Preparation method of unfired Al-Al2O3 carbon-free composite sliding plate

A technology of carbon composite and sliding plate, which is applied in the field of refractory materials, can solve the problems of long-term storage of products, reduce production costs, and difficulties in industrial production, and achieve good hydration resistance, reduce production costs, and excellent physical performance indicators.

Active Publication Date: 2014-12-10
UNIV OF SCI & TECH BEIJING
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to prepare a non-burning Al-Al that does not require high-temperature firing and oil immersion 2 o 3 Carbon-free composite slide, which not only overcomes the large amount of AlN, Al contained in existing slide materials 4 C 3 The products are seriously hydrated at room temperature, and the products cannot be stored for a long time, which makes the industrial production of the products very difficult; the production process is simplified and the production cost is greatly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Example 1: A non-burning Al-Al 2 O 3 The preparation method of the carbonless composite sliding plate, in terms of weight percentage, the raw material composition is: 82% of corundum, 15% of activated alumina, 3% of metal aluminum powder, and 3.5% of thermosetting phenolic resin.

[0019] During production, various raw materials are first weighed according to the proportions, mixed evenly, and then kneaded to obtain mud, which is then pressed and formed by a friction press, and dried at 120-600 ° C for 9 hours; The product of the present invention is made.

[0020] The powder is metal Al powder with a particle size of less than 325 mesh, activated alumina and part of corundum, and the aggregate is corundum with a particle size of 3-1mm and 1-0.1mm; the above-mentioned corundum is divided into tabular corundum and white corundum.

[0021] The performance index of the obtained product is: apparent porosity 3.8%, bulk density 3.35g / cm 3 , The compressive strength at roo...

Embodiment 2

[0022] Embodiment 2: the production technique is the same as that of embodiment 1, and the difference is:

[0023] By weight percentage, the raw material composition is: 82% corundum, 12% activated alumina, 6% metal aluminum powder, and 3.5% thermosetting phenolic resin. The performance index of the obtained product is: apparent porosity 3.9%, bulk density 3.32g / cm 3 , The room temperature compressive strength is 190MPa, the high temperature flexural strength is 61MPa, and its thermal shock resistance, erosion resistance, oxidation resistance and hydration resistance are all good.

Embodiment 3

[0024] Embodiment 3: the production technique is the same as that of embodiment 1, and the difference is:

[0025] By weight percentage, the raw material composition is: 82% corundum, 9% activated alumina, 9% metal aluminum powder, and 3.5% thermosetting phenolic resin. The performance index of the obtained product is: apparent porosity 4.2%, bulk density 3.28g / cm 3 , The compressive strength at room temperature is 187MPa, and the high temperature flexural strength is 50MPa. Its thermal shock resistance, erosion resistance, oxidation resistance and hydration resistance are all good.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an unfired Al-Al2O3 carbon-free composite sliding plate and a preparation method thereof, belonging to the field of refractory materials. The sliding plate is prepared from 57-87% of corundum, 2-25% of active aluminum oxide and 1-20% of metal Al as well as binder phenolic resin accounting for 2-6% of the total amount of the raw materials. The preparation method comprises the following steps: proportionally weighing various raw materials, evenly mixing, compounding to obtain paste, carrying out pressure molding, and drying at 120-600 DEG C for 5-25 hours. The product has metal-nonmetal combined structure; and the apparent porosity is 3-10%, the volume density is 3.05-3.40 g / cm<3>, the ambient compressive strength is 100-250 MPa, and the high-temperature folding strength is 10-70 MPa. The product does not need high-temperature firing or oil impregnation, and has the advantage of low production cost; the used raw materials have high chemical stability and low oxygen potential, are free of carbon and easily hydrated Al4C3, and do not have secondary pollution of C, O, H and other impurities; and the product has excellent thermal shock resistance.

Description

technical field [0001] The invention relates to the preparation of a sliding plate for steel-making continuous casting, in particular to a non-burning Al-Al for clean steel continuous casting 2 O 3 A carbon-free composite sliding plate and a preparation method thereof belong to the field of refractory materials. Background technique [0002] Clean steel is an important variety of high-quality steel, which has developed rapidly in recent years. Regarding clean steel, it is generally believed that clean steel refers to the steel type that strictly controls the non-metallic inclusions (mainly oxides and sulfides) in the steel. This mainly includes: low total oxygen content in steel, small number of non-metallic inclusions, small size, uniform distribution, less brittle inclusions and suitable inclusion shape, impurity elements in steel generally refer to C, S, P, N , H, O. Therefore, the refractory materials for smelting clean steel must meet the requirements that C, S, P, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66
Inventor 李勇张军杰
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products