Method for preparing polyester staple fibers by using waste polyester raw material

A polyester staple fiber and polyester technology, which is applied in the field of polyester staple fiber preparation by using waste polyester raw materials, can solve the problems of low processing efficiency, molecular weight reduction, high-new material ratio, etc., so as to improve processing efficiency, avoid gel phenomenon, and ensure The effect of linearity

Inactive Publication Date: 2012-07-18
ZHEJIANG SCI-TECH UNIV
View PDF8 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to avoid the reduction of molecular weight during the processing and use of polyester, solid-state polycondensation or mixed use of recycled materials and virgin materials is mostly used. The former requires a longer processing time and lower processing efficiency, while the latter requires a higher proportion of virgin materials. , the utilization rate of recycled materials is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing polyester staple fibers by using waste polyester raw material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The waste polyester raw material used is waste pure polyester textile (intrinsic viscosity 0.5g / dl). Adopt the following technological conditions to carry out the preparation of regenerated polyester fiber:

[0019] (1) Raw material preparation: Wash waste polyester textiles to remove stains. The washing conditions are: synthetic detergent 5g / l, sodium tripolyphosphate 5g / l, caustic soda 0.8g / l, and temperature 90°C. The cleaned waste polyester textiles were dried in a hot air dryer for 5 hours, and after the water content dropped to 0.1%, the waste polyester raw materials were compressed with an agglomerator at 235°C in a semi-molten state to prepare spherical pellets.

[0020] (2) Melt preparation and spinning: transfer the pellets prepared in step (1) to a drying device and dry at 120°C for 30 minutes, then dry at 140°C for 6 hours, the moisture content after drying is 30ppm, and then press the pellets 0.5% of the mass is added with a molar ratio of 1,4-phenylbisoxa...

Embodiment 2

[0023] The waste polyester raw material used is the waste silk (intrinsic viscosity 0.6g / dl) produced during the polyester spinning process. Adopt the following technological conditions to carry out the preparation of regenerated polyester fiber:

[0024] (1) Raw material preparation: Wash waste polyester textiles to remove stains. The washing conditions are: synthetic detergent 5g / l, sodium tripolyphosphate 5g / l, caustic soda 0.8g / l, and temperature 90°C. The cleaned waste polyester textiles were dried in a hot air dryer for 5 hours, and after the water content dropped to 0.1%, the waste polyester raw materials were compressed with an agglomerator at 235°C in a semi-molten state to prepare spherical pellets.

[0025] (2) Melt preparation and spinning: transfer the pellets prepared in step (1) to a drying device and dry at 140°C for 10 minutes, then dry at 170°C for 3 hours, the moisture content after drying is 40ppm, and then 3% of 1,4-phenylbisoxazoline (1,4-PBO) polyester ...

Embodiment 3

[0027] The waste polyester raw material used is waste pure polyester textile (intrinsic viscosity 0.52g / dl). Adopt the following technological conditions to carry out the preparation of regenerated polyester fiber:

[0028] (1) Raw material preparation: Wash waste polyester textiles to remove stains. The washing conditions are: synthetic detergent 5g / l, sodium tripolyphosphate 5g / l, caustic soda 0.8g / l, and temperature 90°C. The cleaned waste polyester textiles were dried in a hot air dryer for 5 hours, and after the water content dropped to 0.1%, the waste polyester raw materials were compressed with an agglomerator at 235°C in a semi-molten state to prepare spherical pellets.

[0029] (2) Melt preparation and spinning: transfer the pellets prepared in step (1) to a drying device and dry at 130°C for 20 minutes, then dry at 160°C for 4 hours, the moisture content after drying is 45ppm, and then press the pellets 2.5% of the mass is added to carbonyl bis (1,-caprolactam) (CBC...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Moisture contentaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing polyester staple fibers by using a waste polyester raw material. The method comprises the following steps of: cleaning and drying waste polyester, and performing compression aggregation and granulation; drying, conveying into a reaction type vented screw extruder, and adding phenyl bis-oxazoline and N, N'-carbonyl bis-caprolactam polyester chain extenders which are 0.5 to 3 mass percent of granules; conveying the polyester granules and the chain extenders to the reaction type vented screw extruder together, melting and mixing; and weighing a melt and conveying to a spinning unit to prepare the polyester staple fibers. The degradation of the waste polyester in the processing and using processes can be improved, the molecular weight of the waste polyester is improved, and the processing efficiency and fiber quality of the polyester fibers are improved. The prepared polyester fibers can be used for filling materials of clothing and furniture fabrics, geotextiles, roofing felt base cloth, nonwoven fabrics of insulating materials, shoe covers, wiping cloth and several disposable nonwoven products.

Description

technical field [0001] The invention relates to a method for preparing polyester staple fiber, in particular to a method for preparing polyester staple fiber by using waste polyester raw materials. Background technique [0002] Thermoplastic polyesters include major varieties such as fiber grade, bottle grade and film grade polyester by application. In 2010, the demand for fiber-grade and bottle-grade polyester in my country exceeded 23 million tons, and maintained a certain growth rate, especially for bottle flake polyester used in food packaging, medicine, and daily chemical packaging. rate exceeded 15%. The rapid development of the polyester industry has also brought an unavoidable problem to the world: raw material sources and waste disposal. There are about 2% waste in polyester fiber processing, waste after use of fiber products, and one-time use of food packaging polyester produce a large amount of waste polyester raw materials. [0003] Since the 1980s, countries a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F6/84
Inventor 朱海霖张华鹏陈建勇唐红艳郭玉海
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap