Modified unsaturated polyester colored finish paint or primer

An unsaturated and polyester technology, applied in polyester coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of insufficient technical indicators, poor surface scratch resistance, and low fullness, and achieve excellent technical indicators , strong adhesion, and excellent polishing of the topcoat

Inactive Publication Date: 2012-12-12
FOSHAN OVS SANITARY WARE MFG
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Unsaturated polyester paint for wood products usually has four components, namely main paint, initiator (commonly known as white water), accelerator (commonly known as blue water) and reactive diluent. Finally, the surface needs to be sealed with wax (or film) (if it is air-dry, it can not be sealed), and after curing, it can be finished by machine grinding, polishing and other processes, so the process is more complicated and the price is higher, but its paint film It is hard and plump, so it is mostly used for the top coat of high-end furniture and audio casings with high decorative requirements; while the common polyurethane paint in the market is a two-component one, one is the main paint, the other is the curing agent, and it is used according to the requirements. The ratio is mixed, and an appropriate amount of thinner is added, and the construction can be carried out after stirring evenly. The process is simple, but some technical indicators are not excellent enough. Construction in high humidity environment is prone to foaming, and the requirements for substrate treatment are relatively high, such as the dryness of wood, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A modified unsaturated polyester colored topcoat, including polyurethane (PU) component and unsaturated polyester (PE) component, the two components are mixed according to the weight ratio of 1:1, and applied after mixing;

[0017] The polyurethane (PU) component is composed of the following components (calculated by weight ratio): PU main paint: curing agent: PU thinner = 1:1:1;

[0018] The PU main paint is composed of the following components (calculated in parts by weight): 80% alkyd resin, 9.2% xylene, 0.5% leveling agent, 0.3% defoamer; 5 toner;

[0019] The curing agent is a toluene diisocyanate (TDI)-trimethylolpropane composite and trimer mixture with an aqueous solution concentration of 40%;

[0020] The PU diluent is composed of the following components (calculated in parts by weight): 50 parts of toluene, 40 parts of butyl acetate, and 10 parts of methyl isobutyl ketone;

[0021] The composition of the unsaturated polyester (PE) component is (calculated by ...

Embodiment 2

[0027] A modified unsaturated polyester colored topcoat, including a polyurethane (PU) component and an unsaturated polyester (PE) component, the two components are mixed at a weight ratio of 1:0.5, and applied after mixing;

[0028] The polyurethane (PU) component is composed of the following components (calculated by weight ratio): PU main paint: curing agent: PU thinner = 1:0.1:0.1;

[0029] The PU main paint is composed of the following components (calculated in parts by weight): 30 alkyd resins, 1 xylene, 0.1 leveling agents, 0.1 defoamers; 10 fillers;

[0030] The curing agent is an adduct of toluene diisocyanate (TDI)-trimethylolpropane with an aqueous solution concentration of 10%;

[0031] The PU diluent is composed of the following components (calculated in parts by weight): 10 toluene, 5 butyl acetate, and 1 methyl isobutyl ketone;

[0032] The composition of the unsaturated polyester (PE) component is (calculated by weight ratio): PE main paint: accelerator: initi...

Embodiment 3

[0038] A modified unsaturated polyester colored topcoat, including polyurethane (PU) component and unsaturated polyester (PE) component, the two components are mixed according to the weight ratio of 1:1, and applied after mixing;

[0039] The polyurethane (PU) component is composed of the following components (calculated by weight ratio): PU main paint: curing agent: PU thinner = 1:1:0.6;

[0040] The PU main paint is composed of the following components (calculated in parts by weight): Alkyd resin containing 70, xylene 10, leveling agent 1, defoamer 0.1; filler 19.9;

[0041] The curing agent is an adduct of toluene diisocyanate (TDI)-trimethylolpropane with an aqueous solution concentration of 44%;

[0042] The PU diluent is composed of the following components (calculated in parts by weight): 55% toluene, 35% butyl acetate, and 10% methyl isobutyl ketone;

[0043] The composition of the unsaturated polyester (PE) component is (calculated by weight ratio): PE main paint: ac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
adhesivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a modified unsaturated polyester colored finish paint or primer, which is characterized in that: the paint is prepared by mixing a polyurethane component with an unsaturated polyester component according to a weight prescribed ratio of polyurethane component to unsaturated polyester component of 1: (0.5-1). Compared with the prior art, the modified unsaturated polyester colored finish paint or primer has excellent technical indexes and can replace foreign similar products, and has the advantages of high hardness, good fullness, strong adhesion, good flexibility, easiness in construction and the like.

Description

technical field [0001] The invention relates to the technical field of paint for wood products, more specifically relates to a novel colored topcoat or primer for wood products with good decorative effect. Background technique [0002] Unsaturated polyester paint for wood products usually has four components, namely main paint, initiator (commonly known as white water), accelerator (commonly known as blue water) and reactive diluent. Finally, the surface needs to be sealed with wax (or film) (if it is air-dry, it can not be sealed), and after curing, it can be finished by machine grinding, polishing and other processes, so the process is more complicated and the price is higher, but its paint film It is hard and plump, so it is mostly used for the top coat of high-end furniture and audio casings with high decorative requirements; while the common polyurethane paint in the market is a two-component one, one is the main paint, the other is the curing agent, and it is used acco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/06C09D175/14C09D167/06C09D7/12
Inventor 魏启超
Owner FOSHAN OVS SANITARY WARE MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com