Mineral waste residue liquid composite grinding aid and preparation method thereof

A grinding aid and liquid technology, which is applied in the preparation of slag liquid compound grinding aid, and in the field of slag liquid compound grinding aid, can solve the problems of rising prices, expensive grinding aids, and restrictions on popularization and application, and achieve sufficient supply, Improve the distribution and shape of powder particles, and the effect of simple processing and preparation

Active Publication Date: 2014-02-12
辽宁天宝华瑞建材有限公司
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the increasing shortage of world oil resources, the price of triethanolamine, the main raw material of grinding aids, continues to rise. Therefore, triethanolamine grinding aids are expensive, and their popularization and application are limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mineral waste residue liquid composite grinding aid and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] First, add 5 kg of sodium hexametaphosphate to 90 kg of water, heat and stir slightly, the temperature is 20 ° C, after it is completely dissolved, add 5 kg of sodium lauryl sulfate into the solution, continue heating, the temperature does not exceed 38°C, stirring and dissolving. Finally, 18 kg of trimixed alcohol, 7 kg of ethyl acetate and 8 kg of molasses were added to the solution, stirred evenly, and then cooled and filtered. The mixed alcohol is a mixture of two or three of industrial grade ethylene glycol, diethylene glycol and triethylene glycol.

Embodiment 2

[0028] First, add 2 kg of sodium hexametaphosphate to 95 kg of water, heat and stir slightly, the temperature is 20 ° C, after it is completely dissolved, add 2 kg of sodium lauryl sulfate into the solution, continue heating, the temperature does not exceed 38°C, stirring and dissolving. Finally, 17 kg of trimixed alcohol, 8 kg of ethyl acetate and 8 kg of molasses were added to the solution, stirred evenly, and then cooled and filtered. The mixed alcohol is a mixture of two or three of industrial grade ethylene glycol, diethylene glycol and triethylene glycol.

Embodiment 3

[0030] First, add 1 kg of sodium hexametaphosphate to 85 kg of water, heat and stir slightly, the temperature is 20°C, after it is completely dissolved, add 1 kg of sodium lauryl sulfate into the solution, continue heating, the temperature does not exceed 38°C, stirring and dissolving. Finally, 16 kilograms of trimixed alcohol, 6 kilograms of ethyl acetate and 6 kilograms of molasses were added into the solution and stirred evenly, and the mixture was cooled and filtered. The mixed alcohol is a mixture of two or three of industrial grade ethylene glycol, diethylene glycol and triethylene glycol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a mineral waste residue liquid composite grinding aid and a preparation method thereof. The mineral waste residue liquid composite grinding aid is prepared from the following raw materials: 15-20 parts by weight of mixed alcohol, 5-10 parts by weight of ethyl acetate, 5-10 parts by weight of molasses, 1-10 parts by weight of lauryl sodium sulfate, 1-10 parts by weight of sodium hexametaphosphate and 800-100 parts by weight of water. The mineral waste residue liquid composite grinding aid has low toxicity, does not volatile and is stable in sources, sufficient in supplies, simple to process and prepare and low in cost; after granulated blast-furnace slag is doped in the mineral waste residue liquid composite grinding aid, the distribution and the morphology of separate particles can be improved, and the quality of mineral waste residue micro powder is not affected; the mineral waste residue liquid composite grinding aid has the advantages of increasing the yield and improving the quality of the mineral waste residue micro powder and meanwhile greatly reduces the energy consumption. The mineral waste residue liquid composite grinding aid has stable property, high cost performance and wide adaptability, is low in cost and mixing amount and can be used for improving the grinding effect and increasing the yield of a grinder by above 15%, the specific surface area of the mineral waste residue micro powder by 4.7%-6.2% under the condition of the same grinding time and the activity index of the mineral waste residue micro powder.

Description

technical field [0001] The invention relates to an additive in the field of slag fine powder production. Specifically, the present invention relates to a slag liquid composite grinding aid, and in addition, the present invention also relates to a preparation method of the slag liquid composite grinding aid. Background technique [0002] Granulated blast furnace slag is the main waste slag produced when smelting pig iron. According to the calculation of about 0.5 tons of slag produced in the production of 1 ton of pig iron, the granulated blast furnace slag produced nationwide in 2012 alone was about 360 million tons. How to utilize slag solid waste is a subject that Chinese metallurgists have been studying for many years, and it is also a practical problem that should be solved emphatically in developing circular economy and building a conservation-minded and environment-friendly society. Because granulated blast furnace slag is used as cement active admixture in cement...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/16C04B22/16C04B103/52
Inventor 孙小巍李殿平王玲玲牛晚扬傅柏权王丽华
Owner 辽宁天宝华瑞建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com