A kind of preparation method of yttrium silicate ceramic powder

A ceramic powder, yttrium silicate technology, applied in coating, metal material coating process, melt spraying and other directions, can solve the problem of difficult to obtain a single crystal product and other problems, achieve stable pH value, high purity, guaranteed The effect of purity

Active Publication Date: 2016-08-17
CENT SOUTH UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The system used in this method is Sc 2 o 3 -Y 2 o 3 -ZrO 2 , Y 2 o 3 -ZrO 2 , La 2 o 3 -Y 2 o 3 -ZrO 2 and other systems, in addition, from the existing data, it is difficult to obtain a product with a single crystal form no matter whether the forward titration method or the reverse titration method is used
In a word, so far, there is no report on the preparation of yttrium silicate ultrafine powder with a single crystal form by reverse co-precipitation method.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of yttrium silicate ceramic powder
  • A kind of preparation method of yttrium silicate ceramic powder
  • A kind of preparation method of yttrium silicate ceramic powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Take the preparation of 10 kg of yttrium silicate ceramic powder as an example. Weigh 7.9 kg Y 2 o 3 Dissolve in excess nitric acid, add deionized water to prepare 1mol / LY(NO 3 ) 3 Clear solution. According to Y 2 SiO 5 Medium SiO 2 % by weight, converted to tetraethyl orthosilicate TEOS ((C 2 h 5 ) 4 SiO 4 ) is 8.1L, the density of tetraethyl orthosilicate is 0.929g / ml, SiO 2 The content is 28%. Measure 8.1L tetraethyl orthosilicate, mix with 8.1L absolute ethanol (ErOH) and 36.4L deionized water (H 2 O) mix, and prepare tetraethyl orthosilicate prehydrolyzate. 1mol / LY(NO 3 ) 3 solution and TEOS:ErOH:H 2 O = 1:1:4 pre-hydrolyzate mix. Take 50L of distilled water and adjust its pH to 9-10 with concentrated ammonia water. Slowly add the above mixed solution into ammonia water with a pH value of 9-10 to carry out chemical co-precipitation reaction, adjust the reaction system with 2-fold diluted ammonia water to keep the pH value at 9-10. During this rea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of yttrium silicate ceramic powder, in particular relates to a preparation method of yttrium silicate ceramic powder for environment barrier coating, and belongs to the technical field of oxide ceramic material preparation. The method comprises the following steps: using a yttrium solution with Y<3+> ion concentration of 0.6-1.5 mol / L as solution A; weighing silicate ester according to a molar ratio of Y to Si being 2: 1; adding alcohol and water in the weighed silicate ester according to a volume ratio of the silicate ester to alcohol to water being 1: 1-2: 2-6 to obtain solution B; uniformly mixing the solutions A and B solution to obtain the mixed solution containing aluminum and silicon; adding the mixed solution containing aluminum and silicon into ammonium hydroxide with pH value of 9-10 at a speed of dropwise adding 0.2-0.5 L of the mixed solution containing aluminum and silicon in 1L of precipitator every minute, and stirring to obtain the co-precipitate; after the reaction is finished, standing, filtering, washing and drying the residue, calcining for at least 4 hours at 800-1000 DEG.C to obtain the Y2SiO5 ceramic composite powder. The method provided by the invention is short in reaction period and good in repeatability; and the obtained product is high in purity and is of a single crystal form.

Description

technical field [0001] The invention relates to a preparation method of yttrium silicate ceramic powder, in particular to a preparation method of yttrium silicate ceramic powder for an environmental barrier coating, belonging to the technical field of oxide ceramic material preparation. The composite powder is used to prepare an environmental barrier coating, and is suitable for high temperature protection on the surface of silicon-based materials such as C / C-SiC composite materials and silicon nitride. technical background [0002] Carbon / carbon-silicon carbide (C / C-SiC) composite material is a ceramic matrix composite material with carbon fiber as the reinforcing phase, which combines the superior mechanical properties of fiber reinforcement and the good chemical and thermal stability of ceramics, and has a high specific Strong, high specific modulus, low density, good oxidation resistance, corrosion resistance, excellent mechanical properties and thermophysical properties...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/16C04B35/505C04B35/622C23C4/10
Inventor 刘怀菲熊翔王雅雷
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com