Catalyst for synthesizing ethylidene diacetate and application of catalyst
A technology of diethylene acetate and catalyst, which is applied in the direction of physical/chemical process catalyst, carboxylate preparation, metal/metal oxide/metal hydroxide catalyst, etc., can solve the problem of low yield of diacetate, Low selectivity and other issues, to achieve the effect of improving yield and selectivity, improving activity and stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0025] The preparation of catalyst: the Ru(OAc) that contains 5.80gRu, contains 2.50gCr and contains 1.25gBe 3 ·3H 2 O, Cr(OAc) 3 ·6H 2 O and BeO are fully mixed and dissolved in hydrochloric acid to obtain 500ml of impregnation solution, and 1.0L of spherical SiO with a diameter of 5.6mm 2 The carrier was immersed in the above impregnating solution, and dried at 100°C for 3 hours. 2 The catalyst was obtained by raising the temperature to 500° C. and calcining for 5 h in the atmosphere.
[0026] Synthesis of diethylene acetate: Add 1.5mol acetic acid, 0.05mol catalyst and 0.45mol methyl acetate into a 1.5L titanium reactor, first use argon to exhaust the air in the kettle, then pressurize to 2.0MPa, and then introduce carbon monoxide And hydrogen until the pressure is 7.8MPa, increase the stirring speed to 1500rpm, while stirring and heating to the reaction temperature, control the reaction temperature to 181°C, the molar ratio of carbon monoxide to hydrogen is 2:1, cont...
Embodiment 2
[0049] The preparation of catalyst: will contain 5.80gRu, contain 2.50gCr and contain the Ru(NO 3 ) 3 ·3H 2 O, Cr(NO 3 ) 3 9H 2 O and MgSO 4 ·H 2 O is fully mixed and dissolved in pure water to obtain 500ml of immersion solution, and 1.0L of spherical Al with a diameter of 5.6mm 2 o 3 The carrier was immersed in the above impregnating solution, left to stand for 3 hours, dried at 80° C., and then heated to 400° C. and calcined for 5 hours in a He atmosphere to obtain the catalyst.
[0050] Synthesis of diethylene acetate: Add 1.5mol acetic acid, 0.05mol catalyst and 0.45mol methyl acetate into a 1.5L titanium reactor, first use argon to exhaust the air in the kettle, then pressurize to 2.0MPa, and then introduce carbon monoxide And hydrogen until the pressure is 7.8MPa, increase the stirring speed to 1500rpm, while stirring and heating to the reaction temperature, control the reaction temperature to 181°C, the molar ratio of carbon monoxide to hydrogen is 2:1, contin...
Embodiment 3
[0054] Preparation of catalyst: RuCl containing 5.80gRu, 2.50gCr and 1.25gCa 3 ·3H 2 O, CrCl 3 ·6H 2 O and Ca(NO 3 ) 2 4H 2 O, fully mixed and dissolved in hydrochloric acid to obtain 500ml of impregnation solution, and 1.0L of spherical Al with a diameter of 5.6mm 2 o 3 The carrier was immersed in the impregnating solution, left to stand for 3 hours, dried at 120° C., and then heated to 600° C. and calcined for 5 hours in an Ar atmosphere to obtain the catalyst.
[0055] Synthesis of diethylene acetate: Add 1.5mol acetic acid, 0.05mol catalyst and 0.45mol methyl acetate into a 1.5L titanium reactor, first use argon to exhaust the air in the kettle, then pressurize to 2.0MPa, and then introduce carbon monoxide And hydrogen until the pressure is 7.8MPa, increase the stirring speed to 1500rpm, while stirring and heating to the reaction temperature, control the reaction temperature to 181°C, the molar ratio of carbon monoxide to hydrogen is 2:1, continue the reaction for...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com