High-performance thermoplastic polyolefin waterproof coiled material with high scrap rubber powder doping amount

A thermoplastic polyolefin and waterproof coiled material technology, which is applied in rubber layered products, synthetic resin layered products, chemical instruments and methods, etc. The mechanical properties remain stable, the welding peel strength is large, and the strength is high.

Active Publication Date: 2015-01-07
BEIJING UNIV OF CHEM TECH
View PDF11 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In summary, although there are many domestic studies on the blending of waste rubber powder and thermoplastics to prepare elastomers, waste rubber powder-based thermoplastic elastomers with high waste rubber powder content, mechanical properties, and excellent processing fluidity are waterproof. Material not reported
In addition, in the selection of processing equipment, most of them are open mills and internal mixers. In order to improve the performance of waste rubber powder-based thermoplastic elastomers, researchers often need to pre-treat waste rubber powder. The process is cumbersome and cannot be continuously produced. Unfavorable for the industrialization of products
Finally, the current application of waste rubber powder-based thermoplastic elastomers is mostly concentrated in areas with low added value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance thermoplastic polyolefin waterproof coiled material with high scrap rubber powder doping amount
  • High-performance thermoplastic polyolefin waterproof coiled material with high scrap rubber powder doping amount
  • High-performance thermoplastic polyolefin waterproof coiled material with high scrap rubber powder doping amount

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The high-performance thermoplastic polyolefin waterproof membrane with high waste rubber powder content of the present invention will be further described below in combination with examples and comparative examples.

[0029] The raw material formulas of waste rubber powder-based thermoplastic elastomer implementation cases 1-10 of the present invention are listed in Table 1. Unless otherwise specified, the data in Table 1 are all parts by mass. The waste tire rubber powder with an average particle size of 200 μm was purchased from Jiangyin Anqiang High Wear-resistant Rubber Powder Co., Ltd.; the polypropylene with a yield strength > 24 MPa was selected from Yanshan Petrochemical K8303, Shanghai Petrochemical GM 160E and Maoming Petrochemical EPS30R, with a melt index > 5g / The 10-minute polypropylene uses Shanghai Petrochemical M2101R and Yanshan Petrochemical K9020; SEBS uses Formosa Plastics 6150; phenolic resin chooses HY-2045 from Shanxi Rubber Auxiliary Factory; fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-performance thermoplastic polyolefin waterproof coiled material with a high scrap rubber powder doping amount. The high-performance thermoplastic polyolefin waterproof coiled material is formed by compounding an upper surface thermoplastic polyolefin (TPO) coiled material layer, an intermediate fiber fabric enhancement layer and a lower surface scarp rubber powder-based thermoplastic elastomer (WRTPE) coiled material layer. The composite waterproof coiled material disclosed by the invention is high in tensile strength and high in breakage ductility; all the coiled material layers are tightly combined, and all properties are higher than the indexes of enhancement coiled materials in a fabric GB 27789-2011; the composite coiled material is convenient to construct, and the cost of the composite coiled material is lowered by 20-30 percent when compared with the cost of a TPO enhanced coiled material with the same thickness; the high-performance thermoplastic polyolefin waterproof coiled material has a wide application prospect.

Description

technical field [0001] The invention relates to a high-performance thermoplastic polyolefin waterproof coiled material with high waste rubber powder content, belonging to the field of waterproof materials. Background technique [0002] Polymer waterproof membrane is a new type of building material. It is light, high-strength, low-energy and multi-functional in line with the development trend of building material innovation. Common varieties include PVC waterproof membrane, EPDM waterproof membrane, CPE waterproof membrane and TPO waterproof membrane. Coil. Among them, the TPO waterproof membrane is a new type of waterproof membrane prepared with petroleum resin, ethylene, acetic acid, and vinyl resin as the base material and other additives. It combines the weather resistance, low temperature temperature of EPDM membrane and the reliability of PVC membrane. Weldability. Due to the relatively high price of TPO waterproofing membranes, the current domestic sales of TPO water...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B25/10B32B27/02B32B27/12B32B27/32C08L21/00C08L23/12C08L53/02B29C43/28B29C43/30
CPCB29C48/0021B32B5/028B32B27/12B32B27/32B32B2274/00B32B2305/38B32B2323/10B32B2419/00B32B2419/06
Inventor 卢咏来肖鹏冯予星刘力田明张立群田凤兰段文峰
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com