Preparation method of titanium dioxide-mesoporous polymer nano porous composite visible light catalytic material

A nanoporous, titanium dioxide technology, applied in the field of material science, can solve the problems of unfavorable product separation, poor thermal stability, etc., and achieve the effects of excellent visible light catalytic degradation ability, good adsorption performance, and excellent visible light catalytic degradation performance.

Inactive Publication Date: 2013-04-17
SHAOXING UNIVERSITY
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Titanium dioxide catalytic materials doped with transition metals generally have relatively poor thermal stability, while titanium dioxide doped with non-metallic elements such as C, N, and S has better stability and visible light catalytic performance. However, the introduction of conventional heteroatoms Generally, very harsh high-temperature treatment conditions (>400°C) are required. At the same time, the particle size of nano-titanium dioxide series catalytic materials obtained after doping is small, generally nano-sized, which is not conducive to separation from the product during the reaction process. The above shortcomings limit the visible light of titanium dioxide. Wide range of applications of catalytic materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of titanium dioxide-mesoporous polymer nano porous composite visible light catalytic material
  • Preparation method of titanium dioxide-mesoporous polymer nano porous composite visible light catalytic material
  • Preparation method of titanium dioxide-mesoporous polymer nano porous composite visible light catalytic material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Firstly, titanium dioxide-mesoporous polymer nanoporous composite visible light catalytic material, PDVB-VI-TiO, was synthesized by using ethyl acetate solvent and imidazole as functional monomers. 2 -xs (where xs represents the molar ratio of titanium species to imidazole in the material).

[0035] 2.0 g DVB, 0.72 g 1-vinylimidazole (VI) were added to a mixed solution containing 0.065 g AIBN and 25 mL ethyl acetate, then 2.5 mL n-butyl titanate (TBOT), stirred at room temperature for 3 hours, 100 ℃ hydrothermal treatment for 24 h, a brownish-yellow blocky solid was obtained. In order to fully crystallize the titanium dioxide in the material, open the lid of the reactor after hydrothermal treatment, add 2-3mL of water, continue the hydrothermal treatment at 160°C for 24 hours, take it out, open the lid, and volatilize the solvent to obtain PDVB-VI-TiO 2 -0.92. The DVB / AIBN / VI / TBOT / ethyl acetate (molar ratio) during the synthesis was 1 / 0.026 / 0.5 / 0.46 / 16.7.

Embodiment 2

[0037] Titanium dioxide-mesoporous polymer nanoporous composite visible light catalytic materials were synthesized with ethyl acetate solvent and imidazole as functional monomers, and the content of titanium species in the materials was adjusted.

[0038]2.0 g DVB, 0.72 g 1-vinylimidazole (VI) were added to a mixed solution containing 0.065 g AIBN and 25 mL ethyl acetate, then 1.25 mL n-butyl titanate (TBOT), stirred at room temperature for 3 hours, 100 After hydrothermal treatment at ℃ for 24 h, a brownish-yellow block solid was obtained. In order to fully crystallize the titanium dioxide in the material, open the lid of the reactor after hydrothermal treatment, add 2-3mL water, continue the hydrothermal treatment at 150℃ for 24 hours, take it out, and open Cover, volatilize the solvent to get PDVB-VI-TiO 2 -0.46. The DVB / AIBN / VI / TBOT / ethyl acetate (molar ratio) during the synthesis was 1 / 0.026 / 0.5 / 0.23 / 16.7.

Embodiment 3

[0040] In the process of synthesizing titanium dioxide-mesoporous polymer nanoporous composite visible light catalytic materials, the synthesis solvent in the synthesis process of materials is modulated.

[0041] Add 2.0 g DVB, 0.72 g 1-vinylimidazole (VI) to a mixed solution containing 0.065 g AIBN and 20-30 mL tetrahydrofuran, then add 2.5 mL n-butyl titanate (TBOT), stir at room temperature for 3 hours, 100 ℃ hydrothermal treatment for 24 h, a brownish-yellow blocky solid was obtained. In order to fully crystallize the titanium dioxide in the material, open the lid of the reaction kettle after hydrothermal treatment, add 2-3mL water, continue the hydrothermal treatment at 150℃ for 24 hours, take it out, and open Cover, volatilize the solvent to get PDVB-VI-TiO 2 -0.92. DVB / AIBN / VI / TBOT / THF was 1 / 0.026 / 0.5 / 0.46 / 16.7 during the synthesis.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Pore volumeaaaaaaaaaa
Adsorption capacityaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a titanium dioxide-mesoporous polymer nano porous composite visible light catalytic material, which comprises the following steps: a. polymerizing azodiisobutyronitrile used as initiator, divinylbenzene used as a crosslinking monomer, 4-vinyl pyridine or 1-vinyl imidazole used as a functional monomer and n-butyl titanate used as a titanium source under solvothermal conditions at 80-140 DEG C for 12-24 hours, thus obtaining a bulk polymer solid; and b. placing the polymer solid product into a reaction kettle, adding a right amount of water, and performing hydrothermal treatment at 150-180 DEG C for 10-24 hours, thus obtaining the titanium dioxide-mesoporous polymer multistage nano porous composite visible light catalytic material. The material preparation method is simple; the obtained photocatalyst has excellent enriching effect and catalytic degradation activity on organic pollutants, especially decabromobisphenol A; and the bulk shape is beneficial to the recycling of the catalyst in the use process.

Description

technical field [0001] The invention belongs to the technical field of material science, and in particular relates to a preparation method of a titanium dioxide-mesoporous polymer nanoporous composite visible light catalytic material with a large specific surface area and excellent enrichment effect on organic pollutants. Background technique [0002] Since Fujishim et al. discovered in 1972 that titanium dioxide can produce hydrogen by photolysis of water (Nature 1972, 238, 37), crystalline titanium dioxide series materials have received more and more attention as an important class of inorganic semiconductor materials. Compared with other materials, titanium dioxide material has low cost, excellent chemical stability and high photoelectric conversion efficiency. So far, titanium dioxide series have been widely used in optoelectronic devices, photoelectric sensors, dye-sensitized solar cells and photocatalysis. [0003] From the perspective of photocatalysis, titanium diox...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J31/38B01J35/10C02F1/30
Inventor 刘福建李建涛刘华
Owner SHAOXING UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com