Method for visually determining basic metallurgical performance of iron powdered ore

A determination method and technology of iron ore powder, applied in flow characteristics, measuring devices, testing moving fluids/granular solids, etc., to achieve the effect of simple and easy-to-learn method operation, reduce errors, and improve precision and accuracy

Inactive Publication Date: 2013-01-16
UNIV OF SCI & TECH BEIJING
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the determination of the pyrometallurgical properties of iron ore powder still needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for visually determining basic metallurgical performance of iron powdered ore
  • Method for visually determining basic metallurgical performance of iron powdered ore
  • Method for visually determining basic metallurgical performance of iron powdered ore

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Assimilation of iron ore powder:

[0053] The iron ore powder used in the test comes from the blast furnace production site. The iron ore powder and analytical pure CaO reagent are made into fine powder (less than 0.149mm); Make a cylindrical sample with a diameter of 7 mm × 5 mm in the medium, and dry it for use; take a little CaO and press it into a small CaO cake with a diameter of 20 mm × 5 mm under a certain pressure, and the pressing pressure is 20000 N; The sample was placed on the CaO cake and placed in a magnetic boat equipped with a corundum plate. Make four groups of samples according to this method and put them into the magnetic boat respectively; slowly push the magnetic boat into the horizontal heating furnace so that it is located in the constant temperature zone of the horizontal heating furnace, turn on the camera, and adjust the position of the magnetic boat appropriately. Make the image clearly visible; select assimilation; set the heating system of ...

Embodiment 2

[0057] Liquid phase fluidity of iron ore powder:

[0058] The iron ore powder used in the test comes from the blast furnace production site. The iron ore powder and analytical pure CaO reagent are made into fine powder (-0.149mm), and mixed according to a certain alkalinity; the mixed sample is put into a special stainless steel In the mold, under a certain pressure, press it into a cylindrical test sample with a diameter of 8 mm × 5 mm; put it into a magnetic boat equipped with a corundum plate. Make four groups of samples according to this method and put them into the magnetic boat respectively; slowly push the magnetic boat into the horizontal heating furnace so that it is located in the constant temperature zone of the horizontal heating furnace, turn on the camera, and adjust the position of the magnetic boat appropriately. Make the image clearly visible; select the fluidity of the liquid phase; set the heating system of the horizontal heating furnace: room temperature to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for determining the basic metallurgical performance of iron powdered ore. A test process comprises the following steps of: selecting a blocky mixture of the iron powdered ore and auxiliary materials, placing the blocky mixture in a horizontal heating furnace, and starting a computer and a video camera to start acquiring an image; raising temperature according to a set program heating system, wherein a certain amount of mixture of CO, CO2, O2, N2 and H2 can be introduced in a heating process, and the proportion and flow of each gas can be controlled through a program; and calculating metallurgical performance indexes of the iron powdered ore according to change rates of shape and area of the blocky mixture of the iron powdered ore, which are shot by the video camera. Equipment is simple, the method is easy to operate, the computer is used for real-time control, the high-temperature metallurgical performance indexes of the iron powdered ore under a specific temperature control system can be calculated, and errors caused by manual operation when the conventional method is used for measuring the metallurgical performance of the iron powdered ore can be reduced.

Description

Technical field: [0001] The invention belongs to the field of blast furnace ironmaking, in particular to a method for measuring the high-temperature metallurgical properties of visualized iron ore powder. Background technique [0002] The main iron-containing raw material for blast furnace ironmaking in China is sinter. The quality of sinter has an important impact on blast furnace production, and the quality of sinter is largely limited by the iron ore powder raw material used in the sintering process. With the shortage of high-quality iron ore powder resources, some low-quality iron ore powders have entered the Chinese market, which has brought a certain impact on the sintering production of various enterprises. In addition, under the circumstances of the global financial crisis, energy conservation, emission reduction and cost reduction have become urgent problems for all enterprises. Therefore, it is necessary to carry out in-depth research on various iron ore powders f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N21/85G01N11/00
Inventor 左海滨张建良国宏伟焦克新张涛
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap