Preparation method of water-based lubricant for metal stamping

A metal stamping and lubricant technology is applied in the field of preparation of water-based lubricants for metal stamping, which can solve the problems of easily polluted environment and poor anti-rust effect, and achieve the effects of reducing labor intensity, easy cleaning and good anti-rust performance.

Inactive Publication Date: 2015-04-29
芜湖华金冲压加工件厂
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the disadvantages of oil-based lubricants in the prior art, such as poor anti-rust effect and easy to pollute the environment, and provide a method for preparing a water-based lubricant for metal stamping. The lubricant of the present invention is distributed through creative components. Ratio, so that the lubricant has good lubricating performance and anti-rust effect, and is easy to clean and does not pollute the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A water-based lubricant for metal stamping in this embodiment, each component is composed of the following parts by mass: polyethylene glycol 22 kg, sodium polyacrylate 25 kg, fatty acid amide 26 kg, gull gum 12 kg, sodium pyrophosphate 4 kg, 5 kg of silica sol, 21 kg of polyacrylamide, 2 kg of dipotassium hydrogen phosphate, 3 kg of naphthalene sulfonate, and 880 kg of water.

[0025] It is worth noting that the polyethylene glycol makes the lubricant have good lubricating properties, and the polyethylene glycol is PEG-3000. The molecular weight of the sodium polyacrylate is 2000-3000, and the fatty amide is also called N.N-bishydroxyethyl alkylamide, coconut acid diethanolamide, coconut oil diethanolamide and the like.

[0026] In addition, it must be noted that the guar gum is a water-soluble polymer, and its chemical name is guar gum hydroxypropyltrimethylammonium chloride. The sodium pyrophosphate in this example is also called tetrasodium phosphate, sodium pyroph...

Embodiment 2

[0034] The basic content of this embodiment is the same as that of Example 1, and the difference is that each component of the lubricant of this embodiment is composed of the following parts by mass: 25 kg of polyethylene glycol, 30 kg of sodium polyacrylate, 28 kg of fatty acid amide, Gur gum 15 kg, sodium pyrophosphate 5 kg, silica sol 6 kg, polyacrylamide 26 kg, dipotassium hydrogen phosphate 3 kg, naphthalenesulfonate 4 kg, water 900 kg.

[0035] A kind of water-based lubricant for metal stamping of the present embodiment, its specific preparation method is as follows:

[0036] (1) Weigh 25 kg of polyethylene glycol, 30 kg of sodium polyacrylate, 28 kg of fatty acid amide, 15 kg of gull gum and 5 kg of sodium pyrophosphate in parts by mass, and mix polyethylene glycol, sodium polyacrylate, fat Amide, gull gum and sodium pyrophosphate were mixed with 100 kg of water and stirred for 15 min to obtain mixture A;

[0037] (2) Heat the mixture A prepared in step (1). First, hea...

Embodiment 3

[0042] The basic content of this embodiment is the same as that of Example 1, and the difference is that each component of the lubricant of this embodiment is composed of the following parts by mass: 20 kg of polyethylene glycol, 20 kg of sodium polyacrylate, 22 kg of fatty acid amide, Gur gum 8 kg, sodium pyrophosphate 3 kg, silica sol 2 kg, polyacrylamide 18 kg, dipotassium hydrogen phosphate 1 kg, naphthalene sulfonate 2 kg, water 800 kg.

[0043] A kind of water-based lubricant for metal stamping of the present embodiment, its specific preparation method is as follows:

[0044] (1) Weigh 20 kg of polyethylene glycol, 20 kg of sodium polyacrylate, 22 kg of fatty amide, 8 kg of gull gum and 3 kg of sodium pyrophosphate in parts by mass, and mix polyethylene glycol, sodium polyacrylate, fat Amide, gull gum and sodium pyrophosphate were mixed with 100 kg of water and stirred for 10 min to obtain mixture A;

[0045] (2) Heat the mixture A prepared in step (1). First, heat up a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a water-based lubricant for metal stamping, and belongs to the technical field of lubricants for metal stamping. The preparation method comprises the following steps: (1) preparing a mixture A: mixing components such as polyethylene glycol and sodium polyacrylate; (2) preparing a mixture B: heating the mixture A; (3) preparing a mixture C: adding components such as silica sol and polyacrylamide in the mixture B; (4) preparing the water-based lubricant: adding naphthalenesulfonate in the mixture C to prepare the lubricant. Through the creative component ratio, the lubricant has favorable anti-corrosion performance while ensuring the favorable lubricating property, and in addition, the lubricant is convenient to clean, and not only greatly reduces the cleaning labor intensity, but also endows a workpiece with a favorable degree of finish.

Description

technical field [0001] The invention relates to the technical field of metal stamping lubricants, in particular to a preparation method of a water-based lubricant for metal stamping. Background technique [0002] Stamping processing is a metal cold deformation processing method, which uses the power of conventional or special stamping equipment to directly deform the sheet metal in the mold to obtain product parts of a certain shape, size and performance. technology. Among them, sheet metal, mold and equipment are the three elements of stamping processing. Stamping has the advantages of high production efficiency, high product precision, and less raw material consumption. Due to such advantages, stamping has a wide range of applications in various fields of the national economy. [0003] Lubricants are essential in the stamping process. Lubricants not only increase the life of the die, but also improve the finish and reduce the precision of the workpiece. However, the exi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/02C10N40/24C10N30/06C10N30/04C10N30/12
Inventor 汪先金
Owner 芜湖华金冲压加工件厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com