Fluid bed catalyst for acrylonitrile production

A fluidized bed catalyst and acrylonitrile technology, which is applied in physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, bulk chemical production, etc. It can solve the problems of low propylene load and low reaction pressure , to achieve the effect of improving activity and stability

Active Publication Date: 2008-11-19
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] The technical problem to be solved by the present invention is that the propylene loading in the prior art is lower and the reaction pressure is lower, and a new method for producing acrylonitrile is provided Fluidized bed catalyst, which is not only suitable for operation under higher propylene loading and higher reaction pressure, but also has the advantage of higher acrylonitrile yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluid bed catalyst for acrylonitrile production
  • Fluid bed catalyst for acrylonitrile production
  • Fluid bed catalyst for acrylonitrile production

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Add 10 grams of water to 1.40 grams of sodium hydroxide and 2.35 grams of potassium hydroxide and dissolve after heating to obtain material (A); 734.6 grams of ammonium molybdate is dissolved in 600 grams of 60~90 ℃ of hot water to obtain material (B); gram of bismuth nitrate, 594.4 gram of iron nitrate, 611.2 gram of nickel nitrate, 177.8 gram of magnesium nitrate, 40.9 gram of calcium nitrate and 118.8 gram of telluric acid mix, add 450 grams of water, after heating and dissolving, take as material (C); Weigh 70.1 gram of chromium trioxide Dissolve in 75 grams of water to obtain material (D); weigh 22.6 grams of cerium nitrate and dissolve it in 10 grams of water and heat to dissolve to obtain material (E); weigh 430.0 grams of 50% manganese nitrate as material (F).

[0053] Mix material (A) with 2475 grams of silica sol with a weight concentration of 40%, add materials (B), (C), (D), (E) and (F) in turn under stirring, and obtain a slurry after fully stirring Materia...

Embodiment 2～6 and comparative example 1～4

[0056] Catalysts with different compositions in the following table were prepared by the same method as in Example 1, and the ammoxidation of propylene to acrylonitrile was carried out under the following reaction conditions with the prepared catalysts. See the results.

[0057] The reaction conditions of above-mentioned embodiment and comparative example are:

[0058] 38 mm fluidized bed reactor

[0059] Reaction temperature 440°C

[0060] Reaction pressure 0.14MPa

[0061] Catalyst loading 400 grams

[0062] Catalyst propylene loading (WWH) 0.11 hours -1

[0063] Raw material ratio (mole) C 3 ＝ / NH 3 / air=1 / 1.2 / 9.8

[0064]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a fluidized bed catalyst which is used for producing acrylonitrile through propene ammoxidation, and mainly solves the problems of lower propene loading and lower reaction pressure in the prior art. The invention adopts a mixture which takes silicon dioxide as a carrier and has the chemical formula calculated in atomic ratio as follows: AaBbCcDdTeeNifMggFehBijMo12Ox, wherein, A is at least one of Li, Na, K, Rb and Cs; B is at least one of La, Ce, Nd and Eu; C is at least one of Cr, W and Mn; and D is at least one of Cu, Zn, Ag, Cd, Ca and S r or at least one in the B; thereby the technical proposal can better solve the problems. The catalyst can be applied to the industrial production of the acrylonitrile under higher reaction pressure and higher propene loading condition.

Description

technical field [0001] The invention relates to a fluidized bed catalyst for producing acrylonitrile by ammoxidation of propylene. Background technique [0002] Acrylonitrile is an important organic chemical raw material, which is produced by ammoxidation of propylene. In order to obtain a fluidized bed catalyst with high activity and high selectivity, people have made a series of improvements through continuous exploration. Most of these improvements involve the active composition of the catalyst, focusing on the combination of the active components of the catalyst to improve the activity and selectivity of the catalyst, thereby achieving an increase in the single-pass yield of acrylonitrile and an increase in production load. [0003] After more than 40 years of development in the production of acrylonitrile by ammoxidation, the production capacity of the factory and the market demand are close to balance. At present, the main development trend of acrylonitrile productio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J23/887C07C255/08C07C253/26
CPCY02P20/52
Inventor 陶跃武吴粮华
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap