A kind of steel bar lap welding method

A technology of lap welding and steel bar, applied in the field of steel bar lap welding, can solve problems such as affecting welding quality, and achieve the effect of preventing welding porosity defects, reducing man-hours, and improving labor efficiency

Active Publication Date: 2016-02-24
STATE GRID CORP OF CHINA +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because in the actual construction process, there are rust and other dirt on the surface of the steel bar during welding, so defects such as pores and slag inclusions inevitably exist after the steel bar is welded, which affects the welding quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of steel bar lap welding method
  • A kind of steel bar lap welding method
  • A kind of steel bar lap welding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] control Figure 1-4 The operation steps of the present invention are further described:

[0026] A drug core CO 2 The steel bar lap welding method of gas shielded welding wire is characterized in that: the welding equipment uses inverter CO 2 Gas shielded welding machine, using ER501T-1CO 2 Flux cored gas shielded welding wire, the steel bar is HRB335 with Φ20mm-30mm steel bar;

[0027] The welding method is as follows:

[0028] 1) Lap the steel bars and spot weld them;

[0029] 2) Root-layer welding of steel bar lap welds: the arc moves in a straight line 4, welding parameters: welding current is 260A, welding voltage is 23V, welding speed is 35-40cm / min;

[0030] 3) Carry out cover layer welding on the root layer weld: the arc moves in a zigzag shape 5, welding parameters: welding current is 260A, welding voltage is 23V, and welding speed is 25-35cm / min.

[0031] The said overlapping of steel bars means that the ends of two steel bars are folded and overlapped r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for overlap welding of steel bars by adopting flux-cored CO2 gas shielded welding wires. The method is characterized in that an inverter type CO2 gas shielded welding machine is utilized as welding equipment, the ER501T-1 CO2 flux-cored gas shielded welding wires are adopted, and the steel bars are HRB335 ribbed steel bars with phi being 20mm-30mm. The method comprises the following steps that 1) the steel bars are overlapped, and spot welding is conducted on the overlapped steel bars; 2) root-layer welding is conducted on the overlapped weld joints of the steel bars, wherein an electric arc moves linearly, as for welding parameters, a welding current is 260A, a welding voltage is 23V, and welding speed is 35-40cm / min; 3) covering-layer welding is conducted on the root-layer weld joints, the electric arc moves in a zigzag mode, as for welding parameters, a welding current is 260A, a welding voltage is 23V, and welding speed is 25-35cm / min. The method can increase the welding speed, enhance rust resisting capability of the weld joints, prevent pore defects, and achieve the fact that cleaning does not need to be conducted in a welding process.

Description

technical field [0001] The invention relates to a steel bar lap welding method. Background technique [0002] In the prior art, the lap welding of steel bars mainly uses the welding method of electrode arc welding, which has the disadvantages of unstable welding quality and low production efficiency. [0003] Using solid wire CO 2 Semi-automatic gas shielded welding is a low-hydrogen welding method, and the surface of the steel bar is required to be clean and free of dirt before welding. Because in the actual construction process, there are rust and other dirt on the surface of the steel bar during welding, so defects such as pores and slag inclusions inevitably exist after the steel bar is welded, which affects the welding quality. Contents of the invention [0004] The technical problem to be solved by the present invention is to provide a steel bar lap welding method, which has the characteristics of avoiding defects such as welding pores and slag inclusion, eliminati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/16
CPCB23K9/0216B23K9/173
Inventor 王迎军张大刚何生贵焦荣格苏召王秉洪
Owner STATE GRID CORP OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com