Shower room base mould capable of being tiled with ceramic tiles and manufacturing method thereof

A technology for shower room and tiling, which is applied to small buildings and other directions, can solve the problems of tearing and difficult to demould, and achieve the effect of reducing weight, convenient for handling and installation, and convenient for tiling.

Inactive Publication Date: 2012-10-10
崔岱岩
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] Another object of the present invention is to provide the preparation method of the shower room base tire that can be tiled. The preparation method can make the shower room base tire at one time, which overcomes the tearing of the product due to the shrinkage of the artificial stone composite material during the curing process. And the problem that it is difficult to demould, the operation is simple, and the success rate of the product can reach 100%.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Shower room base mould capable of being tiled with ceramic tiles and manufacturing method thereof
  • Shower room base mould capable of being tiled with ceramic tiles and manufacturing method thereof
  • Shower room base mould capable of being tiled with ceramic tiles and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] figure 1 Shown is a schematic diagram of the structure of the base tire of the existing cement and foam plastic materials in the shower room. It can be seen from the figure that this type of base tire has no thin water retaining edge, and the base body of the base tire is directly bonded to the wall during installation. Leaks easily.

[0058] figure 2 Shown is a schematic diagram of the structure of the base tire of the existing shower room made of glass fiber reinforced plastic and stainless steel. It can be seen from the figure that the base of the base tire is a horizontal plane, and there is no slope between the base and the drain, so it is not easy to drain water, and the water retaining sides are relatively large. Thin, not easy to undertake the body of the shower room.

[0059] According to the deficiencies of the prior art, the invention provides a new shower room base tire, which is convenient for waterproofing and tiling. Its preferred structure is as im...

Embodiment 2

[0067] To make a 900mm×900mm square shower room base tire with a total weight of 22.42kg, the steps are as follows:

[0068] Step 1: Add 10kg of unsaturated polyester resin, 10kg of calcium carbonate powder, and 220g of accelerator into the container, and stir for 5 minutes with electric machinery to make it evenly mixed.

[0069] Step 2: Add 2kg of perlite powder and stir for 3 to 5 minutes to make it even.

[0070] Step 3: Add 200g of curing agent and stir for 2 to 5 minutes to make it even.

[0071] The fourth step: inject the mixture of the third step into the mold of the base tire of the shower room that has been evenly coated with release wax.

[0072] Step 5: After setting for 20-60 minutes, the material enters the primary stage of curing and starts to generate heat. At this time, the material has been cured and formed but has not yet started to shrink. At this time, it should be demoulded quickly before shrinkage occurs.

[0073] Step 6: Place the demoulded product o...

Embodiment 3

[0076] To make a 900mm×900mm jewel-shaped base tire with a total weight of 26.42kg, the steps are as follows:

[0077] Step 1: Add 10kg of unsaturated polyester resin, 15kg of calcium carbonate powder, and 220g of accelerator into the container, and stir for 5 minutes with electric machinery to make it evenly mixed.

[0078] Step 2: Add 1kg of perlite powder and stir for 3 to 5 minutes to make it even.

[0079] Step 3: Add 200g of curing agent and stir for 2 to 5 minutes to make it even.

[0080] The fourth step: inject the mixture of the third step into the mold of the base tire of the shower room that has been evenly coated with release wax.

[0081] Step 5: After setting for 20-60 minutes, the material enters the primary stage of curing and starts to generate heat. At this time, the material has been cured and shaped but has not yet started to shrink. At this time, it should be demoulded quickly before shrinkage occurs.

[0082] Step 6: Place the demoulded product on a ho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a shower room base mould capable of being tiled with ceramic tiles. The base mould comprises a base body and water retaining edges, wherein water retaining edges are located on the periphery of the base body, a drainage opening is arranged on the base body, water retaining edges are perpendicular to or almost perpendicular to the base body, and the base body and water retaining edges are made of resin matrix artificial stone composites. The base mould is made of artificial stones and is simple in structure and good in water resistance, tiling is convenient, and risks of water leakage are greatly reduced. The invention also discloses a manufacturing method of the shower room base mould. According to the method, the shower room base mould can be manufactured once, the problems that products are torn and difficult to demold due to material shrinkage in the curing process of artificial stone composites are solved, the operation is easy, and the success rate of products can reach 100%.

Description

technical field [0001] The invention relates to a tileable shower room base tire and a preparation method thereof, belonging to the technical field of building materials. Background technique [0002] The shower room is generally composed of a shower room body and a base. The shower room itself can be surrounded by an independent small space to control the bathing range in a small space, prevent bath water from overflowing, and keep other places dry. The shower room is generally attached to the wall during installation, and the shower room body and base are combined with the wall to form an independent space. [0003] At present, many European and American countries, including Australia, New Zealand and other countries, mostly adopt wooden structure houses. The wall is generally made of wood as a load-bearing frame, and interior wall panels are installed on the inner surface of the wall. The material of the interior wall panels is generally 10mm thick gypsum board, and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04H1/12C04B26/02
Inventor 崔岱岩
Owner 崔岱岩
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com