Cadmium plating method for metal product surface treatment

A surface treatment and cadmium plating technology, which is applied in the field of surface treatment of metal products, can solve problems such as unqualified and affecting product quality, and achieve the effect of product quality assurance and adhesion enhancement

Inactive Publication Date: 2015-01-07
GUIZHOU HANGRUI AVIATION PRECISION PARTS MFG
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] The purpose of the present invention is to solve the problem that the traditional surface treatment cadmium plating method is unqualified, which affects the quality of the product, thereby providing a new surface treatment cadmium plating method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cadmium plating method for metal product surface treatment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0043] The specific embodiment described in the present invention is described as follows again:

[0044] Surface treatment cadmium plating process method step of the present invention:

[0045] Qualified products are chemically degreased (according to the steps in C below); when washing with hot water for the first time, wash with hot water at 50°C to 90°C, and after the first wash, wash at 10°C to 30°C Wash in clean water; dry, dry in an oven at 40°C to 80°C; loosen and tumbling, use a vibrating tumbling machine for tumbling; the second washing, wash in clean water at 10°C to 30°C; the first time Activation, (according to the following instructions); the third washing, cleaning in clean water at 10°C to 30°C; pre-plating with nickel; the fourth washing, cleaning in clean water at 10°C to 30°C; cadmium plating; fifth Washing with water for the first time in clean water at 10°C to 30°C; the first time for light emission to remove surface oxides; washing with water for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A cadmium plating method for metal product surface treatment comprises steps of alkaline degreasing; first cleaning by hot water, and then cleaning by clear water with the temperature of 10 DEG C-30 DEG C; drying and baking in a drying oven at the temperature of 40 DEG C-80 DEG C; loosening and roller burnishing by a vibrating roller burnishing machine; second cleaning; first activating; third water washing; nickel preplating; fourth water washing; cadmium plating; fifth water washing; first bright dipping to remove surface oxide; sixth water washing; second cleaning by hot water; first spin-drying by a spin dryer for 5-10 minutes; hydrogen removal with the time of 6-8 hours; second activating; seventh water washing; second bright dipping; eighth water washing; passivating; ninth water washing, wherein water washing from the second time to the ninth time adopts clear water with the temperature of 10 DEG C-30 DEG C; third cleaning by hot water, wherein the temperature of hot water used by the first time, the second time and the third time is 50 DEG C-90 DEG C; second spin-drying for 5-10 minutes; ageing; inspecting; and packaging. The corrosion resistance test of a product is prolonged to be longer than 96 hours, and the quality is guaranteed.

Description

technical field [0001] The invention relates to a metal product surface treatment method, in particular to a novel metal product surface treatment cadmium plating method, which improves the corrosion resistance of the product and ensures product quality at the same time. Background technique [0002] Similar products in the early stage required a maximum of 48 hours for the salt spray test, and some products did not have clear requirements. Some products have higher requirements. Components and parameters in the traditional process: [0003] 1. Activation [0004] A. Main ingredients Hydrochloric acid: 35~60g / L [0005] B. Process parameters: T(°C): room temperature; [0006] t(min): 0.5~2. [0007] 3. Cadmium plating [0008] A. Main ingredients: cadmium oxide: 20~40g / l; [0009] Sodium cyanide: 90~150g / l; [0010] Sodium sulfate: 40~60g / l; [0011] Nickel sulfate: 1~1.5ml / l [0012] Sodium carbonate (Na2CO3.10H2O): ≤60g / l ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C18/18C23C18/31
CPCC25D5/34C25D3/28C25D5/48C25D5/52
Inventor 王道益
Owner GUIZHOU HANGRUI AVIATION PRECISION PARTS MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com