Laser near net shaping method of low-porosity titanium alumina ceramic piece

A technology of near-net laser shaping and alumina, which is applied in the direction of ceramic products, other household utensils, household utensils, etc., can solve the problems of losing the use value of structural parts, achieve the suppression of thermal growth and cooling shrinkage, solve the problem of pores, expand Effect of Feasible Parameter Range

Active Publication Date: 2012-08-08
DALIAN UNIV OF TECH
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, trying to improve the pores through technological means will often lead to other problems, and even lose the original use value of the structural parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Laser near net shaping method of low-porosity titanium alumina ceramic piece
  • Laser near net shaping method of low-porosity titanium alumina ceramic piece
  • Laser near net shaping method of low-porosity titanium alumina ceramic piece

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] Below in conjunction with accompanying drawing and embodiment the present invention will be further described: as figure 1 As shown, the laser near-net forming method of low porosity alumina-titanium ceramics requires that the embodiment of the present invention: the length of alumina-titanium ceramics is 17mm, the width is 2mm, and the height is 6mm, using JK1002 type Nd:YAG solid The continuous laser performs laser near-net forming on alumina titanium powder, and the specific forming steps are as follows:

[0037] A. Select 42-90 μm near-spherical aluminum oxide titanium according to the requirements, add 10wt.% SiC, mix the powder with a good ratio in a planetary ball mill for 24 hours, and then dry it in an electric blast drying oven at 100°C for 4 hours;

[0038] B. Before processing, sand the forming substrate 6 with sandpaper and clean it with alcohol;

[0039] C. Put the pretreated composite powder into the powder feeder 7, and adjust the working distance betwe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a laser near net shaping method of a low-porosity titanium alumina ceramic piece. Laser net shaping is performed on titanium alumina ceramic powder by using a laser processing system. The laser near net shaping method specifically comprises the following steps of: mixing the titanium alumina ceramic powder and SiC powder, drying and then placing in a powder feeder; connecting a laser processing head with a Nd:YAG solid laser through a transmission optical fiber; and realizing the laser net shaping of the low-porosity titanium alumina ceramic piece by controlling continuous movement of the processing head by taking argon gas as powder feeding and protecting gas. According to the laser near net shaping method, on one hand, the laser net shaping of the low-porosity titanium alumina ceramic piece can be realized, and on the other hand, the complexity of parameter optimization is simplified; the introduction of other adverse problems is avoided; and thus, a feasibleparameter range is expanded and the production efficiency is increased.

Description

technical field [0001] The invention relates to a forming technology of an alumina-titanium ceramic part, in particular to a laser near-net forming method for a low-porosity alumina-titanium ceramic part. Background technique [0002] With the rapid development of the world's industrial level and advanced manufacturing technology, the service life requirements of structural parts in special environments continue to increase, and the performance of metal materials in high-temperature corrosion, insulation and high-wear environments has been difficult to meet the requirements, such as aerospace engines. High wear and high temperature resistant impellers, manipulators for extreme industrial and mining conditions, special parts for national defense and high-tech fields, etc. Due to its wide range of sources, and its unique properties of wear resistance, corrosion resistance, high hardness and high temperature resistance, ceramic materials have attracted much attention in the mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/06
Inventor 吴东江杨策马广义吴楠康仁科
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com