Interior wall coating coil and preparation method thereof

A technology for interior wall coatings and coils, which is applied to the preparation of interior wall coatings coils, in the field of coils with coating functions, can solve the problems of poor air permeability and flammability of stone paper, and achieve good air permeability, low cost, and high quality stable effect

Inactive Publication Date: 2014-04-16
上海利民环保节能科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This utility model patent uses stone paper as the base material to replace the traditional paper-based or plastic-based wallpaper, which has good waterproof performance and strength, but the stone paper has poor air permeability and has the risk of being flammable, so it cannot completely replace the interior wall. paint layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Interior wall coating coil and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] 1) Mix 30kg of calcined kaolin, 35kg of light calcium carbonate, 15kg of rutile titanium dioxide, and 1kg of EVA wax in a blender, and add them to a 30-type three-chamber continuous vortex airflow refiner to make the inorganic powder and white pigment The interface is fully contacted and evenly dispersed;

[0041] 2) Introduce the above-mentioned modified material into the L100 high-speed mixer, add 0.5kg maleic anhydride, and react for 15 minutes under the temperature condition of 140°C and 900r / min stirring condition;

[0042]3) Add ethylene bisoleic acid amide 1kg, antioxidant B-(4-hydroxy-3.5 di-tert-butylphenyl) stearyl propionate 0.2kg, light stabilizer 2-( 2'-hydroxyl-5'-tert-octylphenyl)benzotriazole 0.2kg, flame retardant antimony trioxide 0.8kg, reacted for 10min under the temperature condition of 140°C and stirring condition of 900r / min;

[0043] 4) Add 8kg PET into the above-mentioned high-speed mixing equipment and stir and mix evenly;

[0044] 5) The abo...

Embodiment 2

[0047] 1) Mix 25kg of heavy calcium carbonate, 40kg of talcum powder, 5kg of lithopone, 5kg of sharp titanium dioxide, and 1.5kg of Sasol wax in a mixer, and add it to a 60-type three-chamber continuous vortex airflow refiner , so that the interface between the inorganic powder and the white pigment is fully contacted and dispersed uniformly;

[0048] 2) Introduce the above-mentioned modified material into the L100 high-speed mixer, add 0.1kg maleic anhydride and 0.5kg polybutylacrylic acid, and react for 30min at a temperature of 80°C and stirring at 900r / min;

[0049] 3) Add stearic acid amide 0.5kg, ethylene bisstearic acid amide 1.0kg, antioxidant tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propane to the above-mentioned high-speed mixer Acid] pentaerythritol ester 0.3kg, light stabilizer bis(2,2,6,6,-tetramethyl-4-piperidinyl) sebacate 0.3kg, flame retardant magnesium hydroxide 1.2kg, at 120°C Reaction for 8 minutes under temperature conditions and 1000r / min stirring c...

Embodiment 3

[0054] 1) Mix 30kg of sericite, 30kg of wollastonite, 5kg of lithopone, 5kg of rutile titanium dioxide, and 1.5kg of oxidized polyethylene wax in a blender, and add it into a 45-type three-chamber continuous vortex airflow refiner, Make the interface of inorganic powder and white pigment fully contact and disperse evenly;

[0055] 2) Introduce the above-mentioned modified material into the L100 high-speed mixer, add 0.2kg methyl methacrylate and 0.5kg polybutylacrylic acid, and react for 20min under the temperature condition of 100°C and stirring condition of 1500r / min;

[0056] 3) Add 1.5 kg of glyceryl monostearate, 0.4 kg of antioxidant tris(2,4-di-tert-butylphenyl) phosphite, and light stabilizer 2-hydroxyl-4-methanol in the above-mentioned high-speed mixer. 0.4kg of oxybenzophenone and 1.6kg of flame retardant aluminum hydroxide were reacted at 120°C and 1500r / min stirring for 5min;

[0057] 4) Add 12kgLDPE into the above-mentioned high-speed mixing equipment and stir an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an interior wall coating coil and a preparation method thereof. The interior wall coating coil comprises the following components in part by weight: 60 to 70 parts of inorganic powder, 10 to 20 parts of white pigment, 1 to 2 parts of dispersant, 1 to 2 parts of lubrication aid, 1 to 3 parts of stabilizer, 0.5 to 1 part of grafting agent and 8 to 12 parts of macromolecular polymer. The interior wall coating coil which has high air permeability, water resistance and flame retardance is prepared by utilizing mechano-chemical modification and stretch thermoforming of polymeric materials, and uniformly dispersing a large amount of inorganic powder and white pigment into a small amount of polymeric material. The interior wall coating coil has white and bright color, is odorless and convenient to use, and can be directly pasted on a mortar layer or a putty layer of an interior wall of a house. The interior wall coating coil avoids the pollution of various kinds of volatile matter generated in the production, construction and use of the traditional brushable interior wall coating, meets the national industrial policy of low cost, environment friendliness and energy conservation, has remarkable economic and social benefits, and is easy to popularize and use widely.

Description

technical field [0001] The invention relates to an interior wall paint coil, more specifically a coil with coating function, which can replace the existing brushable common interior wall paint, and further relates to a preparation method of the interior wall paint coil . Background technique [0002] Brushing interior wall paint (including latex paint) has become an indispensable basic building material for house decoration. With the continuous expansion of new buildings and the transformation of old buildings, the demand for interior wall coatings is increasing. Although the technology of interior wall coatings is very mature, due to the characteristics of coatings that are painted on site, the film-forming substances can only form a film after being painted. Therefore, the paint contains a large amount of film-forming substances, has a strong smell, and even contains formaldehyde, etc. Toxic substances have seriously affected the health and comfort of paint production wo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/02
Inventor 陈庆曾军堂
Owner 上海利民环保节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com