Water-tolerant oil-resistant rubber material

A technology of oil-resistant rubber and rubber, which is applied in the field of rubber materials, can solve the problems of great influence on water and oil resistance, achieve excellent weather resistance, excellent ozone resistance, and improve the effect of flame retardant and heat resistance

Inactive Publication Date: 2014-10-22
宁国日格美橡塑股份有限公司
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to improve the water resistance or oil resistance of rubber materials, people add various compounding components in the process of making rubber products from raw rubber. Various compounding agents have a great influence on the water and oil resistance of rubber products. The current water and oil resistant rubber The material still cannot meet the demand, how to prepare a rubber material with excellent water resistance and oil resistance has become a technical problem that needs to be solved at present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-tolerant oil-resistant rubber material
  • Water-tolerant oil-resistant rubber material
  • Water-tolerant oil-resistant rubber material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] In the following, the technical solutions of the present invention are described in detail through specific examples. In Examples 1-4, the raw materials of a water- and oil-resistant rubber material proposed by the present invention are composed as shown in the following table in parts by weight.

[0014]

[0015]

[0016] Wherein, the particle size of barite powder, calcite powder and brucite powder in Example 1-4 is 50-65 μm, specifically, the particle size can be 50-55 μm or 55-60 μm or 60-65 μm or 50-60 or 55 μm -65μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-tolerant oil-resistant rubber material which is prepared from the following raw materials in parts by weight: 20-30 parts of fluororubber TP (Tetrafluoroethylene-Propylene), 30-35 parts of nitrile silicone rubber, 45-50 parts of hydrogenated butyl rubber, 2-3 parts of a vulcanizing agent DCP (Dicalcium Phosphate), 2.3-3.4 parts of sulfur, 1.2-1.6 parts of epoxy resin, 1.7-2.7 parts of potassium acrylate, 5-8 parts of zinc oxide, 4-9 parts of magnesium oxide, 7-9 parts of aluminum oxide, 10-15 parts of baryte powder, 20-23 parts of calcite in powder, 7-9 parts of brucite powder, 1.6-3.4 parts of brominated polystyrene, 3.4-5.3 parts of brominated polystyrene, 2.8-3.7 parts of a rubber antioxidant 4010NA and 1-1.2 parts of a monoalkoxy titanate coupling agent. The water-tolerant oil-resistant rubber material disclosed by the invention has an excellent oil-resistant water-tolerant performance as well as flame retardant and heat resistant performances and ageing-resistant performance and further has high elasticity, high hardness and high strength.

Description

technical field [0001] The invention relates to the technical field of rubber materials, in particular to a water- and oil-resistant rubber material. Background technique [0002] Rubber materials are non-polar substances. According to the principle of similar compatibility, rubber materials are often easily dissolved in oil, which is not conducive to the use of rubber materials in oil-filled environments, and some rubber materials need to be used in high-humidity environments. The above two usage environments will change the physical and mechanical properties of the rubber material. In order to improve the water or oil resistance of rubber materials, people add various compounding components in the process of making rubber products from raw rubber. Various compounding agents have a great influence on the water and oil resistance of rubber products. The material still cannot meet the demand, and how to prepare a rubber material with excellent water and oil resistance has be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/26C08L83/04C08L27/12C08L63/00C08K13/02C08K3/22C08K3/06
CPCC08L23/26C08K2201/003C08L2201/02C08L2201/08C08L2205/035
Inventor 李元焕
Owner 宁国日格美橡塑股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com