Wear-resisting oxford fabric

A slurry and coating technology, applied in the field of Oxford cloth, can solve the problems of low coating stability, no fabric performance, and reduced wear resistance, and achieve the effect of thick hand feeling, good coating stability, and high strength

Inactive Publication Date: 2014-05-07
NANTONG QUANJI TEXTILE COATING
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing high wear-resistant Oxford cloth mainly improves the wear resistance of Oxford cloth by coating a layer of wear-resistant layer on the fabric, but the effect is not ideal. On the one hand, there is no performance for the fabric, and on the other hand On the one hand, the coating stability is low, resulting in an overall decrease in wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A wear-resistant Oxford cloth, comprising a fabric layer and at least one size coating, wherein the fabric layer is interwoven with 150D polyester filaments, and the size coating is composed of the following components in parts by mass: silicone resin 60 parts, 5 parts of silane coupling agent, 3 parts of crosslinking agent, 4 parts of aluminum silicate fiber, 6 parts of copper oxide powder and 10 parts of toluene.

Embodiment 2

[0013] A wear-resistant Oxford cloth, comprising a fabric layer and at least one size coating, wherein the fabric layer is interwoven with 350D polyester filaments, and the size coating is composed of the following components in parts by mass: silicone resin 80 parts, 10 parts of silane coupling agent, 6 parts of crosslinking agent, 8 parts of aluminum silicate fiber, 10 parts of copper oxide powder and 15 parts of toluene.

Embodiment 3

[0015] A wear-resistant Oxford cloth, comprising a fabric layer and at least one size coating, wherein the fabric layer is interwoven with 200D polyester filaments, and the size coating is composed of the following components in parts by mass: silicone resin 75 parts, 6 parts of silane coupling agent, 5 parts of crosslinking agent, 5 parts of aluminum silicate fiber, 70 parts of copper oxide powder and 12 parts of butanone.

[0016] The excellent effects achieved by the present invention will be further illustrated through specific experiments below.

[0017] The Oxford cloth made by the above-mentioned specific embodiment is made into a model, and the untreated Oxford cloth is taken as a control group, and tested according to the abrasion resistance test standard of ISO5981, the results show that:

[0018] Abrasion resistance (back): 1005 for Example 1; 1083 for Example 2; 1117 for Example 3; 712 for the control group.

[0019] It can be seen that the Oxford cloth provided b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a wear-resisting oxford fabric comprising a shell fabric layer and at least one layer of sizing agent coating, wherein the shell fabric layer is interweaved by 150-350D polyester filament yarn; and the sizing agent coating is composed of the following components in parts by weight: 60-80 parts of organic silicon resin, 5-10 parts of silane coupling reagent, 3-6 parts of cross-linking agent, 4-8 parts of alumina silicate fiber, 6-10 parts of copper oxide powder and 10-15 parts of solvent. The wear-resisting oxford fabric provided by the technical scheme is high in strength, firm, wear-resisting and firm in handfeel, has good coating stability and can be used as a material of products of cases, traveling bags, tent bottoms, and the like.

Description

technical field [0001] The invention relates to an Oxford cloth. Background technique [0002] Oxford cloth, also known as Oxford spinning, is made of finer combed high-count yarns as double warps, and thicker weft yarns are interwoven with weft-heavy flat weave. There are many varieties and styles. In daily life, processed Oxford cloth is often used as a material for bags and other products that require high friction performance. According to the requirements of these products, Oxford fabrics can be coated to better meet people's needs. [0003] The existing high wear-resistant Oxford cloth mainly improves the wear resistance of Oxford cloth by coating a layer of wear-resistant layer on the fabric, but the effect is not ideal. On the one hand, there is no performance for the fabric, and on the other hand On the one hand, the low stability of the coating leads to an overall decrease in wear resistance. Contents of the invention [0004] Purpose of the invention: To addr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/643D06M11/79D06M11/42D03D15/00D06M101/32D03D15/283D03D15/30
Inventor 吴强曹宗政陈凤周一丹马苏扬廖萍倪永超钱永明
Owner NANTONG QUANJI TEXTILE COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com