Preparation method of PVC (Polyvinyl Chloride) sectional material with surface coated with metal film

A metal-coated and metal-film technology, applied in the field of composite profile preparation, can solve problems such as uneven bonding between metal and PVC, difficult continuous production, and unfavorable production and processing, and achieves strong plasticity and solves problems of easy aging, stickiness, etc. Knots uniform and strong effect

Inactive Publication Date: 2014-04-16
山东华信塑胶股份有限公司
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the above method is to apply the adhesive on the surface of the inner lining without compounding the PVC profile through a special extruder, the bonding between the metal and the PVC is uneven, the bonding strength is not high, and it is not easy to carry out continuous production.
The prepared PVC-aluminum-plastic co-extruded profile has low plasticity and is not conducive to production and processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The preparation of PVC profiles covered with aluminum film, the thickness of the aluminum film is 0.3mm, the steps are as follows:

[0036] (1) Mixing: 100kg SG-5 PVC resin powder, 10kg light calcium carbonate, 3.5kg calcium zinc stabilizer, 0.8kg stearic acid, 0.5kg calcium stearate, 0.5kg PE wax, 6kg CPE, 3kg of anti-impact ACR, 1kg of processing aid type ACR and 5kg of titanium dioxide were mixed in a high-speed mixer and the temperature was controlled at 120°C. After reaching the temperature, it was transferred to a cold mixer to cool to 40°C and discharged to obtain a mixed material;

[0037] (2) Co-extrusion, vacuum cooling and shaping: Put the hot melt adhesive into the 45-type single-screw extruder, and the temperature of the extruder is controlled at 140-180°C; put the compounded material into the 65-type conical twin-screw extruder In the extruder, the temperature of the extruder is controlled at 160-205°C; then it is extruded in a double-channel co-extrusion ...

Embodiment 2

[0041] The preparation of the PVC profile with copper film on the surface, the thickness of the copper film is 2mm, the steps are as follows:

[0042] (1) Mixing: 100kg SG-4 type PVC resin powder, 12kg active calcium carbonate, 3.8kg calcium zinc stabilizer, 0.5kg stearic acid, 0.3kg calcium stearate, 0.6kg PE wax, 3kg CPE, 3kg Impact-resistant ACR, 0.8 kg of processing aid type ACR and 4 kg of titanium dioxide were mixed in a high-speed mixer and the temperature was controlled at 125°C. After reaching the temperature, it was transferred to a cold mixer to cool to 45°C and discharged to obtain a mixed material;

[0043] (2) Co-extrusion, vacuum cooling and shaping: Put the hot melt adhesive into the 45-type single-screw extruder, and the temperature of the extruder is controlled at 135-175°C; put the compounded material into the 80-type conical twin-screw extruder In the extruder, the temperature of the extruder is controlled at 165-200°C; then it is extruded in a double-chann...

Embodiment 3

[0047] The preparation of the PVC profile covered with stainless steel film, the thickness of the stainless steel film is 6mm, the steps are as follows:

[0048] (1) Mixing: 100kg SG-5 type PVC resin powder, 25kg active calcium carbonate, 5kg organotin stabilizer, 0.5kg stearic acid, 0.5kg calcium stearate, 1.2kg PE wax, 10kg CPE, 5kg anti Punch ACR, put 3kg of processing aid type ACR and 8kg of titanium dioxide into a high-speed mixer and mix and control the temperature at 135°C. After reaching the temperature, transfer to a cold mixer to cool to 30°C and discharge to obtain the mixed material;

[0049] (2) Co-extrusion, vacuum cooling and shaping: Put the hot melt adhesive into the 55-type single-screw extruder, and the temperature of the extruder is controlled at 150-180°C; put the compounded material into the 90-type parallel twin-screw extruder In the extruder, the temperature of the extruder is controlled at 180-205°C; then it is extruded in a double-channel co-extrusion...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a PVC (Polyvinyl Chloride) sectional material with surface coated with a metal film. The PVC sectional material with the surface coated with the metal film is prepared by material mixing, co-extrusion, vacuum cooling and sizing, coating of an aluminum film on the surface of the sectional material, cutting and molding. According to the preparation method provided by the invention, a PVC raw material and hot melt adhesive are compounded together by a way of co-extrusion, so that the bonding strength of the hot melt adhesive is high, the bonding of the metal film is uniform and strong, the bonding strength is high, delamination is unlikely to occur, and the continuous production of the hot melt adhesive, PVC raw material powder and PVC sectional material products with the surfaces coated with the metal films can be realized.

Description

technical field [0001] The invention relates to a preparation method of a PVC profile coated with a metal film on the surface, and belongs to the technical field of composite profile preparation. Background technique [0002] The materials used in the doors and windows of housing construction have increasingly replaced the original wooden windows and steel windows with aluminum alloy or plastic steel, and the use of plastic steel doors and windows is more common. Plastic-steel doors and windows have many advantages, and are known as a new generation of energy-saving doors and windows rising after wooden windows, steel windows, and aluminum alloy windows. Compared with aluminum windows and steel windows, they are superior in sealing, heat preservation, and corrosion resistance. Coordinated with similar buildings, it has better aesthetics and can meet individual needs, and has good fire resistance and insulation. However, plastic steel profiles will age and change color under...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B37/12B32B27/06B32B27/30B32B15/082C08L27/06C08L23/28C08K13/02C08K3/26C08K3/22C09J123/08C09J193/04B29C47/92B29C48/92
CPCB29C48/151B29C48/40B29C48/92B29C2948/92704B29C2948/92895
Inventor 汤毅李小虎
Owner 山东华信塑胶股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com