Biodegradable polyester composite catalyst, as well as preparation method and using method thereof

A biodegradable polyester and composite catalyst technology, applied in the field of preparing biodegradable polyester catalysts, can solve the problems of complex preparation process, difficult industrial production, high preparation cost, etc., and achieve simple preparation process, shortened reaction time, and low preparation cost Effect

Inactive Publication Date: 2013-10-02
XINJIANG BLUE RIDGE TUNHE CHEM IND JOINTSTOCK +1
View PDF19 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a biodegradable polyester composite catalyst and its preparation method and use method, which overcomes the above-mentioned deficiencies in the prior art, and can effectively solve the problems of complex preparation process, inconvenient operation, high preparation cost and difficult preparation of existing polyester catalysts. The problem of industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1, the biodegradable polyester composite catalyst contains: 50 to 98 parts of organic titanium compounds, 1 to 30 parts of organosilicon compounds, 0 to 10 parts of cocatalysts, and press Obtained by the method: first stir and mix the required amount of organotitanium compound and the required amount of organosilicon compound, and then continue to mix the required amount of co-catalyst with the required amount of organotitanium compound and the required amount of organosilicon compound Stir and mix evenly to obtain a biodegradable polyester composite catalyst.

Embodiment 2

[0020] Embodiment 2, the biodegradable polyester composite catalyst contains: 50 parts or 98 parts of organotitanium compound, 1 part or 30 parts of organosilicon compound, 0 part or 10 parts of cocatalyst, and Stir and mix the required amount of organotitanium compound and the required amount of organosilicon compound uniformly, and then continue to stir and mix the required amount of co-catalyst with the required amount of organotitanium compound and the required amount of organosilicon compound to obtain the biodegradable polymer Ester composite catalyst.

Embodiment 3

[0021] Embodiment 3, as a preference of the above embodiment, the cocatalyst is a metal salt compound or a multifunctional organic compound. The choice of metal salt compound or multifunctional organic compound can shorten the reaction time.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of catalysts for biodegradable polyester and discloses a biodegradable polyester composite catalyst, as well as a preparation method and a using method thereof. The biodegradable polyester composite catalyst comprises the following raw materials in parts by weight: 50-98 parts of organic titanium compound, 1-30 parts of organic silicon compound and 0-10 parts of cocatalyst, and the biodegradable polyester composite catalyst is obtained through the following method: firstly stirring and uniformly mixing the organic titanium compound in the required quantity with the organic silicon compound in the required quantity, and then continuously stirring and uniformly mixing the cocatalyst in the required quality with the organic titanium compound in the required quantity and the organic silicon compound in the required quantity to get the biodegradable polyester composite catalyst. The biodegradable polyester composite catalyst disclosed by the invention has the characteristics of simple preparation process, simplicity and convenience in operation, lower preparation cost and easiness in industrial production, and by adopting the biodegradable polyester composite catalyst obtained in the invention, the reaction time is shortened, and the polyester with good color phase and high molecular weight can be prepared.

Description

technical field [0001] The invention relates to the technical field of preparing biodegradable polyester catalysts, and relates to a biodegradable polyester composite catalyst, a preparation method and a use method thereof. Background technique [0002] Marked by the invention of polyethylene by Karl Ziegler in Germany and polypropylene by Giulio Natta in Italy in the 1950s and 1960s, the plastics industry has begun to develop vigorously. Various plastic products have greatly facilitated and enriched people's lives. But what follows is the "white pollution" brought by traditional plastic products to the human living environment. With the ever-increasing demand for plastic products, the pressure on the human living environment has also intensified. Therefore, it is an urgent requirement to seek materials that are degradable and can replace traditional plastic products, so as to eliminate human's stigma on plastic products. The contradiction between demand and increasingly se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G63/87C08G63/85C08G63/82C08G63/16
Inventor 丁建萍朱雪锋陈文生孙建新魏志和
Owner XINJIANG BLUE RIDGE TUNHE CHEM IND JOINTSTOCK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products