Foam cement insulation board containing industrial solid waste and preparation method thereof

A technology for solid waste and foamed cement, applied in solid waste management, sustainable waste treatment, ceramic products, etc., can solve problems such as poor thermal insulation performance, poor stability and construction performance, and improve production efficiency and weight. The effect of light and self-weight reduction

Inactive Publication Date: 2013-01-02
ZHENJIANG ZHONGRUI ENERGY SAVING TECH
View PDF2 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And although the existing thermal insulation boards have good fireproof performance, the thermal insulation performance is poor, and the stability performance and construction performance are not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] This embodiment is a foamed cement insulation board containing industrial solid waste, which is composed of a mixture A and a mixture B, and the weight ratio of the mixture A and the mixture B is 1:1.

[0033] The weight percentage components of Mixture A are: cement: 60%, gypsum powder: 15%, hydrogen peroxide: 15%, flocculant: 3%, water reducing agent: 1%, coagulant: 1%, cement waterproofing agent: 2%, lithium carbonate: 1%, fiber: 1%, stable masterbatch: 1%.

[0034] The stable masterbatch is composed of the following components by weight percentage: 25% lithium carbide and 75% calcium stearate.

[0035] The flocculant is aluminum sulfate; the water reducing agent is lignosulfonate sodium salt water reducing agent; the coagulant is water glass or aluminum sulfate.

[0036] The weight percentage components of mixture B are: base material: 38%, magnesium chloride solution: 39%, magnesium oxide: 13%, binder: 2%, industrial hydrogen peroxide: 2%, lanthanide rare earth: 1%, additi...

Embodiment 2

[0053] This embodiment is a foamed cement insulation board containing industrial solid waste, which is composed of a mixture A and a mixture B, and the weight ratio of the mixture A and the mixture B is 2:1.

[0054] The weight percentage components of Mixture A are: cement: 65%, gypsum powder: 10%, hydrogen peroxide: 8%, flocculant: 4%, water reducing agent: 2%, coagulant: 2%, cement waterproofing agent: 3%, lithium carbonate: 2%, fiber: 2%, stable masterbatch: 2%.

[0055] The stable masterbatch is composed of the following components by weight percentage: 75% lithium carbide and 25% calcium stearate.

[0056] The flocculant is a mixture of aluminum sulfate, aluminum chloride and iron sulfate; the water reducing agent is a polycarboxylic acid superplasticizer; the coagulant is water glass or aluminum sulfate.

[0057] The weight percentage components of mixture B are: base material: 45%, magnesium chloride solution: 35%, magnesium oxide: 10%, binder: 2%, industrial hydrogen peroxide...

Embodiment 3

[0074] This embodiment is a foamed cement insulation board containing industrial solid waste, which is composed of a mixture A and a mixture B, and the weight ratio of the mixture A and the mixture B is 3:1.

[0075] The weight percentage components of Mixture A are: cement: 58%, gypsum powder: 20%, hydrogen peroxide: 10%, flocculant: 3%, water reducing agent: 1%, coagulant: 2%, cement waterproofing agent: 2%, lithium carbonate: 1%, fiber: 2%, stable masterbatch: 1%.

[0076] The stable masterbatch is composed of the following components by weight percentage: 45% lithium carbide and 55% calcium stearate.

[0077] The flocculant is iron sulfate; the water reducing agent is aliphatic superplasticizer; the coagulant is water glass or aluminum sulfate.

[0078] The weight percentage components of the mixture B are: base material: 35%, magnesium chloride solution: 36%, magnesium oxide: 12%, binder: 5%, industrial hydrogen peroxide: 3%, lanthanide rare earth: 2%, additives :7%; the weight ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

he invention relates to a foam cement insulation board and a preparation method thereof, and provides a foam cement insulation board containing industrial solid wastes and a preparation method thereof. The foam cement insulation board is composed of a mixture A and a mixture B. The mixture A comprises 55-65% of cement, 10-20% of gypsum powder, 8 -15% of hydrogen peroxide,3-4% of a flocculant, 1-2% of a water reducing agent, 1-2% of a coagulant, 2-3% of a cement waterproof agent, 1-2% of lithium carbonate, 1-2% of fiber, and 1-2% of solid master batch. The mixture B comprises 35-47% of a base material, 35-39% of a magnesium chloride solution, 10-15% of magnesium oxide, 2-5% of a binding agent, 2-3% of industrial hydrogen peroxide, 1-2% of lanthanide rare earth and 5-7% of an additive. The Foam cement insulation board provided by the invention has advantages of fireproof, waterproof, light weight, compressive and flexural resistance and high strength, and effectively utilizes industrial solid waste, facilitates environmental protection, and truly realizes turning wastes into treasures.

Description

technical field [0001] The invention relates to a foamed cement insulation board and a preparation method thereof, in particular to a foamed cement insulation board containing industrial solid waste and a preparation method thereof. Background technique [0002] With the development of industrial production, the amount of industrial waste is increasing day by day. Its passive stacking occupies land, pollutes soil, water and air, affects crop growth, and endangers human health. After industrial waste is generated, it must occupy an area and be piled up. The larger the amount of accumulation, the more land will be occupied. The waste is piled up, and the harmful components in it are easy to pollute the land. When pathogenic microorganisms and other harmful substances in polluted soil enter water bodies with natural precipitation, runoff or seepage, they may further endanger human health. Industrial solid waste also disrupts the ecological balance within the soil. Soil is a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B28/32C04B18/30
CPCY02W30/91
Inventor 郭振勤
Owner ZHENJIANG ZHONGRUI ENERGY SAVING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com