Efficient continuous water atomizing process for producing steel powder

A technology of iron and steel powder and process method, which is applied in the field of powder metallurgy, can solve problems such as bulk density and particle size distribution fluctuations, and achieve the effects of improving quality, reducing tapping temperature, and improving atomization efficiency

Active Publication Date: 2014-12-31
ANGANG (ANSHAN) METALLURGY POWDER MATERIAL CO LTD
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the common problems in the domestic water atomization process are: in order to successfully complete the water atomization process, the molten steel must have a high superheat, and the atomization temperature changes continuously from high to low during the atomization process, resulting in loose density and particle size. The distribution fluctuates (the difference between the beginning and the end) is relatively large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Efficient continuous water atomizing process for producing steel powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] See figure 1 , is a specific embodiment of a high-efficiency continuous water atomization process for producing steel powder in the present invention. The system is equipped with two electric arc furnaces, one 5t electric arc furnace 1, one 10t electric arc furnace 2, and the capacity of the intermediate heating device 3 The molten steel smelted by the electric arc furnace 1 and 2 is continuously poured into the intermediate heating device 3; after the atomization starts, the molten steel flows out through the leak hole 5 of the tundish 4, and the high-pressure water pumped out by the high-pressure pump sprays the molten steel in the mist The atomizer 7 is broken into tiny liquid droplets, which are sprayed out from the atomizing nozzle. This embodiment is equipped with three high-pressure pumps, which are respectively high-pressure pump (1), high-pressure pump (2) and high-pressure pump (3), with two working and one standby, or two standby and one working. In addition,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an efficient continuous water atomizing process for producing steel powder. The process includes: continuously injecting molten steel into an intermediate thermal insulation heating device, continuously adjusting components and temperatures, continuously providing temperature signals to a control system by a temperature measuring device during atomizing, and controlling tundish temperature to be at 1550-1580 DEG C; by a weighing system located on the tank support base of the large tank of the intermediate thermal insulation heating device. continuously displaying the weight of the residual molten steel in the large tank to guarantee that the weight of the residual molten steel in the large tank is not less than 5 tons. Compared with the prior art, the efficient continuous water atomizing process has the advantages that two magnetic separation drying production lines are used, two working high-pressure pump and a backup high-pressure pump are equipped, and continuous steel powder water atomizing is achieved; atomizing temperature is fed back and controlled through real-time temperature measuring, and the physical and chemical performance of base powder is allowed to be even and consistent; reasonable nozzle size, draining hole diameter and atomizing pressure are used, tapping temperature is lowered, atomizing efficiency is increased, and base powder quality is increased.

Description

technical field [0001] The invention relates to a water atomization process in the field of powder metallurgy, in particular to a high-efficiency continuous water atomization process for producing iron and steel powder. Background technique [0002] Water atomization process technology is a common technology in the field of powder metallurgy to realize industrial production. The method is to use high-pressure atomized water to beat the high-temperature molten steel into extremely fine powder through a special nozzle, and then pass through magnetic separation, dehydration, Drying, reduction, crushing, screening, batching, packaging, and industrial production methods for producing steel powder. [0003] High-quality water-atomized iron powder-based powder with uniform performance is the prerequisite for the production of high-quality powder metallurgy parts. The characteristics of the raw material powder determine the properties of the finished iron powder for pressing and si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/08
Inventor 周振龙马全嘉卜福昌纪向军李恩林安喜峰高扬
Owner ANGANG (ANSHAN) METALLURGY POWDER MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products