Solid spherical Li[Ni0.8Co0.1Mn0.1]O2 positive electrode material precursor preparation method

A cathode material and precursor technology, applied in the field of lithium-ion battery manufacturing, can solve the problems of reduced cycle performance, high price, environmental pollution, etc., and achieve the effects of simplifying the preparation process, high powder purity, and superior electrical performance

Inactive Publication Date: 2013-08-21
NANJING UNIV
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the positive electrode material used in commercial lithium-ion batteries is mainly lithium cobaltate, which has a layered structure and is easy to synthesize, but its disadvantages are: 1. The actual reversible capacity is low, generally about 140 mAh / g; 2. .Short cycle life, about 300 to 500 times; 3. Poor safety performance; 4. Cobalt raw material is a scarce strategic metal, expensive; 5. Cobalt element is a heavy metal, which pollutes the environment
However, during the charging and discharging process, the crystal structure changes repeatedly between the layered structure and the spinel structure, which causes repeated expansion and contraction of the electrode volume and reduces its cycle performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid spherical Li[Ni0.8Co0.1Mn0.1]O2 positive electrode material precursor preparation method
  • Solid spherical Li[Ni0.8Co0.1Mn0.1]O2 positive electrode material precursor preparation method
  • Solid spherical Li[Ni0.8Co0.1Mn0.1]O2 positive electrode material precursor preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] 1. Raw material weighing

[0026] Weigh 0.8 mol nickel compound, 0.1 mol cobalt compound and 0.1 mol manganese compound respectively.

[0027] Wherein, the nickel compound can be at least any one of nickel sulfate, nickel nitrate, nickel acetate, nickel chloride, nickel bromide or nickel iodide, etc.;

[0028] The cobalt compound can be at least any one of cobalt sulfate, cobalt nitrate, cobalt acetate, cobalt chloride, cobalt bromide or cobalt iodide, etc.;

[0029] The manganese compound may be at least any one of manganese sulfate, manganese nitrate, manganese acetate, manganese chloride, manganese bromide, or manganese iodide.

[0030] 2. Preparation process

[0031] 1. Dissolution: Mix and dissolve weighed nickel sulfate, cobalt sulfate and manganese sulfate in a solvent to prepare a mixed solution with a certain concentration. The concentration range is 0.01 mol / L-2 mol / L; the solvent is at least any one of water, alkanes, alcohols, ethers, ketones, esters, aro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a solid spherical Li[Ni0.8Co0.1Mn0.1]O2 positive electrode material precursor preparation method. According to the method, a nickel compound, a cobalt compound and a manganese compound are matched according to a stoichiometric ratio to prepare a solution having uniform components, the solution is subjected to atomization through an ultrasonic atomizer to form droplets, and the whole atomization thermal decomposition process is rapidly completed, such that component segregation of the droplets does not occur timely so as to ensure component distribution uniformity of the Li[Ni0.8Co0.1Mn0.1]O2 precursor; and regular spherical particles are formed after the droplets are dried, agglomeration is less, and the subsequent washing and grinding is not required, such that high purity of the product is ensured so as to obtain the Li[Ni0.8Co0.1Mn0.1]O2 precursor with good sphericity. The method has the following advantages that: the preparation process is simplified, the stoichiometric ratio of the components can be precisely controlled, the prepared powder has high purity, and the Li[Ni0.8Co0.1Mn0.1]O2 material with an excellent electrical performance is easily prepared after sintering.

Description

technical field [0001] The invention relates to the technical field of manufacturing lithium ion batteries, in particular to the positive electrode material for lithium ion secondary batteries—Li[Ni 0.8 co 0.1 mn 0.1 ]O 2 Preparation method of spherical precursor. Background technique [0002] At present, the positive electrode material used in commercial lithium-ion batteries is mainly lithium cobaltate, which has a layered structure and is easy to synthesize, but its disadvantages are: 1. The actual reversible capacity is low, generally about 140 mAh / g; 2. .The cycle life is short, about 300-500 times; 3. The safety performance is poor; 4. The cobalt raw material is a scarce strategic metal, which is expensive; 5. The cobalt element is a heavy metal, which pollutes the environment. [0003] LiNiO 2 with LiCoO 2 The properties are similar, the actual reversible capacity is higher, and the price is relatively low. However, the preparation is difficult, the structura...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/48
CPCY02E60/10
Inventor 唐月锋唐琨陈庆霖杨华珍刘学文戎葆华沈飞陆彦文吴星云刘盼星彭慕洋谢双飞倪亮陈延峰
Owner NANJING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products