric in the mixed solution, soaking, soaking twice and padding twice, and drying, thereby obtaining the antibacterial blended cotton fabric. The prepared blended cotton fabric has high antibacterial performance.

Description

technical field [0001] The invention belongs to the field of textile dyeing and finishing, and relates to an antibacterial finishing method for textile fabrics, in particular to an antibacterial finishing method for blended cotton fabrics. Background technique [0002] Spandex has excellent elasticity, and its strength is higher than that of latex silk, its linear density is also finer, and it is more resistant to chemical degradation. Spandex has good acid and alkali resistance, sweat resistance, sea water resistance, dry cleaning resistance and abrasion resistance. The ratio of spandex used in general clothes is relatively low. When used, a large number of other fibers such as cotton and polyester blends are added to minimize the luster. [0003] Polyester has the characteristics of high strength. The short fiber strength is 2.6-5.7cN / dtex, and the high-strength fiber is 5.6-8.0cN / dtex. And its hygroscopicity is low, and its wet strength is basically the same as the dr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M13/00D06M15/00D06M15/03D06M11/46D06M101/06D06M101/38D06M101/32
Inventor 费芬芳
Owner 素肌(广州)科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com