Acid-corrosion-free and high electric insulation red phosphorus flame retarded reinforced nylon and production method thereof

A technology of acid corrosion and nylon, applied in the field of engineering plastics, can solve the problems of reducing the electrical insulation safety performance of nylon materials, affecting the expansion of the application range of materials in the electrical field, and achieving the effect of preventing damage

Inactive Publication Date: 2013-09-18
广东泰昊新材料科技有限公司
View PDF10 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The above disclosed patents play a certain role in slowing down the corrosion of phosphoric acid precipitation, but in the process of nylon processing, under the action of damp heat, high temperature and strong shear, the coating layer of red phosphorus will be destroyed, and phosphoric acid or acid will be generated after red phosphorus is hydrolyzed and oxidized. Substances, thereby reducing the electrical insulation safety performance of nylon materials, affecting the expansion of the application range of materials in the electrical field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acid-corrosion-free and high electric insulation red phosphorus flame retarded reinforced nylon and production method thereof
  • Acid-corrosion-free and high electric insulation red phosphorus flame retarded reinforced nylon and production method thereof
  • Acid-corrosion-free and high electric insulation red phosphorus flame retarded reinforced nylon and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0072] Such as figure 1 As shown, the embodiment of the present invention also provides a preparation method of red phosphorus flame-retardant reinforced nylon without acid corrosion and high electrical insulation, including:

[0073] S100, step (1): pre-dry PA66 and microcapsule red phosphorus master batch, and the drying temperature is 80~120℃;

[0074] Preferably, the pre-drying treatment in step (1) includes:

[0075] Dry PA66 at a drying temperature of 100~120℃ for no less than 4 hours;

[0076] Dry the microcapsule red phosphorus masterbatch at a drying temperature of 80~90℃ for not less than 2 hours.

[0077] It should be noted that since water is not only a necessary reactant for the hydrolysis of red phosphorus, but also an important factor affecting the electrical insulation safety of the material, the water content of the raw materials must be controlled before processing. The auxiliary materials and additives in the formula do not contain crystal water, and generally do no...

Embodiment 1

[0120] Pre-dry PA66 at a drying temperature of 100°C for 6 hours, and pre-dry the microcapsule red phosphorus master batch at a drying temperature of 80°C for 3 hours; 1 part of red phosphorus stabilizer, 4 parts of acid absorbent, and 1 part of nylon are heat stabilized Mixing agent, 0.3 parts of nylon antioxidant, 0.5 parts of silicone lubricant, 1.2 parts of black powder, 51 parts of PA66 and 18 parts of microcapsule red phosphorus masterbatch after pre-drying treatment in parts by weight to obtain a mixture ; Put the mixture and 23 parts of glass fiber into the screw extruder, use the bimodal processing temperature to control the melting temperature to melt and extrude at 240 ~ 290 ℃, and use the vacuum pump to vacuum during the melt extrusion process, and to the screw The extruder barrel is injected with inert gas, and finally, it is cooled to form and pelletized to obtain red phosphorus flame-retardant reinforced nylon.

Embodiment 2

[0122] Pre-dry PA66 at a drying temperature of 115°C for 5 hours, and pre-dry the microcapsule red phosphorus master batch at a drying temperature of 85°C for 2.5 hours; 4 parts of red phosphorus stabilizer, 2 parts of acid absorbent, and 0.7 parts of nylon are heat stabilized Mixing agent, 0.5 parts of nylon antioxidant, 0.8 parts of silicone lubricant, 2 parts of black powder, 53 parts of PA66 and 16 parts of microcapsule red phosphorus masterbatch which have undergone pre-drying treatment in parts by weight to obtain a mixture; The mixture and 21 parts of glass fiber are put into the screw extruder, and the bimodal processing temperature is adopted to control the melting temperature to melt and extrude at 240~290℃, and the vacuum pump is used to vacuum during the melt extrusion process while extruding to the screw The barrel of the machine is injected with inert gas, and finally, it is cooled to form and pelletized to obtain red phosphorus flame-retardant reinforced nylon.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses acid-corrosion-free and high electric insulation red phosphorus flame retarded reinforced nylon. The acid-corrosion-free and high electric insulation red phosphorus flame retarded reinforced nylon comprises, by weight percent, 50 to 60 parts of PA 66, 10 to 18 parts of microencapsulated red phosphorus master batch, 1 to 4 parts of red phosphorus stabilizer, 2 to 5 parts of acid absorbent, 0.5 to 1 part of nylon thermal stabilizer, 0.2 to 0.5 part of nylon antioxygen, 0.5 to 1 part of silicone lubricant, 0.5 to 2 parts of black powers and 20 to 30 parts of glass fibers. The embodiment of the invention also discloses a production method of the acid-corrosion-free and high electric insulation red phosphorus flame retarded reinforced nylon. According to the acid-corrosion-free and high electric insulation red phosphorus flame retarded reinforced nylon and the production method thereof, production formulas and production technologies are improved, general performances such as a good mechanical performance, a thermal performance, a flame retardant performance and a CTI (Comparative Tracking Index) are maintained, the phosphoric acid precipitation and corrosion problem of the PA66 of the red phosphorus flame retarded reinforced nylon is solved, and the electric insulation safety performance of the materials is improved.

Description

Technical field [0001] The invention relates to an engineering plastic, in particular to a red phosphorus flame-retardant reinforced nylon PA66 with no acid corrosion and high electrical insulation performance, and provides a method for preparing the red phosphorus flame-retardant reinforced nylon PA66. Background technique [0002] Nylon PA66 is an engineering plastic with relatively strong water absorption. Red phosphorus is an efficient flame retardant that easily absorbs water. Red phosphorus flame retardant reinforced nylon PA66 has excellent electrical properties (measured by high relative tracking index CTI) and attractive properties. The cost-effectiveness of human beings has become more and more popular among manufacturers in the electrical and electrical industry. Famous electrical manufacturers such as Schneider Electric, Chint Electric, and Sirix Electric are all using this material in large quantities, and the market prospect is very broad. [0003] Nylon PA66 is relat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08K13/06C08K9/10C08K7/14C08K3/22B29C47/92B29C48/92
CPCB29C48/04B29C48/022B29C48/92B29C2948/92704B29C2948/92895
Inventor 赖楚怀
Owner 广东泰昊新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com