A preparation method of functional magnetic adsorbent for industrial wastewater treatment

A magnetic adsorbent, industrial wastewater technology, applied in the fields of adsorption water/sewage treatment, chemical instruments and methods, alkali metal oxides/hydroxides, etc. Uniformity, slow magnetic separation speed, etc., to achieve the effect of controllable structure, controllable magnetic content, and fast magnetic response performance

Inactive Publication Date: 2014-10-15
JINGDEZHEN CERAMIC UNIV
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the magnetic adsorbents prepared at present have weak magnetic response, slow magnetic separation speed, and uneven particle shape and wide particle size distribution, which greatly reduce the magnetic separation performance of magnetic adsorption materials.
Moreover, the preparation process is generally cumbersome, time-consuming, and energy-intensive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of functional magnetic adsorbent for industrial wastewater treatment
  • A preparation method of functional magnetic adsorbent for industrial wastewater treatment
  • A preparation method of functional magnetic adsorbent for industrial wastewater treatment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Example 1: Preparation of Amino Functional Magnetic Adsorbent

[0028] Step 1, ferric oxide nanocrystal clusters with high magnetic saturation

[0029] Take 2.2 g of iron sulfate (Fe 2 (SO 4 ) 3 ), 1.8 g of sodium citrate, and 5.6 g of sodium acetate (NaAc), were dissolved in 80 mL of ethylene glycol, and then transferred to a 250 mL three-neck flask, mechanically stirred at room temperature for 1 h, and then the flask was The liquid was transferred into a high-pressure reactor with a capacity of 100 ml and lined with polytetrafluoroethylene, and then the reactor was placed in an oven at 180 °C for 12 h, and then it was taken out and quickly cooled to room temperature with tap water. Finally, the product was washed by magnetic separation, and unreacted reactants were removed by washing with absolute ethanol and deionized water, respectively, until the supernatant was colorless, and then the product was dispersed in absolute ethanol for subsequent use;

[0030] Ste...

Embodiment 2

[0036] Example 2: Preparation of Carboxyl Functional Magnetic Adsorbent

[0037] The preparation of step 1, iron ferric oxide nanocrystal cluster is described in step 1 in embodiment 1;

[0038] Step 2, modifying the double bond functional group on the surface of ferric oxide nanocrystal clusters is as described in step 2 in Embodiment 1;

[0039] The preparation of the magnetic microspheres modified by step 3, surface epoxy functional group is described in step 3 in embodiment 1;

[0040] Step 4, preparation of carboxyl functional magnetic adsorbent;

[0041] Add 50 mg surface epoxy-modified magnetic microspheres, 15 ml water and 0.4 g mercaptoacetic acid into a three-neck flask, control the pH of the solution to 11, control the temperature to 25 °C, and stop the reaction after mechanical stirring for 12 h. The washing product is separated by a magnetic separation method, and the amino functional magnetic adsorbent is obtained after being washed several times with absolut...

Embodiment 3

[0042] Example 3: Preparation of Amino Functional Magnetic Adsorbent

[0043] Step 1, ferric oxide nanocrystal clusters with high magnetic saturation

[0044] Take 5.2 g of ferric chloride hexahydrate, 3 g of sodium citrate, and 15.6 g of ammonium acetate, dissolve them in 150 mL of ethylene glycol, transfer them to a 250 mL three-necked flask, and stir them mechanically at 160 °C After 6 h, transfer the liquid in the flask to a 200 ml high-pressure reaction kettle with a polytetrafluoroethylene liner, then put the reaction kettle in an oven at 200 ° C for 32 h, take it out, and make it dry with tap water. Cool quickly to room temperature. Finally, the product was washed by magnetic separation, and unreacted reactants were removed by washing with absolute ethanol and deionized water, respectively, until the supernatant was colorless, and then the product was dispersed in absolute ethanol for subsequent use;

[0045] Step 2, modifying the surface of ferric oxide nanocrystal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a functional magnetic adsorbent for industrial wastewater treatment. The method is divided into four steps: (1) using a solvothermal method to prepare ferric oxide nanocrystal clusters with high magnetic saturation; (2) Using the sol-gel method to modify the surface of ferroferric oxide nanocrystal clusters into double bond functional groups; (3) using distillation precipitation polymerization to coat the surface of ferric oxide nanocrystal clusters with a polymer shell containing epoxy functional groups ; (4) The surface of the microspheres is modified into amino groups or carboxyl groups by the ring-opening reaction of epoxy groups. The magnetic adsorbent has high functional group content, fast magnetic response, and easy magnetic separation; regular structure, stable chemical and physical properties, and high dispersion stability in aqueous solution; its surface-modified amino and carboxyl functional groups can efficiently adsorb multiple A heavy metal or organic pollutant, which can be used in the field of industrial wastewater treatment. The method of the invention has simple operation, controllable process and good application prospect.

Description

technical field [0001] The invention belongs to the technical field of wastewater treatment, and in particular relates to a preparation method of a functional magnetic adsorbent used for industrial wastewater treatment. Background technique [0002] Printing and dyeing wastewater has the characteristics of high inorganic salt content, complex composition, good chemical stability, and difficult biodegradation. Direct discharge will bring great harm to the environment and seriously damage the survival of aquatic organisms and human health. Adsorption method has the advantages of simple equipment, simple operation method and large-scale application. Therefore, adsorption method is considered to be one of the most thorough and effective dye wastewater treatment methods, and adsorbent is the key to determine the effect of adsorption treatment. [0003] The magnetic adsorbent with magnetic response can be simply and quickly enriched and separated from the water body under the acti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/26B01J20/28B01J20/30C02F1/28
Inventor 李菊梅江向平熊珊
Owner JINGDEZHEN CERAMIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com