High-hardness pressure-resistant terrace material

A floor material and high hardness technology, applied in the field of floor materials, can solve the problems of restricting the use of purification workshops, poor hardness and compressive strength of floor materials, and achieve good hardness and compressive strength, high compressive strength, The effect of high hardness

Active Publication Date: 2013-12-18
江苏悠谷未来科技有限公司
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved: the poor hardness and compressive strength of the floor material limit its use in the purification workshop

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-hardness pressure-resistant terrace material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] Take 28kg of polypropylene, 13kg of furan resin, 11kg of magnesium bicarbonate, 7kg of calcium pyrophosphate, 11kg of acrylonitrile, 5kg of diphenyl ether, and 5kg of methyl ethyl ketone. Stir the ingredients evenly at 80°C, keep warm for 1 hour, seal and cool to room temperature, and the final product is a high-hardness pressure-resistant floor material.

Embodiment 2

[0009] The preparation method is the same as that in Example 1. The content of each component in this example is: 27kg of polypropylene, 11kg of furan resin, 12kg of magnesium bicarbonate, 8kg of calcium pyrophosphate, 13kg of acrylonitrile, 6kg of diphenyl ether, and 3kg of methyl ethyl ketone.

Embodiment 3

[0011] The preparation method is the same as that in Example 1. The content of each component in this example is: 26 kg of polypropylene, 9 kg of furan resin, 11 kg of magnesium bicarbonate, 9 kg of calcium pyrophosphate, 12 kg of acrylonitrile, 5 kg of diphenyl ether, and 4 kg of methyl ethyl ketone.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-hardness pressure-resistant terrace material which is composed of the following components in parts by weight: 26-28 parts of polypropylene, 9-13 parts of furan resin, 11-12 parts of magnesium bicarbonate, 7-9 parts of calcium pyrophosphate, 11-13 parts of acrylonitrile, 5-6 parts of diphenyl ether and 3-5 parts of methylethylketone. The prepared terrace material has the characteristics of high hardness and pressure resistance.

Description

technical field [0001] The invention relates to a floor material, in particular to a high-hardness and pressure-resistant floor material. Background technique [0002] During the use of floor materials in the purification workshop, many problems will be encountered. For example, floor materials are prone to collapse due to their low hardness. The lower hardness can also lead to problems with uneven flooring. If the floor material itself has low hardness and insufficient compressive strength, it will greatly restrict the application field of the floor material. It is a new research direction to improve the hardness and pressure resistance of floor materials by adding some other ingredients. Contents of the invention [0003] The technical problem to be solved: the hardness and compressive strength of the floor material are poor, which limits its use in the purification workshop. [0004] Technical solution: The invention discloses a high-hardness and pressure-resistant ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F291/10C08F291/00C08K13/02C08K3/26C08K3/32C08K5/06
Inventor 葛卫平陈宗美
Owner 江苏悠谷未来科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com