Special alkali-free direct yarn wetting agent for grinding wheel reinforcing sheets and preparation method thereof

A reinforcement sheet and sizing technology, which is applied in the preparation of the alkali-free direct yarn sizing agent and the alkali-free glass fiber sizing agent for grinding wheel reinforcement sheet, which can solve the problems of not being resistant to textiles, easy to produce yarn, and strength that cannot meet customer requirements, etc. problem, to achieve the effect of good soaking effect, good strength, and guaranteed binding effect

Inactive Publication Date: 2015-04-29
JIANGSU JIUDING NEW MATERIAL CO LTD
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there is no alkali-free direct yarn sizing specially developed for grinding wheel reinforcement sheets in the industry. The common alkali-free direct yarn used for grinding wheel reinforcement fabrics mainly has the following problems: 1. It is not resistant to textiles, and wool yarn is easily produced during the weaving process; 2. The strength cannot meet the customer's requirements; 3. The combination effect of the yarn and the resin for impregnating the reinforced cloth is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special alkali-free direct yarn wetting agent for grinding wheel reinforcing sheets and preparation method thereof
  • Special alkali-free direct yarn wetting agent for grinding wheel reinforcing sheets and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] The preparation method of alkali-free direct yarn sizing agent of the present invention is:

[0051] (1) Set the required weight of deionized water to 100 parts, add 15 to 25 parts of deionized water at 20 to 30°C in the preparation kettle, add glacial acetic acid and stir for 5 to 10 minutes, add coupling agent in proportion, and stir for 30 to 40min;

[0052] (2) Dissolve and dilute the lubricant with 10-20 parts of deionized water at 60-80°C, and add it to the preparation kettle;

[0053] (3) Dilute the epoxy emulsion and water-soluble epoxy resin with 5-15 parts of deionized water respectively, and add them to the preparation kettle;

[0054] (4) Dilute the polyester emulsion with 5 to 15 parts of deionized water and add it to the preparation kettle;

[0055] (5) Dissolve the new additive A with 2 to 4 parts of deionized water and add it to the preparation kettle;

[0056] (6) Dissolve the new additive B with 2 to 4 parts of deionized water and add it to the prep...

Embodiment 1

[0060] Bisphenol A type epoxy resin emulsion: 3%

[0061] Unsaturated polyester resin emulsion: 2%

[0062] Bisphenol A water-soluble epoxy resin: 0.3%

[0063] Polyethylene glycol fatty acid ester: 0.5%

[0064] Nonionic alkyl modified silicone lubricant: 0.1%

[0065] Inorganic salt antistatic agent: 0.05%

[0066] γ-Aminopropyltriethoxysilane: 0.3%

[0067] γ-(Methacryloyloxy)propyltrimethoxysilane: 0.8%

[0068] Zinc salt 0.5%

[0069] Aminocarboxylate complexing agent 0.25%

[0070]Glacial acetic acid: 0.4%

[0071] Deionized water balance

Embodiment 2

[0073] Bisphenol A type epoxy resin emulsion: 4%

[0074] Unsaturated polyester resin emulsion: 2%

[0075] Bisphenol A water-soluble epoxy resin: 0.3%

[0076] Polyethylene glycol fatty acid ester: 0.6%

[0077] Nonionic alkyl modified silicone lubricant: 0.1%

[0078] Inorganic salt antistatic agent: 0.05%

[0079] γ-Aminopropyltriethoxysilane: 0.3%

[0080] γ-(Methacryloyloxy)propyltrimethoxysilane: 0.9%

[0081] Zinc salt 0.5%

[0082] Aminocarboxylate complexing agent 0.25%

[0083] Glacial acetic acid: 0.4%

[0084] Deionized water: balance

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a special alkali-free direct yarn wetting agent for grinding wheel reinforcing sheets and a preparation method thereof. The alkali-free direct yarn wetting agent comprises the following components in percentage by mass: 2-6% of epoxy emulsion, 1-5% of polyester emulsion, 0.2-0.6% of water-soluble epoxy resin, 0.2-0.8% of lubricant, 0.05-0.3% of antistatic agent, 0.8-1.4% of coupling agent, 0.2-2% of novel assistant A, 0.1-1% of novel assistant B, 0.1-0.5% of glacial acetic acid and the balance of deionized water. Various components are adopted to endow the yarn with high power and favorable permeation effect in the dipping treatment process. Multiple high-performance lubricants are utilized, and the two novel assistants are introduced, thereby implementing favorable weaving effect on the premise of ensuring favorable permeation effect. The two coupling agents are combined to well ensure the combination effect between the glass fiber and resin.

Description

technical field [0001] The invention relates to an alkali-free textile direct yarn sizing agent, in particular to a special alkali-free glass fiber sizing agent for a grinding wheel reinforcement sheet which can be used for both warp and weft yarns of a grinding wheel reinforcement cloth, and also relates to a preparation method of the alkali-free direct yarn sizing agent. Background technique [0002] Glass fiber reinforced grinding wheel uses glass fiber mesh as the reinforcing base material of the grinding wheel to improve the overall strength of the grinding wheel. It has been used in China for many years. Grinding wheels with glass fiber mesh as reinforcement are widely used in mechanical metallurgy, construction, military industry, railway construction, fire-fighting and demolition and other fields. [0003] As the selective reinforcement of glass fiber reinforced grinding wheel, it is generally necessary to process glass fiber into unidirectional or multiaxial fabric....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C25/36
Inventor 严程荣陈伟鹏高进波曹正兵顾柔坚
Owner JIANGSU JIUDING NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com