A technology of liquid metal and wetting agent, applied in the direction of coating, etc., can solve the problems of difficulty in waste liquid treatment and increase of treatment cost, and achieve the effects of environmental protection in the processing process, low production cost and simple process operation

Active Publication Date: 2017-01-04
GUANGDONG JANUS SMART GRP CO LTD +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the chemical treatment liquid generally contains strong acid, strong alkali and chemical modifiers of other components, the waste liquid increases the treatment cost to a large extent, and there are many difficulties in the treatment of waste liquid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of liquid metal wetting agent and composite material
  • A kind of preparation method of liquid metal wetting agent and composite material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] refer to figure 1 , according to an embodiment of the present invention, the preparation method of the composite material includes the following steps:

[0037] Surface laser treatment of liquid metal substrates to form tiny holes;

[0038] Surface treatment of liquid metal substrates with fine pores with liquid metal wetting agents;

[0039] Injection-molding the liquid metal base material and plastic treated with the liquid metal wetting agent to obtain a composite material integrating liquid metal and plastic;

[0040] Wherein, the liquid metal wetting agent contains an organic modifier for improving the difference in surface tension coefficient between the liquid metal substrate and the plastic.

[0041] The materials involved in the practice of the method of the present invention are as follows.

[0042] 1. Liquid metal: It can be a shaped liquid metal substrate prepared by copper mold suction casting method, liquid quenching method, sputtering method, spray gun...

Embodiment 1

[0063] Preparation of liquid metal wetting agents:

[0064] In 1000 parts of solvent, wherein 350 parts of water, 250 parts of ethanol, 400 parts of ethylene glycol monomethyl ether, add the raw material that has following weight ratio:

[0065] 1) 82 parts of concentrated hydrochloric acid;

[0066] 2) 240 parts of organic modifier

[0067] Among them: 160 parts of maleic acid + 80 parts of malic acid.

[0068] The preparation method of the liquid metal composite material specifically includes the following steps:

[0069] 1) Provide a shaped liquid metal substrate.

[0070] 2) Carry out chemical decontamination treatment on the liquid metal substrate with a cleaning agent to remove the dirt on the metal surface; the chemical decontamination temperature is 80°C, and the decontamination time depends on the specific effect.

[0071] 3) Perform surface ultraviolet laser treatment on the liquid metal after decontamination treatment to form holes with an opening diameter of 10...

Embodiment 2

[0078] Preparation of liquid metal wetting agents:

[0079] In 1000 parts of solvent, wherein 350 parts of water, 350 parts of ethanol, 300 parts of ethylene glycol monobutyl ether, add the raw material that has following weight ratio:

[0080] 1) 265 parts of inorganic acid

[0081] Among them: 200 parts of concentrated hydrochloric acid + 65 parts of concentrated phosphoric acid;

[0082] 2) 150 parts of organic modifier

[0083] Among them: 105 parts of maleic acid + 45 parts of malic acid.

[0084] The preparation method of liquid metal composite material specifically comprises the following steps:

[0085] 1) Provide a shaped liquid metal substrate.

[0086] 2) Carry out chemical decontamination treatment on the liquid metal substrate with a cleaning agent to remove the dirt on the metal surface; the chemical decontamination temperature is 80°C, and the decontamination time depends on the specific effect.

[0087] 3) Perform surface ultraviolet laser treatment on the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
wavelengthaaaaaaaaaa
poweraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method for a composite material, and a liquid metal wetting agent. The method comprises the following steps: (1) carrying out laser treatment on the surface of a liquid metal base material to form fine holes; (2) carrying out surface treatment on the liquid metal base material with the fine holes by using the liquid metal wetting agent; and (3) carrying out injection molding on plastic and the liquid metal base material treated by the liquid metal wetting agent to obtain the composite material integrating liquid metal and the plastic. The liquid metal wetting agent contains an organic modifier for improving a surface tension coefficient difference between the liquid metal base material and the plastic. According to the preparation method for the composite material, and the liquid metal wetting agent, the bonding strength of the liquid metal and the plastic can be improved.

Description

technical field [0001] The invention relates to a preparation method of a liquid metal wetting agent and a composite material. Background technique [0002] Liquid metal (also known as amorphous material) has a unique microstructure of atomic arrangement in short-range order, long-range disorder, and no grain boundary. Compared with corresponding crystal materials, liquid metal has high strength, good scratch resistance, and excellent appearance. Excellent performance such as fashion and high gloss. [0003] Treating the surface of the liquid metal base material with a chemical treatment liquid can form irregular holes on the surface of the liquid metal base material, and then perform integral molding with plastic to prepare a composite material. Since the chemical treatment liquid generally contains strong acid, strong alkali and chemical modifiers of other components, the waste liquid increases the treatment cost to a large extent, and there are many difficulties in the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C45/14B29C45/17C23F1/16
CPCB29C45/14795B29C2045/14803B29C2045/14868B29C2045/1696C23F1/16
Inventor 邓崇浩王长明谢守德
Owner GUANGDONG JANUS SMART GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com