Extrusion-grade inflaming retarding ACS (acrylonitrile-chlorinated polyethylene-styrene) resin and preparation method thereof

An extrusion-grade and resin technology, applied in the field of extrusion-grade flame-retardant ACS resin and its preparation, can solve the problems of difficult to meet the requirements of composite co-extrusion processing, low melt strength, easy to break, etc., to improve thermal processing performance and Anti-thermal oxidation aging stability, excellent flame retardant performance, guaranteeing the effect of service life

Active Publication Date: 2012-01-04
ZHEJIANG OCEANKING DEVELOPMENT CO LTD
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the melt strength of general flame-retardant ACS is low, and it is easy to break during the melting and stretching process, so it is difficult to meet the processing requirements of composite co-extrusion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Extrusion-grade inflaming retarding ACS (acrylonitrile-chlorinated polyethylene-styrene) resin and preparation method thereof
  • Extrusion-grade inflaming retarding ACS (acrylonitrile-chlorinated polyethylene-styrene) resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] 100 parts of ACS resin (produced by Ningbo Zhenyang New Material, weight average molecular weight 200,000, rubber content 30wt%), 2.0 parts of lead salt composite stabilizer (produced by Zhejiang Longhua Plastic Additives, brand LH-900), 1.0 part of calcium zinc Composite stabilizer (produced by Zhejiang Hepton Chemical, brand HCZ 1086L), 15 parts of brominated epoxy resin (produced by Shandong Haiwang Chemical, brand EP-5000), 6 parts of ultrafine antimony trioxide (particle size 0.5μm), 5 parts of ACR (manufactured by Mitsubishi Rayon, brand P-531), 0.5 part of stearic acid, 0.5 part of antioxidant 245, 0.1 part of weathering agent UV-P are added to the high-speed mixer and stirred and heated to 60℃, mixed at 1000rpm for 10 Minutes, discharge, and add the above-mentioned mixture into a twin-screw extruder for extrusion granulation to obtain an extrusion-grade flame-retardant ACS resin. The screw speed of the extruder is 100 rpm, and the temperature settings of the 10 z...

Embodiment 2

[0052] 100 parts of ACS resin (produced by Ningbo Zhenyang New Materials, weight average molecular weight 300,000, rubber content 20wt%), 2.0 parts of lead salt composite stabilizer (produced by Zhejiang Longhua Plastic Additives, brand LH-900), 1.0 part of calcium zinc Compound stabilizer (produced by Zhejiang Hepton Chemical, brand HCZ 1086L), 25 parts of brominated epoxy resin (produced by Shandong Neptune Chemical, brand EP-5000), 3 parts of ultra-fine antimony trioxide (particle size 0.5μm), 5 parts of CPE rubber (produced by Qingdao Haijinghua, grade 135A), 5 parts of ACR (produced by Mitsubishi Rayon, grade P-531), 0.5 parts of stearic acid, 0.5 parts of antioxidant TNPP, 0.3 parts of weathering agent UV-327 Add the mixture to a high-speed mixer, stir and raise the temperature to 80°C, mix at 1000 rpm for 15 minutes, and discharge, and add the above-mentioned mixture to a twin-screw extruder for extrusion granulation to obtain an extrusion-grade flame-retardant ACS resin....

Embodiment 3

[0068] 100 parts of ACS resin (produced by Ningbo Zhenyang New Materials, weight average molecular weight 300,000, rubber content 20wt%), 1.0 part of lead salt composite stabilizer (produced by Zhejiang Longhua Plastic Additives, brand LH-900), 5.0 parts of calcium zinc Compound stabilizer (produced by Zhejiang Hepton Chemical, brand HCZ 1086L), 20 parts of brominated epoxy resin (produced by Shandong Haiwang Chemical, brand EP-5000), 6 parts of ultrafine antimony trioxide (particle size 0.25μm), 5 parts of ASA high gum powder (produced by Kumho Chemical in South Korea, brand XC-500), 5 parts of ACR (produced by Mitsubishi Rayon, brand P-531), 0.5 parts of polyethylene wax, 1.0 part of antioxidant 225, 0.5 part of weather resistance Add UV-531 to a high-speed mixer, stir and heat up to 100°C, mix at 1000rpm for 15 minutes, and discharge. Add the above-mentioned mixture into a twin-screw extruder for extrusion granulation to obtain an extrusion-grade flame-retardant ACS resin. T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an extrusion-grade inflaming retarding ACS (acrylonitrile-chlorinated polyethylene-styrene) resin. The resin is characterized by comprising the following components in parts by weight: 100 parts of ACS resin, 15-25 parts of brominated inflaming retarding agent, 3-6 parts of super-fine antimonous oxide, 0-10 parts of flexibilizer, 1-5 parts of melt strength regulator, 3-6 parts of thermal stabilizer, 0.5-1.5 parts of lubricant, 0.5-2 parts of antioxidant and 0.1-1.0 part of weather resisting agent. The extrusion-grade inflaming retarding ACS resin provided by the invention can be compounded and co-extruded with PVC (polyvinyl chloride) and has uniform coating, good surface gloss and smooth section, and the maximum processable width of the resin is greatly improved.

Description

Technical field [0001] The invention relates to the field of polymer modification, and specifically refers to an extrusion-grade flame-retardant ACS resin and a preparation method thereof. Background technique [0002] PVC plastic doors and windows have been widely used in China because of their light weight, corrosion resistance, high strength, energy saving, sound insulation, easy processing and low cost. Compound co-extrusion is one of the main methods of colorization of PVC profiles. By co-extruding a layer of color co-extrusion material with a thickness of 0.2mm~0.5mm on the surface of PVC profiles, the product is bright in color and beautiful in appearance. Commonly used co-extrusion raw materials are PVC, ASA and PMMA, but due to the poor weather resistance of PVC itself, more choices are ASA and PMMA as co-extrusion raw materials. [0003] PMMA has excellent weather resistance and high coloring performance. However, due to its poor flowability, it is difficult to form a un...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/06C08L51/00C08L25/12C08L63/00C08K13/02C08K3/22C08K5/09C08K5/109
Inventor 傅建永沈曙光谢滨周文斌邱琪浩方义红
Owner ZHEJIANG OCEANKING DEVELOPMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com