Metal derusting and antirusting agent and preparation method of metal derusting and antirusting agent

A kind of anti-rust agent and metal technology, which is applied in the coating process of metal materials, etc., can solve the problems of unstable properties of ethylene oxide, endangering the health of operators, and high toxicity of ethylene oxide, and achieves strong binding force and high treatment efficiency. The effect of short time and little pollution

Active Publication Date: 2013-04-17
ANHUI WEILAI SURFACE TECH
View PDF6 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The degreasing and derusting agent is unfavorable for production operation because the ethylene oxide contained in the raw material is unstable, and ethylene oxide is highly toxic, endangering the health of operators and causing great environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Metal derusting antirust agent in the present embodiment, the weight percent of raw material used is:

[0043] Phosphoric acid: 18%;

[0044] Zinc oxide: 0.5%;

[0045] Aluminum hydroxide: 0.5%;

[0046] Sodium tripolyphosphate: 6%;

[0047] Fatty alcohol polyoxyethylene ether with a polymerization degree of 9: 5%;

[0048] Carboxymethylcellulose: 0.5%;

[0049] Acetic acid: 3%;

[0050] Deionized water: 66.5%.

[0051] Preparation method: weigh zinc oxide, aluminum hydroxide and phosphoric acid according to the formula dosage, heat, mix and stir until the solution is clear, and prepare A liquid; weigh the fatty alcohol polyoxyethylene ether with a polymerization degree of 9, carboxymethyl fiber Vegetables and water, heat and mix until completely dissolved to obtain liquid B; mix liquid A and liquid B, and add the prescribed amount of sodium tripolyphosphate and acetic acid under stirring until a uniform aqueous solution can be prepared. Finished rust remover and...

Embodiment 2

[0053] Metal derusting antirust agent in the present embodiment, the weight percent of raw material used is:

[0054] Phosphoric acid: 25%;

[0055] Zinc oxide: 0.8%;

[0056] Aluminum hydroxide: 0.8%;

[0057] Sodium tripolyphosphate: 5%;

[0058] Octylphenol ethoxylate: 4%;

[0059] Carboxymethylcellulose: 0.4%;

[0060] Acetic acid: 1%;

[0061] Deionized water: 63%.

[0062] Preparation method: weigh zinc oxide, aluminum hydroxide and phosphoric acid according to the formula dosage, heat, mix and stir until the solution is clear, and prepare liquid A; weigh the formula dosage of octylphenol polyoxyethylene ether, carboxymethyl cellulose and water, Heat, mix and stir until completely dissolved to obtain liquid B; mix liquid A and liquid B, and add the prescribed amount of sodium tripolyphosphate and acetic acid under stirring until a uniform aqueous solution can be prepared. finished product.

Embodiment 3

[0064] Metal derusting antirust agent in the present embodiment, the weight percent of raw material used is:

[0065] Phosphoric acid: 20%;

[0066] Zinc oxide: 0.6%;

[0067] Aluminum hydroxide: 0.6%;

[0068] Sodium tripolyphosphate: 8%;

[0069] Fatty alcohol polyoxyethylene ether with a degree of polymerization of 15: 3%;

[0070] Carboxymethylcellulose: 0.3%;

[0071] Citric acid: 2.5%;

[0072] Deionized water: 65%.

[0073] Preparation method: Weigh zinc oxide, aluminum hydroxide and phosphoric acid according to the formula dosage, heat, mix and stir until the solution is clear, and prepare liquid A; weigh the fatty alcohol polyoxyethylene ether with a polymerization degree of 15, carboxymethyl fiber Vegetable and water, heated and mixed with stirring until completely dissolved to obtain liquid B; mix liquid A and liquid B, and add the formula dosage of sodium tripolyphosphate and citric acid under stirring until a uniform aqueous solution can be prepared. A fini...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention provides a metal derusting and antirusting agent as well as a preparation method and an application of the metal derusting and antirusting agent. The metal derusting and antirusting agent comprises phosphoric acid, zinc oxide, aluminium hydroxide, sodium tripolyphosphate, organic acid, a surfactant, a thickener and deionized water. The metal derusting and antirusting agent can be used for finishing derusting, passivating and phosphating for a metal surface via one-step treatment, is free from any strong acid and strong base, non-toxic, smokeless and non-smell-volatile, and is free from environment pollution; and the treated metal surface can be antirust for more than half a year and has a strong binding force with a paint layer. The metal derusting and antirusting agent is a derusting and antirusting product which is safe and reliable, less in pollution, simple in process and low in cost.

Description

technical field [0001] The invention relates to a metal surface treatment technology, in particular to a metal derusting and antirusting agent and a preparation method thereof. Background technique [0002] Steel products are easily corroded in the atmosphere, and the amount of steel lost due to corrosion is huge every year in the world. In order to solve the corrosion of steel products, it is often necessary to take various anti-corrosion measures on the steel surface. At present, the metal surface treatment fluids commonly used in industry mainly have the functions of rust removal, rust prevention, decontamination, phosphating, passivation, etc. The products have both single functions and multi-functional ones. However, in practical applications, either due to the high price of raw materials and high cost; or due to incomplete degreasing and rust removal, the corrosion resistance performance, especially the long-term corrosion resistance performance is poor; or the complex...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/20C23G1/02
Inventor 童学宝
Owner ANHUI WEILAI SURFACE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com