Production method of phosphor copper ball for electroplating

A production method, the technology of phosphor copper balls, applied in the direction of electrodes, metal rolling, etc., can solve the problems of large consumption, and achieve the effect of reducing consumption and uniform metallographic structure

Inactive Publication Date: 2014-04-23
JINCHUAN GROUP LIMITED
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Phosphor bronze balls produced by many phosphor bronze ball manufacturers are very good in terms of appearance, gloss, and surface quality. They are used as anode phosphor copper for electroplating in phosphor bronze balls. Balls, some products will have a problem of excessive consumption compared with the same period last year

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of phosphor copper ball for electroplating
  • Production method of phosphor copper ball for electroplating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0015] A method for producing phosphor bronze balls for electroplating. The production process adopts the upward drawing method, and the operation steps include: producing phosphor bronze rods by upward drawing method → ​​rolling → metallographic analysis (the crystal grains are extremely coarse, see figure 1 ) → production of phosphor copper rods by up-drawing method → ​​rolling → metallographic analysis (the grains have been reduced, but still relatively coarse) → production of phosphor-bronze rods by up-drawing method → ​​pier thickening → rolling → metallographic analysis → ( Grain refinement, uniform structure, dense, see figure 2 ) → packaged delivery.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method of a phosphor copper ball for electroplating, and relates to a method which adopts a metallographic analysis method to control the quality of a phosphor copper ball for electroplating. The production method is characterized by adopting an up-drawn method; after the rolling of phosphor copper rods, metallographic analysis is carried out on the phosphor copper rods so as to judge whether the phosphor copper rods meet the preset metallographic structure analysis standards of finished phosphor copper rod on crystal particle fineness, tissue homogeneity, and compactness; the unqualified phosphor copper rods are returned to the rolling process by adopting the up-drawn method, and the rolling-judging-rolling process is continuously repeated until the phosphor copper rods meet the standards on crystal particle fineness, tissue homogeneity, and compactness so as to finish the preparation of phosphor copper balls. The production method utilizes metallographic analysis to observe the crystal particle size of phosphor copper ball, and has the advantages of directness, simplicity, and visualization. The prepared phosphor copper ball is used as a positive pole material for electroplating, and has the advantages of uniform and compact metallographic structure; moreover the fineness of the crystal particle size is strictly controlled to avoid the existence of crude and big crystal particles, and thus the consumption amount of phosphor copper ball during the electroplating process is effectively reduced.

Description

technical field [0001] The invention discloses a method for producing phosphor bronze balls for electroplating, and relates to a method for controlling the quality of phosphor bronze balls for electroplating by metallographic analysis. Background technique [0002] Phosphor bronze balls are mainly used in the electroplating of double-sided boards and multi-layer boards in printed circuit boards, in addition to electroplating in hardware and other industries. The production of phosphor bronze balls usually adopts horizontal continuous casting to produce phosphor bronze balls and upward drawing method to produce phosphor bronze balls. [0003] At present, there are domestic standards for the composition of phosphor bronze balls, and the quality of phosphor bronze balls is usually judged from the chemical composition and appearance quality. Phosphor bronze balls produced by many phosphor bronze ball manufacturers are very good in terms of appearance, gloss, and surface quality...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D17/10B21B1/46
Inventor 陈琴袁承人苏俊斌赵有军赵多生
Owner JINCHUAN GROUP LIMITED
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products