Anti-corrosion coating

A technology of anti-corrosion coatings and raw materials, applied in the field of coatings, to achieve excellent boiling water resistance, good curing activity, and improve the effect of temperature denaturation resistance

Inactive Publication Date: 2014-04-02
SHANDONG LANXING WASHING & ANTI CORROSION
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The coating can form a uniform, hydrophobic, elastic and non-porous surface, with a total thickness of 200μm-300μm. The thermal conductivity of the high-temperature epoxy modified urushiolphthalein anti-corrosion coating is 2.134w / m??k, and the coating thickness is thin , so the effect on the heat transfer coefficient is very small. Since the anti-corrosion coating is smooth and not easy to scale, the overall thermal conductivity of the heat exchanger tube bundle with epoxy-modified urushiolphthalein anti-corrosion is better than that of the heat exchanger without anti-corrosion and scaling Bundle, but still needs further improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] formula:

[0026] Epoxy: 25%

[0027] Modified urushiolphthalein resin: 30%

[0028] Titanium nanoparticles: 8%

[0029] Pigments and fillers: 12%

[0030] Curing agent: 10%

[0031] Solvent: 15%.

[0032] Wherein, the curing agent is a capsule curing agent, the capsule curing agent includes a core material and a wall material, the particle diameter of the capsule curing agent is 10 μm, the core material is vinyl diamine, and the wall material is polymethyl methacrylate ester.

[0033] The pigment and filler are talc powder, graphite powder, aluminum powder and pigment; the mass ratio of the talc powder, graphite powder, aluminum powder and pigment is 20:5:3:10; the pigment is titanium dioxide.

[0034] The solvent is ethanol and acetic acid, and the mass ratio of ethanol and acetic acid is 3:1.

Embodiment 2

[0036] formula:

[0037] Epoxy: 30%

[0038] Modified urushiolphthalein resin: 30%

[0039] Titanium nanoparticles: 5%

[0040] Pigment and filler: 10%

[0041] Curing agent: 10%

[0042] Solvent: 15%.

[0043]Wherein, the curing agent is a capsule curing agent, the capsule curing agent includes a core material and a wall material, the particle diameter of the capsule curing agent is 10 μm, the core material is vinyl diamine, and the wall material is polymethyl methacrylate ester.

[0044] The pigment and filler are talc powder, graphite powder, aluminum powder and pigment; the mass ratio of the talc powder, graphite powder, aluminum powder and pigment is 20:5:3:10; the pigment is zinc oxide. The solvent is ethanol.

Embodiment 3

[0046] formula:

[0047] Epoxy: 35%

[0048] Modified urushiolphthalein resin: 25%

[0049] Titanium nanoparticles: 5%

[0050] Pigment and filler: 10%

[0051] Curing agent: 10%

[0052] Solvent: 15%.

[0053] Wherein, the curing agent is a capsule curing agent, the capsule curing agent includes a core material and a wall material, the particle diameter of the capsule curing agent is 10 μm, the core material is vinyl diamine, and the wall material is polymethyl methacrylate ester.

[0054] The pigments and fillers are talcum powder, graphite powder, aluminum powder and pigments; the mass ratio of the talc powder, graphite powder, aluminum powder and pigments is 20:5:3:10; the pigments are titanium dioxide and zinc oxide. The solvent is ethanol.

[0055] The working performance of the anticorrosion coating of the present invention is as follows and Table 1.

[0056] (1) Acid fog-resistant 70mm×150mm×5mm ordinary carbon steel is coated with four layers, the dry film thi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-corrosion coating, belonging to the technical field of coatings. The anti-corrosion coating solves the problems of poor corrosion-resistant effect and short corrosion-resistant life of the traditional coating. The anti-corrosion coating comprises the following raw materials in percentage by weight: 25%-40% of epoxy resin, 25%-40% of modified paint phenolphthalein resin, 5%-10% of titanium nanoparticles, 10%-15% of pigment fillers, 10%-15% of solidifying agents and 15%-20% of solvents. According to the anti-corrosion coating, the solidifying agents are capsule solidifying agents which take ethylene diamine as a core material and polymethyl methacrylate as a wall material and overcome the defects of the traditional epoxy resin solidifying agent, so that the temperature change resistance of the coating can be effectively enhanced; talcum powder and graphite can not only be taken as the components of the pigment fillers, but also have flame-retardant effects. The anti-corrosion coating disclosed by the invention has the advantages of resistance to the corrosion of liquid mediums, such as acid, alkali, salt, organic solvents, oil and the like as well as resistance to boiling water, can be used for a long time in an environment at 220 DEG C, keeps the characteristic of ultra durability of natural raw lacquer, and has no anaphylactic reaction on human bodies.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an anti-corrosion coating. Background technique [0002] With the continuous development of industrial technology and the use of metal materials more and more widely, the corrosion of metal and its components has spread to all fields of the national economy, causing huge losses to human society. In order to reduce the loss of corrosion, people have taken many protective measures, but so far the most common, economical and practical protective measures are paint protection. Among various anti-corrosion technologies, the anti-corrosion technology of paint is the most widely used. It is widely used due to the characteristics of simple construction, economical application, and not being restricted by equipment area and shape. Among the many types of coatings, epoxy resin plays an important role in anti-corrosion coatings. It is widely used as a coating material for metal anti-corro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D193/00C09D5/10C09D5/18C09D7/12
Inventor 姬玉林吴振刘一总许山谢宗仁
Owner SHANDONG LANXING WASHING & ANTI CORROSION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products