Bulletproof and stab-resistant armor and preparation method thereof

A bulletproof and stab-proof clothing, weft-free technology, applied in protective equipment, offensive equipment, personnel protection equipment, etc. The effect of cutting and impact resistance

Inactive Publication Date: 2014-11-19
杨珍芬
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this kind of stab-proof fabric has a good stab-proof effect, it is obvious that this kind of material cannot be used in the field of bullet-proof materials due to its lack of impact resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bulletproof and stab-resistant armor and preparation method thereof
  • Bulletproof and stab-resistant armor and preparation method thereof
  • Bulletproof and stab-resistant armor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] The embodiment of the invention discloses a method for preparing a bullet-proof and stab-proof clothing, comprising:

[0024] a), uniformly spreading and preheating ultra-high molecular weight polyethylene fibers;

[0025] b), on the ultra-high molecular weight polyethylene fiber after preheating, coat adhesive and dry, and the prepared area density is 135g / m 2 single-layer non-weft fabric;

[0026] c), taking 36 layers of the above-mentioned single-layer non-weft cloths superimposed on each other, and the fibers in the adjacent non-weft cloths are arranged at 0° / 10°, and the above-mentioned 36 layers of non-weft cloths and 1 layer of titanium alloy are hot-pressed and composited to obtain a composite layer;

[0027] d), the composite layer is superimposed with 2 layers of titanium alloy sheets, the composite layer forms the outer layer, the titanium alloy sheet adjacent to the composite layer forms the middle layer, and another layer of titanium alloy sheet forms the ...

Embodiment 1

[0049] 1. Place the 400-denier RYX90 ultra-high molecular weight polyethylene fiber produced by Ningbo Rongyi Chemical Fiber Technology Co., Ltd. on the creel. The spindles on the creel pass through the cluster frame and then gather into bundles. After passing through the static electricity generation device, they enter the static electricity elimination device. , Eliminate static electricity, and then preheat the uniformly spread ultra-high molecular weight polyethylene fibers at a temperature of 50°C through a heat tunnel.

[0050] 2. Lead the preheated fiber into the gluing device and apply glue through the rubber roller. The adhesive in the rubber roller includes: 15wt% epoxy resin, 8wt% neoprene rubber, 4wt% polystyrene-butadiene Diblock copolymer, 1wt% DOA and the balance of No. 120 mineral spirits (2,3-butanedione), the prepared areal density is 135g / m 2 The non-weft cloth, the content of adhesive in the non-weft cloth is 35wt%.

[0051] 3. Take 36 layers of non-weft f...

Embodiment 2

[0053] 1. Place the 400-denier RYX90 ultra-high molecular weight polyethylene fiber produced by Ningbo Rongyi Chemical Fiber Technology Co., Ltd. on the creel. The spindles on the creel pass through the cluster frame and then gather into bundles. After passing through the static electricity generation device, they enter the static electricity elimination device. , Eliminate static electricity, and then preheat the uniformly spread ultra-high molecular weight polyethylene fibers at a temperature of 45°C through a heat tunnel.

[0054] 2. Lead the preheated fiber into the gluing device and apply glue through the rubber roller. The adhesive in the rubber roller includes: 10wt% epoxy resin, 6wt% neoprene rubber, 5wt% polystyrene-polyisoprene Diene diblock copolymer, 0.6wt% DOA and the balance of No. 120 mineral spirits (2,3-butanedione), the prepared areal density is 135g / m 2 The non-weft cloth, the content of adhesive in the non-weft cloth is 38wt%.

[0055] 3. Take 36 layers of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a bulletproof and stab-resistant armor and a preparation method thereof. The bulletproof and stab-resistant armor sequentially comprises a composite layer, a middle titanium alloy sheet and an inner layer titanium alloy sheet from outside to inside, wherein the composite layer comprises 36 layers of non-woven clothes with the surface density of 135 g / cm<2> and one layer of the titanium alloy sheet from the outside to the inside; and the adjacent layers of the non-woven clothes are arrayed in the angle of 0 degree / 10 degrees. The composite layer in the bulletproof and stab-resistant armor provided by the invention has cutting resistance and impact resistance; the middle titanium alloy sheet and the inner layer titanium alloy sheet are used for further improving the bulletproof performance, so as to resist a plurality of attacks. The test proves that the bulletproof and stab-resistant comprehensive performance of the bulletproof and stab-resistant armor provided by the invention is higher and accords with the standards of bulletproof armors and stab-resistant armors for polices; and the weight of the bulletproof and stab-resistant armor provided by the invention is lighter so that the actions of people dressing the armors are not impeded.

Description

technical field [0001] The invention relates to the field of safety protection, in particular to a bullet-proof and stab-proof clothing and a preparation method thereof. Background technique [0002] Security personnel have to face many critical situations during their duties, such as being attacked by bullets or stabbed with daggers. In order to ensure the life safety of security staff in the fight with criminals, it is of great significance to maintain social public order to provide security staff with bulletproof and stab-resistant clothing to resist external invasion. [0003] Existing multiple anti-stab clothing or bullet-proof clothing, disclose a kind of composite bullet-proof clothing as the Chinese patent that application number is 97108879.9, the basic bullet-proof material part of this bullet-proof clothing at least comprises tuvalon, dyneema, air bubble plastic layer and Polyethylene board. Although this kind of bulletproof material has a certain bulletproof ef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F41H1/02
Inventor 周奇迪黄金帮赵罗杰陈永银陈钢
Owner 杨珍芬
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com