Surface metallization decoration method
An object surface and metallization technology, which is applied in the field of metallization decoration on the surface of non-metallic materials, can solve the problems of slow production speed of the laser method, low controllability of the production process, inability to solve the position of laser engraving, etc., so as to overcome the contour lines. Rough and uneven, controllable and reproducible, high-grade decorative effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0036] (1) After spraying UV curable paint on the surface of the mobile phone case with PC substrate, use vacuum coating equipment to coat a layer of indium tin alloy on the surface; (2) Spray UV curable photosensitive ink on the metal surface; (3) Place it on the workpiece A negative with a black graphic of the target decorative pattern (graphics such as figure 1 As shown), the thickness is 0.18mm, the sheet is tightly attached to the surface by vacuuming, and the exposure energy is 85mj / cm in a standard UV exposure machine. 2 , the ink in the light-transmitting area is cured, while the ink in the opaque area is not cured; (4) After exposure, use a 0.95% mass fraction of sodium carbonate solution as a developing liquid to spray in the developing equipment transported at the standard level , the ink in the opaque area is removed, and the metal layer below it is exposed, while the ink layer in the light-transmitting area remains on the surface of the metal layer; (5) On standar...
Embodiment 2
[0038] (1) After spraying UV curable paint on the surface of the mobile phone case of the PC substrate, coat a layer of aluminum on the surface with vacuum coating equipment; (2) Spray UV curable photosensitive ink on the metal surface; (3) Place a piece of paint on the workpiece Negative film with a black graphic of the target decorative pattern (e.g. image 3 As shown), the thickness is 0.18mm, the sheet is tightly attached to the surface by vacuuming, and exposed in a standard UV exposure machine, the exposure energy is 80mj / cm 2, the ink in the light-transmitting area is cured, while the ink in the opaque area is not cured; (4) After exposure, use a 0.95% mass fraction of sodium carbonate solution as a developing liquid to spray in the developing equipment transported at the standard level , the ink in the opaque area is removed, and the metal layer below it is exposed, while the ink layer in the light-transmitting area remains on the surface of the metal layer; (5) On sta...
Embodiment 3
[0040] As in Example 1, but the plated metal is silicon-aluminum alloy, and the developer solution used is dichloromethane solvent.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com