Method for rapid preparation of polymer multilayer film

A polymer, multi-layer film technology, used in chemical instruments and methods, lamination, lamination devices, etc., can solve the problems of unsuitable industrial production, long preparation process, high substrate requirements, and achieve excellent chemical stability, Improved preparation speed and high transparency

Active Publication Date: 2014-07-09
BEIJING UNIV OF CHEM TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the disadvantages of the prior art that have high requirements on the substrate, the preparation process takes a long time and is not suitable for industrial production, and provide a high-efficiency preparation technology, which realizes the polymer multilayer film on the planar substrate and the non-planar substrate. on the preparation, and the present invention is suitable for industrialized production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for rapid preparation of polymer multilayer film
  • Method for rapid preparation of polymer multilayer film
  • Method for rapid preparation of polymer multilayer film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 1. Soak the quartz piece in a mixed solution of 98% concentrated sulfuric acid and 30% hydrogen peroxide (the volume ratio of concentrated sulfuric acid and hydrogen peroxide is 7:3) and clean until no bubbles are generated, then clean the quartz piece with deionized water , and then blow dry with nitrogen;

[0039] 2. Prepare the required PEI ethanol solution and nano-zinc oxide ethanol solution: dissolve and dilute PEI and nano-zinc oxide ethanol solution with a mass fraction of 30% in absolute ethanol respectively, and the concentration of the prepared solution is 0.1mg / ml;

[0040] 3. Adjust the flow rate of the feed constant flow pump at 42ml / min, and the speed of the supergravity machine at 2400rpm;

[0041] 4. Soak the cleaned quartz slice in 0.1mg / ml PEI ethanol solution for 30min, wash it with absolute ethanol, and then dry it with nitrogen;

[0042] 5. Insert the quartz piece soaked in PEI ethanol solution into the card slot of the rotor of the ultra-gravity ...

Embodiment 2

[0047] 1. Soak the quartz piece in a mixed solution of 98% concentrated sulfuric acid and 30% hydrogen peroxide (the volume ratio of concentrated sulfuric acid and hydrogen peroxide is 7:3) and clean until no bubbles are generated, then clean the quartz piece with deionized water , and then blow dry with nitrogen;

[0048] 2. Prepare the required PEI ethanol solution and nano-zinc oxide ethanol solution: dissolve and dilute PEI and nano-zinc oxide ethanol solution with a mass fraction of 30% in absolute ethanol respectively, and the concentration of the prepared solution is 0.1mg / ml;

[0049] 3. Adjust the flow rate of the feed constant flow pump at 42ml / min;

[0050] 4. Soak the cleaned quartz slice in 0.1mg / ml PEI ethanol solution for 30min, wash it with absolute ethanol, and then dry it with nitrogen;

[0051] 5. The speed of supergravity is adjusted at 3000rpm. Insert the quartz slice soaked in PEI ethanol solution into the card slot of the rotor of the ultra-gravity mac...

Embodiment 3

[0055] 1. Soak the silicon wafer in a mixed solution of 98% concentrated sulfuric acid and 30% hydrogen peroxide (the volume ratio of concentrated sulfuric acid and hydrogen peroxide is 7:3) and clean until no bubbles are generated, then clean the silicon wafer with deionized water , and then blow dry with nitrogen;

[0056] 2. Prepare the required PEI ethanol solution and nano-zinc oxide ethanol solution: dissolve and dilute PEI and nano-zinc oxide ethanol solution with a mass fraction of 30% in absolute ethanol respectively, and the concentration of the prepared solution is 1mg / ml;

[0057] 3. Adjust the flow rate of the feed constant flow pump at 42ml / min, and the speed of the supergravity machine at 2400rpm;

[0058] 4. Soak the cleaned silicon wafer in 1mg / ml PEI ethanol solution for 30min, wash it with absolute ethanol, and then dry it with nitrogen;

[0059] 5. Insert the silicon chip soaked in PEI ethanol solution into the card slot of the rotor of the ultra-gravity m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Belonging to the technical field of chemistry and chemical industry production, the invention discloses a method for rapid preparation of a polymer multilayer film. The method can realize rapid preparation of a polymer multilayer film on a planar substrate and a non-planar substrate, and is suitable for industrial production. The method integrates a hypergravity technology and a layer-by-layer self-assembly technology, or in other words, an alternate layered self assembly process is carried out in a hypergravity machine so as to prepare a polymer multilayer film. The method can effectively enhance the preparation speed of a polymer multilayer film without changing the properties of the prepared polymer multilayer film. Being suitable for substrates of different shapes and different materials, the method has strong concentration adaptability, and can realize rapid preparation of a polymer multilayer film under a low concentration. Being suitable for acidic assembling liquids, alkaline assembling liquids and other assembling liquids of different properties, the method of the invention has the characteristics of simple operation process, short operation time, high efficiency, and suitability for industrial production.

Description

technical field [0001] The invention belongs to the technical field of chemical and chemical production, and mainly relates to a method for quickly preparing polymer multilayer films. The method can realize the rapid preparation of polymer multilayer films on planar and non-planar substrates, and the method is suitable for in industrial production. Background technique [0002] Today, with the increasing development of modern technology, materials with a single function can no longer meet people's needs, and composite materials with various improved properties are more and more popular. Over the years, composite materials have attracted more and more researchers to their research fields due to their unique properties. Among them, the research of assembling a layer of polymer multilayer film on the surface of existing materials to make materials and equipment with additional properties has gradually attracted the attention of more researchers. [0003] Polymer multilayer fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B37/00
Inventor 石峰马兰馨
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap