Method for manufacturing a part having a complex shape by flash sintering, and device for implementing such a method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for rapid sintering, component applications in blade support elements, engine elements, turbines, etc.
Active Publication Date: 2014-01-08
CENT NAT DE LA RECHERCHE SCI
View PDF10 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
As far as the inventors are aware, rapid sintering has never been applied to fabricate components as complex as
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0055] figure 1 A turbine blade preform PF made of TiAl by the rapid sintering method according to the invention is shown. This preform, with a height of 36 mm, was essentially the same as the finished blade, requiring only one finishing step to remove about 0.5 mm of material thickness. Accordingly, the preform may qualify as being "near finished size". The material thickness to be removed can be reduced to a value of about 0.1 mm, which corresponds to a layer in which the material is contaminated with graphite. Just like the ready-to-use blade, the preform PF consists of a solid base B with a complex shape that cannot be defined by a small number of simple geometric shapes, and a sheet shape in the form of a slanted shell with a pronounced slenderness along the axis "x" Part V. It can be immediately noticed that the shape of this part is more complex than that of all the objects manufactured by rapid sintering described in the above-mentioned prior art documents.
[0056...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
porosity
aaaaa
aaaaa
porosity
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a method for manufacturing a metal, ceramic, or composite part (PF) by flash sintering, which comprises simultaneously applying, inside a die (M), a uniaxial pressure and an electric current to a device containing a powder constituent material, said uniaxial pressure being applied by means of at least two pistons (P1, P2) which slide toward one another inside said die and each of which has a bearing surface (F1, F2) contacting said material, said bearing surfaces engaging so as to define the shape of the part to be manufactured, characterised in that: said part has a complex shape, including at least one first slender portion (V), such as a rod, plate, bevel, or shell, and a second portion (B), such as a base, plinth, or solid part, which is not slender in the slender direction of said first portion, and in that said uniaxial pressure is applied in a direction (z) substantially parallel to the smallest dimension of said first portion of the part, or to one of the two smallest dimensions thereof if said part is a rod. The invention also relates to a device for implementing such a method, and to a turbine blade made of a TiAl intermetallic alloy or a metal / silicide composite sintered by flash sintering.
Description
technical field [0001] The present invention relates to a method of using rapid sintering to manufacture components having complex shapes, such as turbine blade preforms near finished dimensions. The invention also relates to a device for carrying out such a method, as well as a turbine blade made of sintered TiAl metal-metal alloy or silicide alloy, which can be obtained with this method. Background technique [0002] Rapid sintering (also known by the acronym "SPS" which stands for "spark plasma sintering") is a sintering technique in which powdered material is subjected to uniaxial pressure inside a mold while applying an electric current to Rapid heating to compact powdery materials. Rapid heating limits the diffusion process and, thus, obtains materials that retain their original microstructure. In the case of metal-metal alloys, the beneficial effect is mainly that the increase in the coarseness of the particle size is limited, thus promoting the refinement of the mi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.