Preparation method of inorganic-organic double-layer coated type aluminum paste

An aluminum-silver paste and aluminum-coated technology, which is applied in the treatment of dyed organosilicon compounds, dyed polymer organic compounds, coatings, etc. The problem is to achieve excellent acid and alkali corrosion resistance, maintain hiding power, and improve acid and alkali corrosion resistance and adhesion.

Inactive Publication Date: 2013-09-25
CENT SOUTH UNIV
View PDF9 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the defect that the modified aluminum-silver paste in the prior art has poor acid and alkali corrosion resistance, is easily subjected to chemical corrosion, and causes the paint to fall off easily during use, and aims to provide a kind of aluminum alloy with excellent acid and alkali corrosion resistance and attached Focus on the preparation method of inorganic-organic double-coated aluminum-silver paste. The aluminum-silver paste prepared by this method is particularly resistant to acid and alkali corrosion, and has good dispersibility in the organic matrix, and can be widely used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of inorganic-organic double-layer coated type aluminum paste
  • Preparation method of inorganic-organic double-layer coated type aluminum paste
  • Preparation method of inorganic-organic double-layer coated type aluminum paste

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Weigh 20g of aluminum silver paste with a solid content of 50-70% and add it to a mixture of 100mL isopropanol and 50mL water, stir and heat and control the temperature of the whole system at 60-70°C, under the catalytic action of 2.0mL ethylenediamine , drop 10g tetraethyl orthosilicate in 1 hour; after dropping, continue to react for 5 hours, cool, wash, and filter to obtain inorganic silica-coated aluminum-silver paste; Add 10g of inorganic silica-coated aluminum silver paste and 100mL of toluene to a 250mL round bottom flask with a funnel and a reflux condenser, and stir thoroughly for about 30 minutes; add 0.2g of methacryloxypropyltrimethoxysilane, and stir for 30 minutes; then add 10 mL of toluene solution dissolved with 0.2 g of azobisisobutyronitrile, and stir for 30 minutes; vacuumize the system and ventilate nitrogen, repeat three times, and keep a continuous nitrogen atmosphere protection throughout the reaction process; place the flask in Heat to 70°C in a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an inorganic-organic double-layer coated type aluminum paste. The method comprises the following steps of: dispersing the aluminum paste in an alcohol-water mixed solvent to obtain a mixture; dropwise adding tetraethoxysilane into the obtained mixture, stirring the resulting product for hydrolysis reaction, cooling the obtained product after the hydrolysis reaction is finished, washing and filtering hydrolyzed products to obtain an inorganic silicon dioxide coated aluminum paste, dispersing the inorganic silicon dioxide coated aluminum paste in a benzene solvent, sequentially adding an organic coupling agent and an azo initiator while stirring, then dropwise adding an organic polymerized monomer, carrying out polymerization reaction in the presence of an inert gas, after the dropwise addition of the organic polymerized monomer is finished, increasing the temperature for further carrying out polymerization reaction, cooling the obtained product after the polymerization reaction is finished, and washing and filtering polymerized products to obtain the inorganic-organic double-layer coated type aluminum paste. The aluminum paste prepared by adopting the method disclosed by the invention especially has acid and alkali corrosion resistance, in addition, can be well dispersed in an organic matrix, and has wide industrial application prospect.

Description

technical field [0001] The invention relates to a preparation method of an inorganic-organic double-layer coated aluminum-silver paste, which belongs to the field of paint modification. Background technique [0002] Aluminum silver paste is a mixed product with flake metal aluminum powder and organic solvent. Due to its special flake structure, aluminum silver paste has good covering properties, shielding properties, floating properties, and metallic luster properties. Widely used in modern paint and pigment industry. Most of its manufacturing methods use wet ball milling, adding mineral oil, 200# solvent oil and other organic solvents to the ball mill, the ball milling medium is steel balls of 1-5mm, the ball milling time is about 8-30 hours, and then sieved and filtered , and finally the filter cake is kneaded with an appropriate surface treatment agent and an organic solvent to obtain an aluminum silver paste product with a solid content of about 50-70%. The aluminum-si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09C1/64C09C3/12C09C3/10C08F112/08C08F120/14C08F122/14C08F2/44C09D7/12C09D17/00
Inventor 刘辉叶红齐崔欢庆王瑞萌邹鑫
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com