A kind of preparation method of organic silane modified high adhesion solid acrylic resin

A solid acrylic and acrylic resin technology, used in coatings, powder coatings, polyester coatings, etc., can solve the problems of poor adhesion of powder coatings, decreased coating storage, affecting the weather resistance and boiling resistance of coating films. , to achieve the effect of improving boiling resistance and improving adhesion

Active Publication Date: 2016-04-20
六安捷通达新材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for some special substrates such as glass, stainless steel, galvanized sheet, ceramics, etc., the usual powder coatings have poor adhesion, which affects the application properties of the coating film such as weather resistance and water boiling resistance, and limits the application properties of powder coatings. Coating application range
At present, organic silanes can be introduced into powder coatings through physical methods, usually by using ordinary liquid silane coupling agents, and adding them into powder coatings through filler dispersion. This method can improve the adhesion of coatings to a certain extent, but the operation It is inconvenient, and often reduces the storage performance of the coating, and even has a certain adverse effect on the solvent resistance and water boiling resistance of the coating film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of organic silane modified high adhesion solid acrylic resin
  • A kind of preparation method of organic silane modified high adhesion solid acrylic resin
  • A kind of preparation method of organic silane modified high adhesion solid acrylic resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Add 250g of toluene to a 1000ml four-necked flask equipped with a stirring device, condenser, dropping funnel, thermometer and nitrogen inlet, fill it with nitrogen, heat to reflux, drop the monomer mixture (see Table 1 for the formula), drop Adding time is controlled at 3.5 hours. After the dropwise addition is completed, cool down to 70°C and keep the reaction at this temperature for 3 hours. Dissolve 3g of 2,2′-azobisisobutyronitrile with 20g of toluene, add it to the reaction system at one time, and keep it warm The reaction was refluxed for 1.5 hours. Use normal pressure distillation to remove most of the solvent. When a small amount of solvent remains, you can use reduced pressure distillation to remove the solvent, discharge while hot, cool, and pulverize. Finally, the product silane-modified acrylic resin 1 was obtained.

[0019] The preparation method of Examples 2-3 is the same as that of Example 1. The ratio of the monomer mixture is shown in Table 1. Silane...

Embodiment 4

[0024] Add 250g of toluene to a 1000ml four-necked flask equipped with a stirring device, condenser, dropping funnel, thermometer and nitrogen inlet, fill it with nitrogen, heat to reflux, drop the monomer mixture (see Table 2 for the formula), drop The adding time was controlled to be 3.5 hours. After the dropwise addition, the temperature was lowered to 90° C., and the temperature was kept at this temperature for 3 hours, and 2 g of tert-butyl peroxide dissolved in 20 g of toluene was added to the reaction system at one time, and then kept at reflux for 1 hour. Use normal pressure distillation to remove most of the solvent. When a small amount of solvent remains, you can use reduced pressure distillation to remove the solvent, discharge while hot, cool, and pulverize. Finally, a silane-modified acrylic resin 4 was obtained. The experimental results are shown in Table 2.

Embodiment 5-6

[0026] The preparation method is the same as in Example 4. The monomer mixture formula is shown in Table 2, and silane-modified acrylic resins 5-6 were prepared. The experimental results are shown in Table 2.

[0027] Table 2

[0028]

[0029] *: 3-Methacryloxypropyltriethoxysilane

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing high-adhesive force solid acrylic resin modified by organosilane. The method disclosed by the invention can be used for preparing the high-adhesive force solid acrylic resin by introducing an organosilane monomer into acrylic resin through a chemically bonding mode; the prepared modified solid acrylic resin as an additive is added to a powder coating system, can outstandingly enhance the adhesive force of a powder coating layer on a substrate and specific substrates, such as a galvanized plate and stainless steel, especially, cannot influence the storage stability of the powder coating due to excellent self characteristics of the solid acrylic resin and achieves certain improvement on the solvent resistance and boiling resistance of the powder coating layer.

Description

technical field [0001] The invention relates to the technical field of paint additives, in particular to a preparation method of organosilane-modified high-adhesion solid acrylic resin. Background technique [0002] Compared with liquid coatings, powder coatings do not use solvents, so there is no solvent volatilization during the application process, and they have the advantages of high recycling rate, easy operation, high productivity, and fast drying of coating films. Therefore, they are widely used in automobiles, household appliances, machinery, construction, and ships. And other fields are widely used to replace liquid paint. However, for some special substrates such as glass, stainless steel, galvanized sheet, ceramics, etc., the usual powder coatings have poor adhesion, which affects the application properties of the coating film such as weather resistance and water boiling resistance, and limits the application properties of powder coatings. The scope of applicatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F230/08C08F220/14C08F220/18C08F212/08C09D7/12C09D5/03C09D167/00
Inventor 鲍远志翁世兵
Owner 六安捷通达新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com