a foam concrete

A foamed concrete, mass percentage technology, applied in the field of foamed concrete, can solve the problems of less than good impermeability, less than 2.0MPa, heavy taste of chemical reagents, etc. Effect

Active Publication Date: 2014-10-22
王寿光
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing foam concrete materials are mainly cement, and the cement is directly used as the cementing material, and the mass percentage in the concrete can account for 70-85%. Add foaming agent to mix and maintain to form concrete, but the demand for cement in this formula is large, and a large amount of coal resources will be consumed in cement production, and a large amount of carbon dioxide greenhouse gas will be released. Over time, it will cause a shortage of resources and aggravate the greenhouse effect, causing pollution to the environment, and the formed concrete still needs to be strengthened in terms of compression, and the compressive strength of each cubic concrete is generally lower than 2.0MPa
[0004] The current self-compacting foam concrete materials are also made of slag and cement as raw materials, but they all need some alkaline activators and surfactants to improve the chemical activity, improve the cohesion, and improve the sound insulation and sound insulation of the formed concrete. Compressive performance, but this kind of concrete is easy to crack and absorb water. Even if fiber and water repellent are added to the material, the cost will increase but it still cannot achieve good impermeability. A large amount of alkaline excitation is added to the formula Agents and surfactants make the formed concrete chemical reagents smell heavy, pollute the environment, and have a very adverse impact on environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment one: the formula of foamed concrete of the present invention comprises external admixture, cementitious material and chemical auxiliary agent, and every kilogram of foamed concrete comprises the external admixture that mass percentage is 25%, mass percentage is the cementitious material of 45%, and The mass percentage is 15% chemical auxiliary agent, the cement clinker, calcium oxide and bone glue, and the mass ratio of the three components in the cement material is 2:2:1. The external admixture includes industrial waste, and the industrial waste includes one or a mixture of fly ash, wet ash or coal gangue after spontaneous combustion. The external admixture can also include aeolian sand, sand, fly ash, and coal gangue after spontaneous combustion in any proportion. Industrial waste is used as an external admixture to realize waste recycling. Adding aeolian sand and sand is mainly It is to fill the external admixture.

[0019] In addition to the above ingred...

Embodiment 2

[0025] Embodiment two: the formula of foamed concrete of the present invention comprises external admixture, cementitious material and chemical auxiliary agent, and every kilogram of foamed concrete comprises the external admixture that mass percentage is 40%, mass percentage is the cementitious material of 50%, and The mass percentage is 5% chemical auxiliary agent, the cement clinker, calcium oxide and bone glue, and the mass ratio of the three components in the cement material is 2:2:1. The external admixture includes industrial waste, and the industrial waste includes one or a mixture of fly ash, wet ash or coal gangue after spontaneous combustion. The external admixture can also include loam, which can be mixed with fly ash and coal gangue after spontaneous combustion in any proportion. Industrial waste is used as the external admixture to realize waste recycling. The main purpose of adding loam is to fill the external admixture .

[0026] In addition to the above-mentio...

Embodiment 3

[0028] Embodiment 3: A kind of foamed concrete disclosed by the present invention, every kilogram of foamed concrete includes the external admixture that is 25% by mass, the cementitious material that is 70% by mass, and the chemical auxiliary agent that is 5% by mass, so The above-mentioned cementing material includes cement clinker, calcium oxide and bone glue, and the mass ratio of the three components in the cementing material is 2:2:1. The external admixture includes industrial waste, and the industrial waste includes one or a mixture of fly ash, wet ash or coal gangue after spontaneous combustion. The external admixture can also include clay, and the clay and industrial waste can be uniformly mixed in any proportion.

[0029] The chemical auxiliary agent includes sodium sulfate and polyvinyl alcohol, and the mass percentages of the two components in the chemical auxiliary agent are: sodium sulfate 10-80%, polyvinyl alcohol 5-45%. The molecular weight of polyvinyl alcoho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
densityaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a foam concrete, which comprises admixture, cementing material and chemical auxiliary agent, wherein the weight percentage of the admixture in the foam concrete is 25-40%, the weight percentage of the cementing material in the foam concrete is 45-75%, the weight percentage of the chemical auxiliary agent in the foam concrete is 5-25%, the cementing material comprises cement clinker, calcium oxide and bone gelatin powder, and the mass ratio of the three ingredients in the cementing material is 2: 2: 1. The invention further discloses a preparation method of the foam concrete. The preparation method comprises the following steps: foam technology, slurry processing, chemical auxiliary agent processing, mixing, shaping and curing. The foam concrete has the advantages that the cementing material is made of cement clinker, calcium oxide and bone gelatin powder and the use of a great amount of cement is avoided, so that the coal resources required for producing cement is reduced, which not only relieves the tension of energy utilization, but also can improve the compressive strength, leakage resistance, sound insulation effect of the foam concrete.

Description

technical field [0001] The invention belongs to the technical field of engineering materials, and in particular relates to a foam concrete. Background technique [0002] Foamed concrete is to introduce air or nitrogen, carbon dioxide, oxygen and other gases into the concrete slurry according to the application needs through chemical or physical means, and after reasonable maintenance and molding, it forms a concrete with a large number of small closed pores and has considerable strength. Products, the production method is usually to prepare the foam agent aqueous solution into foam by mechanical method, and then add the foam to the slurry composed of siliceous material, calcium material, water and various additives, etc., after mixing and stirring, pouring A porous material formed and cured. [0003] At present, in my country's construction industry, cement, sand, and stones are generally used in the form of concrete compounded with admixtures and water. The building body i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/10C04B28/10
Inventor 王寿光耿正王冕王建州胡国君赵瑞雪张世江王贺
Owner 王寿光
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products