A method for three-dimensionally judging the fineness of paste printing patterns

A fine and paste technology, applied in the field of fabric printing, to achieve the effects of accurate results, simple and convenient methods, and reliable judgment basis

Inactive Publication Date: 2015-10-28
DONGHUA UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are no reports at home and abroad on the quantitative method for judging the fineness of paste patterns.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for three-dimensionally judging the fineness of paste printing patterns
  • A method for three-dimensionally judging the fineness of paste printing patterns
  • A method for three-dimensionally judging the fineness of paste printing patterns

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A method for three-dimensionally judging the fineness of paste printed patterns, comprising the following steps:

[0025] (1) According to the printing paste prescription: 1% K-type Argosol Red P-4B, 5% urea, 1% resist salt S, 1% sodium bicarbonate, 70% original paste. Adjust the viscosity of the color paste to 10000±1000mPa·s (25±1°C, No. 4 rotor, 30r / min, measured by a rotational viscometer).

[0026] On a flat screen of 180 mesh, the diameter of the magnetic rod is 8mm, the speed of the vehicle is 6m / min, and the magnetic force is 3 # Cotton fabrics were printed with reactive dyes under certain printing conditions. Print a right-angled wedge-shaped pattern with a length of 100mm and a height of 2mm on the fabric.

[0027] (2) After drying the printed wedge-shaped pattern, measure the actual length and height of the wedge-shaped pattern obtained on the fabric;

[0028] (3) Calculate the fineness of the wedge shape to judge the fineness of the printed pattern.

[0...

Embodiment 2

[0036] A method for three-dimensionally judging the fineness of paste printed patterns, comprising the following steps:

[0037] (1) According to the printing color paste prescription: 1% K-type Argosol Red P-4B, 5% urea, 1% resist salt S, 1% sodium bicarbonate, 70% original paste, prepare the printing color paste.

[0038] On a flat screen of 180 mesh, the diameter of the magnetic rod is 8mm, the speed of the vehicle is 6m / min, and the magnetic force is 3 # Cotton fabrics were printed with reactive dyes under certain printing conditions. Print a right-angled wedge-shaped pattern with a length of 100mm and a height of 2mm on the fabric.

[0039] (2) After drying the printed wedge-shaped pattern, measure the actual length and height of the wedge-shaped pattern obtained on the fabric;

[0040] (3) Calculate the fineness of the wedge shape to judge the fineness of the printed pattern.

[0041]

[0042] In the formula: l is the actual length of the wedge-shaped pattern on th...

Embodiment 3

[0048] A method for three-dimensionally judging the fineness of paste printed patterns, comprising the following steps:

[0049] (1) Cotton fabric reactive dye printing paste prescription: 1% KN type Argosol black B 133%, 5% urea, 1% resist salt S, 1% sodium bicarbonate, 70% raw paste (sodium alginate original Paste mass fraction is 3%).

[0050] Prescription of disperse dye printing paste for polyester fabric: 1% Yatelong Black SW-FG, 1% urea, 0.1% tartaric acid, 70% raw paste (mass fraction of sodium alginate raw paste is 3%).

[0051] Prescription of disperse / reactive homogeneous printing color paste for polyester-cotton fabric: 1% Artron Black SW-FG, 1% KN Argosol Black B133%, 5% Urea, 1% Resist Salt S, 1% Sodium Bicarbonate , 70% raw paste (mass fraction of sodium alginate raw paste is 3%).

[0052] On a flat screen of 180 mesh, the diameter of the magnetic rod is 8mm, the speed of the vehicle is 6m / min, and the magnetic force is 3 # Printing under the printing conditi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a three-dimensional rapid judgment method for the fineness of a thickener-printed flower form. The method comprises the following steps: (1) preparing printing paste and printing a right-angle wedge-shaped pattern with a length of 100mm and a height of 2mm on a piece of fabric; (2) drying the printed right-angle wedge-shaped pattern, and measuring the actual length and height of the right-angle wedge-shaped pattern on the fabric; (3) calculating the right-angle wedge-shaped pattern, so as to judge the fineness of the printed flower form. In an evaluation method provided by the invention, the fineness of a wedge shape needs to be more than 70%; the more the value of the fineness is, the higher the fineness of the printed flower form is; the printing property of the fine flower form prepared from a thickener is relatively good; the invention provides the evaluation method for the fineness of the thickener-printed flower form, which has the advantages of being relatively high in quantification, simple and easy to operate; the printing property of the fine flower form of a thickener can be accurately reflected.

Description

technical field [0001] The invention belongs to the field of fabric printing methods, in particular to a method for three-dimensionally judging the fineness of patterns printed with paste. Background technique [0002] With the advancement of high-mesh screen printing and printing technology, the printed pattern tends to be more refined, and strives to accurately show the pattern on the fabric that conforms to the original design spirit. The fineness of the pattern is high, and the pattern printed on the fabric is closer to the pattern originally designed. [0003] At present, the method of judging the fineness of paste pattern is limited to the traditional method, and there is no quantitative unified standard. It has been reported in the literature that the fineness of printed patterns is evaluated by visual evaluation method. There are also reports in the literature that the sharpness obtained by printing wedge-shaped patterns, that is, the ratio of the actual wedge-shap...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G01N33/00
Inventor 王莉莉刘保江张俊胡春艳金雅雯闵洁
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap