Paraffin-SiO2-TiO2 phase change microcapsule and preparation method thereof as well as application of microcapsule in preparing heat-accumulation thermal insulation coating

A technology of -sio2-tio2, phase-change microcapsules, applied to paraffin-SiO2-TiO2 phase-change microcapsules, the preparation of the above-mentioned phase-change microcapsules, the application field of phase-change microcapsules in the preparation of heat storage and thermal insulation coatings, can Solve the problems of insufficient adsorption of organic phase change materials, low thermal conductivity of phase change microcapsules, and can not be used as a surface layer, etc., to achieve excellent heat storage and heat preservation performance, reduce indoor environment fluctuations, and improve thermal comfort

Inactive Publication Date: 2014-11-19
SOUTHEAST UNIV
View PDF6 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this paint is black and generally cannot be used as a surface layer in buildings.
Chinese patent CN102190932A introduces a composite phase change energy storage architectural coating, which uses expanded perlite as the carrier of the phase change material, and uses vacuum adsorption to absorb the organic phase change material into the porous structure of the expanded perlite. There is a problem that the adsorption of organic phase change materials in expanded perlite is not tight enough, and it is easy to leak after many cycles
Chinese patent CN102391770A uses melamine-urea-formaldehyde resin as the carrier of phase-change materials, synthesizes phase-change microcapsules by in-situ polymerization, and adds this phase-change microcapsules into coatings to make phase-change energy-saving coatings, because it uses polymers as The inclusions of phase change materials have the disadvantages of low thermal conductivity of phase change microcapsules and slow heat storage and release rates.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paraffin-SiO2-TiO2 phase change microcapsule and preparation method thereof as well as application of microcapsule in preparing heat-accumulation thermal insulation coating
  • Paraffin-SiO2-TiO2 phase change microcapsule and preparation method thereof as well as application of microcapsule in preparing heat-accumulation thermal insulation coating
  • Paraffin-SiO2-TiO2 phase change microcapsule and preparation method thereof as well as application of microcapsule in preparing heat-accumulation thermal insulation coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A paraffin / SiO 2 -TiO 2 Phase change microcapsules, including SiO 2 -TiO 2 The capsule wall and the phase-change material sealed in the capsule wall, the phase-change material is paraffin, and the TiO 2 attached to SiO 2 surface.

[0026] Paraffin / SiO above 2 -TiO 2 The preparation method of phase-change microcapsules, comprises the steps:

[0027] Step 1, add 20g of secondary deionized water to the three-necked flask, adjust the pH of the solution to 2 with hydrochloric acid, add 10ml of ethanol and 10.4g of tetraethyl orthosilicate to the deionized water in sequence, and stir at 60°C until it is in the form of a sol;

[0028] Step 2, dissolving 10g of paraffin in 100% deionized water, then adding sodium lauryl sulfate with 1% paraffin mass to the solution, and ultrasonically emulsifying the solution to obtain a milky white emulsion;

[0029] Step 3, add the emulsion of step 2 into the sol of step 1, stir, after stirring, wait for the liquid to cool and put it ...

Embodiment 2

[0035] A paraffin / SiO 2 -TiO 2 Phase change microcapsules, including SiO 2 -TiO 2 The capsule wall and the phase-change material sealed in the capsule wall, the phase-change material is paraffin, and the TiO 2 attached to SiO 2 surface.

[0036] Paraffin / SiO above 2 -TiO 2 The preparation method of phase-change microcapsules, comprises the steps:

[0037] Step 1, add 20g of secondary deionized water to the three-necked flask, adjust the pH of the solution to 2 with hydrochloric acid, add 10ml of ethanol and 10g of tetraethyl orthosilicate to the deionized water in sequence, and stir at 60°C until it is in the form of a sol;

[0038] Step 2, dissolving 20 g of paraffin in 120 deionized water, then adding sodium lauryl sulfate with 1% paraffin mass to the solution, and ultrasonically emulsifying the solution to obtain a milky white emulsion;

[0039] Step 3, add the emulsion of step 2 into the sol of step 1, stir, after stirring, wait for the liquid to cool and put it in...

Embodiment 3

[0045] A paraffin / SiO 2 -TiO 2 Phase change microcapsules, including SiO 2 -TiO 2 The capsule wall and the phase-change material sealed in the capsule wall, the phase-change material is paraffin, and the TiO 2 attached to SiO 2 surface.

[0046] Paraffin / SiO above 2 -TiO 2 The preparation method of phase-change microcapsules, comprises the steps:

[0047] Step 1, add 30g of secondary deionized water into the three-necked flask, adjust the pH of the solution to 3 with hydrochloric acid, add 20ml of ethanol and 20g of tetraethylorthosilicate to the deionized water in sequence, and stir at 60°C until it is in the form of a sol;

[0048] Step 2, dissolving 30 g of paraffin in 150 deionized water, then adding sodium lauryl sulfate with 2% paraffin mass to the solution, and ultrasonically emulsifying the solution to obtain a milky white emulsion;

[0049] Step 3, add the emulsion of step 2 to the sol of step 1, stir, after stirring, wait for the liquid to cool and put it in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a paraffin-SiO2-TiO2 phase change microcapsule. The paraffin-SiO2-TiO2 phase change microcapsule is formed with oil-phase paraffin as a core and a composite material of titanium dioxide and silicon dioxide as a shell. The invention also discloses a method for preparing the paraffin-SiO2-TiO2 phase change microcapsule by use of a sol-gel method, and finally discloses an application of the paraffin-SiO2-TiO2 phase change microcapsule in preparing a heat-accumulation thermal insulation coating, wherein the coating is prepared from the paraffin-SiO2-TiO2 phase change microcapsule, titanium dioxide, calcium carbonate, a styrene-acrylic emulsion and various auxiliaries. The phase change microcapsule with the composite structure has excellent mechanical properties and excellent optical properties; the preparation method of the phase change microcapsule is simple in process, low in cost and capable of effectively solving the problem of leakage during solid-liquid phase change; the heat-accumulation thermal insulation coating prepared from the microcapsule has excellent heat accumulation and thermal insulation properties, and is capable of effectively improving the thermal comfort of a building and reducing the energy consumption of the building.

Description

technical field [0001] The present invention relates to a kind of paraffin-SiO 2 -TiO 2 The phase-change microcapsule also relates to the preparation method of the above-mentioned phase-change microcapsule, and finally relates to the application of the phase-change microcapsule in preparing heat storage and thermal insulation coatings, and belongs to the field of phase-change materials. Background technique [0002] The increasing shortage of energy is a global problem, and energy issues have caused many economic and social problems. How to use energy efficiently and recyclably, develop and use low-grade energy has become an urgent issue to be solved. All countries in the world regard the development of new energy technology as the core content of future development. my country has now entered a new development period of building a well-off society in an all-round way, and it is urgent to solve the contradictions between population, resources, environment and industrializ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K5/06C09D7/12C09D5/33C09D125/14
Inventor 李敏刘健鹏
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products