Transparent conducting solution and preparation method thereof, color film substrate and manufacturing method

A technology of transparent conduction and production method, which is applied in the direction of conductive materials, conductive materials, conductive coatings, etc., can solve the problem of high production cost, achieve good hardness and reduce costs

Inactive Publication Date: 2013-07-10
BOE TECH GRP CO LTD
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, sputtering ITO equipment is required when making the ITO layer, and the production cost is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent conducting solution and preparation method thereof, color film substrate and manufacturing method
  • Transparent conducting solution and preparation method thereof, color film substrate and manufacturing method
  • Transparent conducting solution and preparation method thereof, color film substrate and manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the accompanying drawings. Apparently, the described embodiments are only some of the embodiments of the present invention, not all of them.

[0031] The embodiment of the present invention provides a transparent conductive solution. According to the weight ratio, the transparent conductive solution includes: 15-30 parts of epoxy acrylic resin, 15-30 parts of polyurethane acrylic resin, 10-20 parts of polyaniline, photoinitiated 3-5 parts of agent, 15-25 parts of monomer, 8-10 parts of filler.

[0032] In the embodiment of the present invention, the main resin used to make the transparent conductive solution is acrylic ester, including epoxy acrylic resin and polyurethane acrylic resin. The polyaniline is a conductive resin, so that the transparent conductive solution has a conductive function. The photoinitiator can initiate the polyme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The embodiment of the invention provides a transparent conducting solution and a preparation method thereof, a color film substrate and a manufacturing method, and relates to the field of liquid crystal displays. Equipment for sputtering an indium tin oxide (ITO) is not required any more in a production line of manufacturing the color film substrate, so that the cost is reduced. The transparent conducting solution comprises the following components in parts by weight: 15 to 30 parts of epoxy acrylic resin, 15 to 30 parts of polyurethane acrylic resin, 10 to 20 parts of polyaniline, 3 to 5 parts of photo-initiator, 15 to 25 parts of monomer, and 8 to 10 parts of filler.

Description

technical field [0001] The invention relates to the field of liquid crystal display, in particular to a transparent conductive solution and a manufacturing method thereof, a color filter substrate and a manufacturing method thereof. Background technique [0002] FFS (Fringe Field Switching, fringe field switching) technology generates a fringe electric field between the electrodes between pixels in the same plane, so that the aligned liquid crystal molecules between the electrodes and directly above the electrodes can be rotated and switched in the direction parallel to the plane of the substrate, thereby improving the efficiency of the liquid crystal display. The light transmission efficiency of the layer. FFS technology overcomes the problem of low light transmission efficiency of conventional IPS (In-Plane-Switching, plane direction conversion) or TN (Twist Nematic, twisted nematic) technology, and achieves high light transmission efficiency under the premise of wide view...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D175/14C09D179/02C09D5/24G02F1/1335
CPCC08G18/664C08G18/10C08G18/3206C08G18/44C08G18/6674C08G18/755C09D163/10C09D175/14H01B1/128C08L75/14C08L79/02
Inventor 刘陆舒适齐永莲徐传祥
Owner BOE TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com