Hydrodenitrogenation catalyst capable of removing nitrogen-containing compound from coal tar, and preparation method and application thereof

A nitrogen compound, hydrogenation and denitrogenation technology, applied in the direction of physical/chemical process catalysts, molecular sieve catalysts, chemical instruments and methods, etc., can solve the problems of lack of cleanliness, large-scale utilization technology, pollution, waste of resources, etc., to achieve good results Hydrodesulfurization performance, good water resistance, good denitrification effect

Active Publication Date: 2012-08-01
山西中科化美科技有限责任公司
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, medium and low temperature coal tar is mostly used after direct combustion or simple treatment, and there is still a lack of clean and large-scale utilization technology, which greatly wastes resources and produces a lot of pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrodenitrogenation catalyst capable of removing nitrogen-containing compound from coal tar, and preparation method and application thereof
  • Hydrodenitrogenation catalyst capable of removing nitrogen-containing compound from coal tar, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A hydrodenitrogenation catalyst capable of removing nitrogen-containing compounds from coal tar is composed of an active component, an additive and a carrier, and the active component is composed of tungsten trioxide, nickel monoxide and chromium trioxide, and the content of the tungsten trioxide is 15wt% of the catalyzer, the nickel monoxide content is 5wt% of the catalyzer, and the dichromium trioxide content is 3.5wt% of the catalyzer; the auxiliary agent is fluorine and phosphorus, and in elemental calculation, the fluorine content is 3.2wt% of the catalyzer, so Described phosphorus content is 1.6wt% of catalyzer; Carrier is made up of aluminum oxide, zirconium oxide, Hβ molecular sieve, binding agent and extrusion aid, calculates on a dry basis, and described carrier content is 73wt% of catalyzer, and described alumina, The weight ratio of zirconia and Hβ molecular sieve is 15.8:1.6:2.2, the weight of the binder is 5% of the weight of the alumina, and the content of...

Embodiment 2

[0031] A hydrodenitrogenation catalyst capable of removing nitrogen-containing compounds from coal tar is composed of an active component, an additive and a carrier, and the active component is composed of tungsten trioxide, nickel monoxide and chromium trioxide, and the content of the tungsten trioxide is 17wt% of the catalyzer, the nickel monoxide content is 5wt% of the catalyzer, and the dichromium trioxide content is 2.5wt% of the catalyzer; the auxiliary agent is fluorine and phosphorus, and in elemental calculation, the fluorine content is 2.5wt% of the catalyzer, so Described phosphorus content is 1.5wt% of catalyzer; Carrier is made up of alumina, zirconium oxide, Hβ molecular sieve, binding agent and extrusion aid, calculates on dry basis, and described carrier content is 69wt% of catalyzer, and described alumina, The weight ratio of zirconia and Hβ molecular sieve is 16:1.5:2.5, the weight of the binder is 7% of the weight of the alumina, and the content of the extrus...

Embodiment 3

[0040] Weigh 1000 g of alumina precursor pseudoboehmite, 103 g of zirconia, 162 g of Hβ molecular sieve and NH 4 F 25 g and mix evenly, then add 100 g of pseudo-boehmite binder, 16 g of squash gum, 48 g of acetic acid, and 774 g of distilled water into the above mixture, knead in a kneader for 150 min, put Extrusion molding in strip machine. Then dry at 40 °C for 4 h, and then dry at 100 °C for 10 h, then raise the temperature to 650 °C at a heating rate of 1 °C / min, and roast for 8 h to obtain 1027 g of the finished carrier. Calculated on a dry basis, alumina accounts for 75% of the total weight of the carrier , zirconia accounts for 10% of the total weight of the carrier, and Hβ molecular sieve accounts for 15% of the total weight of the carrier.

[0041] Add 307 g of ammonium metatungstate, the precursor of tungsten trioxide, 343 g of nickel nitrate, the precursor of nickel monoxide, and 309 g of chromium nitrate, the precursor of chromium trioxide, into 575 g of distilled...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of catalysts for hydrodenitrogenation of coal tar. The technical problem to be solved is to provide a hydrodenitrogenation catalyst capable of deeply removing a nitrogen-containing compound from coal tar and provided with high mechanical strength, wear resistance and water resistance, and a preparation method and application thereof. The invention adopts the technical scheme that in the hydrodenitrogenation catalyst capable of removing nitrogen-containing compound from coal tar, active components consist of tungsten trioxide, nickel monoxide and chromium sesquioxide; aids comprise fluorine and phosphorus; and a carrier consists of aluminum oxide, zirconium oxide, a Hbeta molecular sieve, a binder and an extrusion aid. By adopting the hydrodenitrogenation catalyst capable of deeply removing the nitrogen-containing compound from the coal tar, the oil nitrogen content of the hydrogenation product can be reduced to be below 50 micrograms / gram; and the hydrodenitrogenation property is high, so that the oil sulfur content of the hydrogenation product can be reduced to be below 40 micrograms / gram.

Description

technical field [0001] The invention belongs to the technical field of catalysts for hydrodenitrogenation of coal tar. Background technique [0002] Coal tar is a liquid product produced during the pyrolysis process of coal. According to the pyrolysis temperature, it can be divided into high-temperature tar (900-1000°C), medium-temperature tar (700-900°C), and low-temperature tar (500-700°C). At present, the annual output of high-temperature coal tar in my country is about 10 million tons, mainly produced in high-temperature coking industry, and the annual output of medium-low temperature coal tar is also several million tons, mainly produced in coal pyrolysis semi-coke industry and coal gasification industry. In the foreseeable future, the development of large-scale clean and efficient cascade utilization technology of low-rank coal, which is guided by pyrolysis to produce medium and low temperature coal tar, will produce a larger amount of medium and low temperature coal ta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J29/78C10G45/12
Inventor 邱泽刚崔海涛武行洁
Owner 山西中科化美科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com