A preparation process and technology of fine-grained steel, applied in the direction of manufacturing converters, etc., can solve the problems of high sulfide content, difficulty in grain size level above 10, and lack of controlled rolling and cooling system for rolled steel, so as to improve product quality. The effect of grain size level, improved cold workability, and improved product quality

Inactive Publication Date: 2012-07-04
吉林建龙钢铁有限责任公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The 510L produced by the existing process route has high sulfide content, and the rolling steel lacks a strict controlled rolling and controlled cooling system, and its grain size level is difficult to reach above 10

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation technology for fine-grained steel 510L

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] Process flow of the present invention is:

[0012] a. Pretreatment process, using the method of spraying passivated magnesium into molten iron to remove sulfur, controlling the amount of magnesium injection, injection pressure, and injection flow rate, and prolonging the contact time between magnesium and molten iron;

[0013] b. Converter steelmaking: adopt sub-gun steelmaking technology, add medium carbon ferromanganese, ferrosilicon and ferroaluminum for deoxidation alloying after tapping, control the oxygen of molten steel after deoxidation alloying, add Nb iron at the end of tapping to determine the composition of molten steel Nb Micro-alloying, the steel ladle is supplemented by bottom blowing argon stirring while tapping;

[0014] c. After micro-alloying by converter tapping, after refining treatment, fine-tuning of molten steel composition temperature is carried out by adding alloy and feeding aluminum wire by wire feeding machine. At the same time, soft argon b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

A preparation technology for fine-grained steel 510L belongs to the field of steelmaking industry, can reduce the cost, improve the grain size grade of a product and the cold working performance of steel material, and has the following technological processes: a pre-processing process, that is, removing sulphur from molten iron by blowing passivated magnesium to the molten iron, and controlling the passivated magnesium blowing quantity, the blowing pressure and the blowing flow rate, so as to prolong the contact time between magnesium and the molten iron; and making steel with a revolving furnace, that is, a sublance steel making technology is adopted, mid-carbon fe-mn, ferrosilicon and ferro-aluminum are added into output steel for deoxygenation and alloying, the content of oxygen in the molten steel is controlled after deoxygenation and alloying, finally Nb iron is added into output steel for micro-alloying of Nb in the steel liquid, a steel ladle is stirred through bottom argon blowing during steel outputting, refining is carried out after micro-alloying of steel output by the revolving furnace, the ingredients and the temperature of the molten steel are trimmed by adding alloy or feeding aluminum wire by a wire feeding machine; moreover, an LF Furnace adopts the soft argon blowing process so as to remove foreign materials in the molten steel maximally, which improves the cleanliness of the molten steel; and the steel rolling process adopts a method capable of controlling rolling and cold. The invention has the advantages that the product quality is improved considerably; the cost is reduced; the grain size grade of the product is improved; and the cold working performance of the steel material is improved.

Description

technical field [0001] The invention belongs to the field of steelmaking industry. Background technique [0002] The production process of 510L in the past: blast furnace molten iron→pre-desulfurization of molten iron→converter smelting→refining (argon blowing or LF refining)→continuous casting→slab heating→rough rolling→finish rolling→layer cooling→coiling→storage. The 510L produced by the existing process route has high sulfide content, and the rolling steel lacks a strict controlled rolling and controlled cooling system, and its grain size grade is difficult to reach above 10 grades. Contents of the invention [0003] The purpose of the present invention is to provide a preparation process of fine-grained steel 510L that can reduce costs, increase the grain size level of products, and improve the cold working performance of steel products. [0004] Process flow of the present invention is: [0005] a. Pretreatment process, using the method of spraying passivated magne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C33/04C21C1/02C21C5/28C21C7/00C21D8/00
Inventor 朱学刚王磊
Owner 吉林建龙钢铁有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com