A kind of al-fe-cu-mg-sb aluminum alloy for automobile wire and its wire harness

A technology of al-fe-cu-mg-sb and automotive wiring harness, which is applied in the field of aluminum alloy, can solve problems such as shedding, and achieve the effect of overcoming the problem of processing performance and realizing light weight

Active Publication Date: 2015-12-30
ANHUI JOY SENSE CABLE
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the wires of the electric wiring body of the mobile body are riveted to the terminals, and if creep occurs, there is a risk of falling off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of al-fe-cu-mg-sb aluminum alloy for automobile wire and its wire harness

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An aluminum alloy for automotive wires, the components and weight percentages of each component are as follows (total weight: 1T):

[0034] components

Fe

Cu+Mg

Sb

Si

RE

Al

Weight (Kg)

2

0.1

0.01

/

/

997.89

Weight percentage (%)

0.2

0.01

0.001

/

/

99.789

[0035] In the above-mentioned aluminum alloy materials, it is preferable to add a certain amount of Sb. After adding Sb to the aluminum alloy, it can form stable multi-component compounds with aluminum, iron, magnesium, and copper in the alloy. The density of these compounds is similar to that of the alloy liquid. When the alloy is solidified, they are first precipitated, forming a network framework, suspended in the alloy liquid, and hindering the floating of the aluminum-rich phase and the falling of the iron-rich, magnesium, and copper phases, thereby inhibiting the specific gravity segregation of the alloy that is e...

Embodiment 2

[0043] An aluminum alloy for automotive wires, the components and weight percentages of each component are as follows (total weight: 1T):

[0044]

[0045] Among the above-mentioned aluminum alloy materials, the content of Si was compared. An appropriate amount of Si can increase the recrystallization temperature and refine the grains, while exceeding a certain content will reduce its electrical conductivity. In the process of implementation, it was found that the Si content Excessive samples are prone to breakage during the wire drawing process.

[0046] The method for preparing an aluminum alloy wire core by using the above-mentioned aluminum alloy material, the specific steps are as follows:

[0047] a. Melting and casting: add aluminum alloy components according to the above ratio, melt at 730°C, cast ingots at 670°C, and then roll into alloy rods after solution treatment and aging treatment. The aging treatment here is preferably at 140°C or at higher temperatures,

...

Embodiment 3

[0052] An aluminum alloy for automotive wires, the components and weight percentages of each component are as follows (total weight: 1T):

[0053] components

Fe

Cu+Mg

Sb

Si

RE

Al

Weight (Kg)

12.0

5.0

2.0

0.50

2.5

978.00

Weight percentage (%)

1.20

0.50

0.20

0.05

0.25

97.80

[0054] In the above-mentioned aluminum alloy materials, it is preferable to add a certain amount of RE elements, wherein Ce and La account for 50% of the total RE content, and rare earths can significantly improve the electrical properties of the alloy. In the present invention, rare earths are added to the aluminum alloy to make the aluminum alloy melt and cast Increase the supercooling of the composition, refine the grain, reduce the secondary grain distance, reduce the gas and inclusions in the alloy, and make the inclusion phase tend to be spheroidized. It can also reduce the surface tension of the melt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses an Al-Fe-Cu-Mg-Sb aluminum alloy for an automotive wire, a manufacturing method of the aluminum alloy, and a wiring harness made of the aluminum alloy. The Al-Fe-Cu-Mg-Sb aluminum alloy for the automotive wire comprises the following ingredients in percentage by weight: 0.2-1.4wt% of Fe, 0.01-0.5wt% of Cu and Mg, 0.001-0.2wt% of Sb, and the balance of Al and inevitable impurities. The mechanical strength and the tensile properties of the alloy can be improved by adding an Fe element; the high temperature creep resistance also can be obviously improved by Fe; the anti-fatigue performance of the alloy is improved; the strength and the high-temperature creep properties of the alloy can be improved by adding Cu and Mg; the anti-fatigue performance can be improved; the yield limit of the alloy can be improved by adding Sb; meanwhile, the alloy has superplasticity, so as to be drawn into a very thin alloy wire.

Description

Technical field [0001] The invention relates to a wire harness that can be used as a battery cable, wire harness or engine cable in a mobile carrier, and belongs to the field of aluminum alloys. Background technique [0002] At present, the automobile industry is developing rapidly around the world. The automobile industry has not only become a pillar industry in developed countries such as the United States and Japan, but also in some developing countries including China. As one of the important supporting products of automobiles, automobile lines It has good market prospects in terms of scale output and variety demand. [0003] At the same time, automobiles are developing in the direction of miniaturization and lightweight. The control circuits of various electronic devices are increasing, and the wiring locations in motor vehicles are increasing. In order to achieve the purpose of energy saving and consumption reduction, automobile low-voltage wires are required to develo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22C1/02H01B1/02H01B13/012
Inventor 林泽民
Owner ANHUI JOY SENSE CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com